Steel 138-2

06X1 steel 06X1F steel 06XGR steel 06XF steel 07Cr3HNMuA steel Steel 08GDNF (SL-2; 08GDNFL) 08Cr2G2FA steel Steel 08KhMFCH (08KhMFCH) Steel 08KhMHA (08KhMCH) Steel 09GSFA (09GSF) Steel 09N2MFBA (09N2MFBA-A) Steel 09SFA (09SF) 09ХГ2НАБч steel Steel 09KhN2MD (AB2-SH1) Steel 09KhN3MD (AB3) Steel 09KhN4MD (AB4) Steel 10G2 (10G2A) Steel 10GN (10GNA) Steel 10Х1С2М Steel 10Х2ГНМ (10Х2ГНМА) Steel 10Х2М1 (10Х2М1А) 10Х3ГНМЯА steel Steel 10ХН3МД (АБ2-Ш2) Steel 12G1P Steel 12Х2Н4А (ЭИ83) Steel 12Х2НВФА (ЭИ712) Steel 12Х2НВФМА (ЭП506; ЭИ712М) Steel 12Х2НМ1ФА Steel 12Kh2NMFA Steel 12ХГН2МФБДАЮ (VS-4) 12XHNM steel 12CrNiMoV Steel 12KhN steel 12XH2 steel 12XH2A steel Steel 12KhN2MD (AB1) 12KhN3A steel 12XHN3MD steel (AB2; 12XHN3MDF) 12XHN4MBD steel (AB2P) Steel 138 IZ-2 13H2HA steel Steel 13H5A Steel 13Х3НВМ2Ф (DI45; VKS-4) Steel 13ХГМРБ 13CrNi2MoD steel 13CrNi2MoFd steel Steel 13KhGSN1MD Steel 13KhFA (13KhF) Steel 14N2MFD (14N2MFDA) Steel 14Х2ГМР Steel 14Х2Н3МА 14Cr3GMu steel Steel 14ХГ2САФД Steel 14ХГН Steel 14ХГНН2МДАФБ (14ХГНМДАФБ) Steel 14ХГННМДФБРТ (14ХГНМД) Steel 14KhGSN2MA (EP176; DI3A) Steel 14ХН3МА Steel 15G (15G1) 15GUT steel Steel 15H2M (15NM) 15H3MA steel 15X steel 15Kh1SMFB steel 15Cr2Hn2TA steel Steel 15Kh2HN2TRA 15KhA steel 15CrNi2MaFach steel 15CrNi2TA steel (15CrNi2TA) 15KhGNM steel (15KhGNMA) 15KhMFA steel (15KhMF) 15KhN3 steel 15Cr steel 15KhSMFB steel (EP79) 15KhFA steel (15KhF) Steel 16G2 Steel 16Х2Н3МФБАЮ (16Х2Н3МФАБ; VKS7) Steel 16Х3НВФМБ (VKS-5; DI39) Steel 16ХГ (АЦ16ХГ) Steel 16ХГТА (ЭИ274) Steel 16ХН3МА 16KhSN steel Steel 17H3MA 17KhG steel Steel 18Г2ХФЯД Steel 18Kh2H4VA Steel 18Kh2H4MA 18CrNiG Steel 18ХГН2МФБ steel 18KhGT steel 18XH2T steel 18KhN3MA steel 18KhNVA steel Steel 18KhNMFD (18KhNMFDA) Steel 19Х2НВФА (ЭИ763) Steel 19Kh2NMFA Steel 19KhGN Steel 19ХГНМА (19ХГНМ) Steel 19ХГСС Steel 20G (20G1) Steel 20G2 Steel 20G2AF (20G2AFps) 20G2P steel 20GUT steel Steel 20H2M (20NM) Steel 20F (20FA) 20X steel Steel 20X2MA Steel 20X2MFA Steel 20X2H4A Steel 20Х2Н4МФ (20Х2Н4МФА) Steel 20Kh3NMF (20Kh3NMFA) 20XHNM steel 20KhGNMT steel (20KhGNMTA) Steel 20ХГНР 20XHNTR steel 20XGR steel 20KhGSA steel Steel 20ХГСР 20XM steel 20KhN steel Steel 20KhN2M (20KhNM) 20KhN3A steel 20KhN3MFA steel (20KhN3MF) 20KhN4FA steel 20KhNR steel 20KhFA steel (20KhF) Steel 21N5A (EI56) Steel 21Х2НВФА Steel 21Х2НМФА Steel 22KhGNMA (22KhGNM) 22XHNM steel Steel 23G2D Steel 23Х2НВФА (ЭИ659) Steel 23Х2НМФА Steel 23KhN2M Steel 24G2 Steel 24Kh3MF (24Kh3MFA) 24CrNiM Steel Steel 25G (25G2) 50G steel Steel 50G2 50X steel 50KhN steel 5XHNM2 steel 85GF steel AK32 steel AK33 steel AK34 steel AK35 steel AK36 steel AK37 steel AK48 steel AK49 steel AK50 steel Steel 25H Steel 25H3A Steel 25Kh2H4VA Steel 25Х2Н4МА Steel 25ХГ2СФР 25KhGM steel Steel 25KhGNMA (25KhGNM) Steel 25KhGNMT (25KhGNMTA) 25KhGSA steel Steel 25KhGT 25CrM steel Steel 25KhN3 Steel 25KhNTZ Steel 26G1 Steel 26Х1МА (26Х1М) Steel 26Х2НВМБР (KVK-26) Steel 26KhGM Steel 26ХГМФ (26ХГМФА) Steel 26KhMA (26KhM; 25KhM) Steel 27XGR Steel 30G (30G1) 30G1P steel Steel 30G2 30T steel 30X steel Steel 30X2H2VFA Steel 30X2H2VFMA Steel 30Kh2NVA Steel 30Kh2NVFA Steel 30Kh2NVFMA Steel 30Kh2NMA Steel 30Х2НМФА (30Х2НМФ) Steel 30Kh3MF 30Kh3MFSA steel 30Kh3NVA steel 30CGS steel 30KhGSA steel 30KhGT steel 30XM steel 30KhMA steel Steel 30KhN2VA Steel 30KhN2VFA Steel 30KhN2MA (30KhNMA) 30KhN2MFA steel 30KhN3A steel 30KhN3M steel Steel 30KhNMFA (30KhNVFA) 30KhRA steel Steel 30ХСНВФА (ВП30) Steel 32G2 Steel 32G2S Steel 32Х2НВМБР (KVK-32) Steel 33Kh3SNMVFA (SP33; EP613) Steel 33XHN3MA Steel 33HS Steel 34KhN1VA (0KhN1V) Steel 34KhN3M Steel 35G Steel 35G1P Steel 35G2 Steel 35X Steel 35Cr2YuF Steel 35CrNi2 35KhGSA steel Steel 35CrM Steel 35KhN2F Steel 35KHN3MA (35KHN3M) Steel 36G2S Steel 36G2SR Steel 36Х2Н2МФА (36ХН1МФА) Steel 37G2S Steel 37Х2НВМБР (КВК-37) 37KhN3A steel 38Cr2MuA steel (38Cr2MuA) Steel 38Kh2H2VA Steel 38Kh2H2MA (38KhNMA) 38X2H3M steel 38X2HM steel 38Kh2NMF steel 38Kh2Yu (38Kh2YuA) steel 38KhA steel 38KhGM steel 38KhGN steel 38CrNiM steel 38KhGSA steel (38KhGS) Steel 38KhM (42KhM) 38KhMA steel 38KhN3VA steel 38KhN3MA steel 38HS steel Steel 38KhFR (40KhFR) 40G steel Steel 40G2 Steel 40GR (40G1P) Steel 40Kh (40KhA) Steel 40X2H2VA Steel 40X2H2MA Alloy 40Kh3M2FA (USP-40) 40KhGNM steel 40KhGSMA steel 40KhGTR steel Steel 40KhMFA (40KhMF) 40KhN steel Steel 40KhN2VA (40KhNVA) Steel 40KhN2MA (40KhNMA) 40KhR steel 40HS steel 40KhSN2MA steel Steel 40KhFA (40KhF) Steel 42Х2НВМБР (KVK-42) Steel 42Х2НМБР (ABO70Н) Steel 42KhMFA (42KhMF) Steel 44Х2НМБР (ABO70В) 45G steel Steel 45G2 45X steel 45KhN steel 45KhN2MFA steel (45KhNMFA) Steel 47GT 48KhN3M steel

Designation

Name The value
Designation GOST Cyrillic 138 ИЗ-2
Designation GOST Latin 138 IZ-2
Transliteration 138 IZ-2
The chemical elements 138 ИЗ-2

Description

Steel 138−2 applies: for the production of rolled plate with a thickness of 37−90 mm, used for the manufacture of parts of the hydromechanical equipment has a good ductility, high resistance to brittle fracture and satisfactory weldability.

Standards

Name Code Standards
Sheets and stripes В33 TU 108.11.630-87

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu Mo
TU 108.11.630-87 0.11-0.15 ≤0.03 ≤0.03 0.75-1.05 0.6-0.95 0.2-0.4 1.7-2 The rest 0.2-0.6 0.45-0.55
Fe is the basis.
According to TU 108.11.630-87 the chemical composition is presented for steel grade 138 IZ-2. As a technological additive, titanium and vanadium additive are produced at 0,04-0,05% each according to the calculation without correction for fumes. The content of titanium and vanadium is not determined. Deviations from the chemical composition are allowed: carbon ± 0.010%, silicon 0.10 / -0.030%, manganese ± 0.10%, nickel ± 0.10%, chromium + 0.10 / -0.050% , molybdenum ± 0.050%, copper ± 0.050%.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d5, % y, % kJ/m2, кДж/м2
Sheet metal in delivery condition on the other 108.11.630-87. In the graph of the impact toughness values KCV+20/KCV-60
37-50 ≥510 608-784 ≥18 ≥50 ≥784/441
60-90 ≥510 608-784 ≥18 ≥50 ≥784/392

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
y The relative narrowing
kJ/m2 Toughness

Technological properties

Name The value
Macrostructure and contamination On the surface of the leaves is allowed without the removal of the thin layer of oxides that do not impede the detection of surface defects, the roughness of the fallen scale, risks, dents, fingerprints from the rolls, scratches and other minor, local defects, not deducing the size of the sheet beyond the negative deviations. On the surface of the sheet is not allowed defects in the captured, bubbles, cavities, cracks, katanoi dross and slag inclusions are to be removed by a gentle felling. On the edges of plates after flame cutting lamination and cracks are not allowed. Allowed fire snags, if it does not take the leaves for tolerances on dimensions. Grat fire after cutting must be removed. Steel fracture should be fibrous, while in fracture the number of Bologna must be at least 60%. If necessary, re-heat treatment. Sipernet in the turn is not a rejection symptom. Crystal allowed a rash over the whole fracture surface.
Features of production Steel melted in the basic electric arc furnaces. Allowed the smelting of steel in basic open-hearth furnaces.
Correction of defects Remove defects at a depth of up to 5% of the nominal thickness of the sheet over the negative deviations. The total area of Stripping and local thin places on each side of the paper should not exceed 2% of the leaf area and the number of sweep shall not exceed four units on 1 square meter of the sheet. When coincidence Stripping on both sides of a sheet permissible depth of Stripping is determined as the sum of the depths of sweeps on each side of the paper and should not exceed 5% of the nominal thickness of the sheet over the negative deviations. When the depth of defect more than 5% of nominal sheet thickness in excess of negative deviations, but not more than 25% of the nominal thickness of the sheet in excess of negative deviations are allowed cutting or scraping sand around these defects with subsequent welding is repair of technology of the manufacturer. Thus the area of the welding at each location must not exceed 0,0050 m2 (excluding collapse after cutting), and the total area of welding does not exceed 2% of the leaf area.