The welding wire 08H20N9G7T, aisi 307L, N-74
Equivalent
| Grade | analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 08Х20Н9Г7Т | H-74 | 307L | Buy from stock, view availability |
Relevance
Welding wire brand SV-08Х20Н9Г7Т made in accordance with, RD 03−613−03, GOST 2246−70 and technical conditi. 1220−005−84 823 540−2010. This wire is used for manual arc welding of the most critical components of structures made of austenitic steel grades: 08KH18N12B, 12KH18N9T, 08KH18N10T, and similar. Wire is also used for parts of internal devices operated at t° 570−650°, high pressure, and used for welding steels of similar marks in the case when the seam is not present stringent requirements of resistance to intergranular corrosion.
Supply
In rolls of 85−100 kg, frame, metal coil К415, K300, plastic spools D200, 300. Produced wire diameter: 1 mm; 1.2; 1.6 mm; 2; 2.5 mm; 3, 4, 5 mm (allowable under the order production of the required size).
Percentage composition of welding wire SV-08Х20Н9Г7Т (GOST 2246−70)| C | Si | Mn | Ni | S | P | Cr | Ti | Fe |
| 0,07−0.9 | 0.5 — 1 | 5 — 8 | 8 — 10 | up to 0.018 | up to 0.035 | 18.5 — 22 | 0.6 — 0.9 |
Basis |
Mechanical properties of wire
Rupture strength of high-alloy and alloy wire in accordance with the regulations.
| Diameter, in mm | Temporary tear resistance of the electrodes | Temporary tear resistance, kgf/mm2 (MPa) of wire for surfacing |
|---|---|---|
| SV. 2,0 | 637−931 (65−95) kgf/mm2 (MPa) | 686−1029 (70−105) |
| 2,0 | 686−980 (70−100) kgf/mm2 (MPa) | 784−1176 (80−120) |
| 1,6 | 686−980 (70−100) kgf/mm2 (MPa) | 882−1274 (90−130) |
| 0,8−1,5 | - | 882−1323 (90−135) |
Limit deviations and wire diameters correspond to the following
Wire diameter nominal Deviation limiting wire intended for
to| production of electrodes | surfacing (welding) of | surfacing (welding) |
|---|---|---|
| 1,5 | -0,09 | |
| 4,0; 5,0; 6,0 | -0,12 | -0,16 |
| 1,6; 2,0 | - | -0,12 |
| 0,8 | -0,06 | -0,07 |
| 2,5; 3,0 | -0,09 | -0,12 |
| 1,2 | - | -0,09 |
Ferritic phase:
In the wire of the ferritic phase components are regulated with the agreement of the parties.
Welding-technological characteristics
Wire weld metal is used in the environment of inert argon gas. Formation of a filling, root, face layers of the seam, and arc stability.
Mechanical characteristics (test during submerged arc welding) weld metal.
| Brand of welding wire | Temporary resistance at break σ B, in MPa | Relative elongation, % | Yield limit, σ T, MPa | The viscosity of the shock, in j/cm2 KCU |
|---|---|---|---|---|
| -20°C | +20°C | |||
| SV-08Х20Н9Г7Т | 598,3 | 33 | 320,1 | To 119.7 — is 120.2 |
The weld metal of the weld to intergranular corrosion is not inclined.
Buy at best price
Welding wire SV-08Х20Н9Г7Т from «Aureka» complies with GOST and international quality standards. A wide selection of products, comprehensive consultations managers, reasonable prices and timely delivery define the face of our company. Deliveries go directly from the warehouse. It gives consumers a clear choice of product and significant savings on inventory and facilities. The company «Auramo» has all the capabilities to produce quality products with non-standard parameters according to individual order. We invite you to partnership.