HN60WT wire, rod

Wire, rod, bar Strip, sheet


Grade analogue W. Nr. Aisi Uns En Order
XH60VT VZh98 Buy from stock, view availability
XH60VT EI868 Buy from stock, view availability
KhN60VT-p EI868 Buy from stock, view availability


Wire made of an actual nickel-chromium alloy is used for operational use at a high temperature (<1050ºС) in aggressive industrial environment. A high content of nickel and chrome guarantees a high corrosive resistance of a wire. Perfect plasticity allows making wire of a minimal diameter. This makes it much-requested in a manufacture of household and industrial electrical units.


Percentage composition of alloy is compliant with GOST 5632−72. Alloy is smelted in open electric furnaces. It provides a minimal content of unnecessary residual elements. You can order a wire of any diameter.

Percentage composition

Ni Cr Fe W Ti Mn Si Al Ca C S P
59- 63.2 24−26.5 ≤4 13−16 0.3−0.7 ≤0,5 ≤0,8 ≤0,5 ≤0,05 ≤0,1 ≤0,013 ≤0,013

Technical characteristics

Linear expansion coefficient of a wire is 13,7 (1/deg. К). Density is 8,16 g/cm³. Mechanical properties vary according to a working temperature. Heat conduction coefficient changes in a range of 16,9 — 13,4 V/(m•deg. K). Such wire is easy weldable by virtue of well-balanced composition. It simplifies equipment installation and does not require a final heat treatment after welding. Wire surface does not oxidize at durable operational use or at a high temperature. This wire is malleable. It possesses a resistance in oxidizing atmosphere, in environment of ammonia, nitrogen. Its main demerit is that a wire does not have stability in atmosphere of sulfur and sulfur compounds. It is not cheap because its main component — nickel is expensive.


At increased structural requirements to constructions, a wire should be thermohardened at a temperature of 1000 — 1100ºС with further cooling in water or in the air. This conduces to normalization of inherent stress in alloy and to increasing of strength characteristics of details.

Dimension Direction sV mPa sT MPa d5% y % Thermohardening in air
Bar Longitudinal 750 300 45 52  
Strip   700   30   1150−1170ºС


It is used in manufacturing grids for kilns, electrical furnaces. Such a wire is much-needed in rheostats; in manufacture of vacuum device elements, coppers, plates of increased reliability. It also can be used in the capacity of cutting and heating element in packing thermal knives. Its increased plasticity allows performing a rolling at low temperatures, thereby reducing energy demands. Nowadays, the widest application of such wire is found in petrochemical mechanical engineering.

HN60WT wire, rod supplier

«Auremo» supplier offers to buy HN60WT wire, rod by wholesale. There is a wide range of half-finished goods in stock. They comply with GOST and International quality Standards. Wire, rod, bar HN60WT are always in stock. You can buy them for an affordable HN60WT wire, rod price from a supplier. Buy HN60WT wire, rod right now!

Buy HN60WT wire, rod at a bargain price

«Auremo» supplier is a recognized expert on a market of heat-resisting mill-products. We have offices in Eastern Europe, so we are able to make a prompt cooperation with business partners. An experience of our company allows you easily buy goods in a large variety by wholesale. A quality is compliant with GOST (all-Union State Standards) and International Standards. «Auremo» company is a reliable HN60WT wire, rod supplier of heat-resisting mill-products that invites all the wishing to a partnership. We have the best price-quality ratio. HN60WT wire, rod price is privileged for wholesale customers. All products are certificated. A delivery service will supply your order in the shortest possible time. HN60WT rod, wire, bar are always in stock.