C83600 Leaded Red Brass Alloy Products
Request C83600 Red Brass Pricing
Auremo LLC, 505 Ellicott St, Buffalo, NY 14203, handles C83600 inquiries for U.S. valve, fitting, bearing and machinery projects. Call +1 716 910 04 21 or send the standard, casting process, drawing, dimensions and quantity.
Available product forms
- sand and centrifugal castings
- continuous-cast bar and cored bar
- cut blanks with machining allowance
- machined parts supplied to drawing
Information to include in your request
Please provide the governing standard or grade, product form, dimensions and tolerances, quantity, delivery ZIP code and required documentation. Pricing and availability are confirmed individually for each inquiry.
Frequently asked questions
How is the price for UNS C83600 leaded red brass alloy products confirmed?
Prices are provided on request and depend on the exact grade or standard, dimensions, tolerances, quantity, documentation and freight requirements.
Can non-standard dimensions be requested?
Yes. Include a drawing or dimensional requirements. Availability and manufacturing or sourcing feasibility are confirmed with the quotation.
What is the typical delivery time in the United States?
Typical U.S. delivery is 2–3 weeks after order confirmation. The final lead time and delivery terms are stated in the quotation for the selected material, quantity and destination.
Related materials and references
Red brass alloy products · Semi-red brass products · C84400 casting alloy
Equivalent
| Grade | analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 2.1096 | C83600 | G-CuSn5ZnPb | Buy from stock, view availability |
C83600 casting forms and quotation requirements
U.S. searches include C83600 leaded red brass, C83600 cored bar, C83600 bronze and C83600 material. For a quotation, provide UNS C83600 and the applicable ASTM or project specification, required sand, centrifugal or continuous casting, bar, cored bar, blank or machined component, drawing and tolerances, quantity, pressure or inspection requirements, certificates and destination ZIP code.
Technical characteristics
UNS C83600 grade is red-lead brass. It differs with high content of copper in composition. Density of material constitutes 8,83 g / cm3 (0,319 pound / in³). This material is very consistent and widely used. This type relates to two-component brasses. C83600 grade is mostly utilized in electrical engineering and heat-power engineering.
Percentage composition according to EN12165
| Name | Content |
| Aluminium (Al) | 0,0050 |
| Antimony (Sb) | 0,25 |
| Copper (Cu) | 84−86 |
| Iron (Fe) | 0,30 |
| Lead (Pb) | 4,0−6,0 |
| Nickel (Ni) | 1,0 |
| Phosphorous (P) | 0,050 |
| Silicon (Si) | 0,0050 |
| Sulfur (S) | 0,080 |
| Tin (Sn) | 4,0−6,0 |
| Zinc (Zn) | 4,0−6,0 |
Mechanical properties:
1) Brinell hardness (typical index) = 60;
2)Tensile strength rupture limit of material is 255 MPa (37000 pounds per square inch);
3) Yield limit of material (0.500% strain) is 117 MPa (17000 pounds per square inch);
4) Ultimate elongation at break (50 mm) is 30%;
5) Resistance to long duration loads (on 0,1% of creeping 10000 h, t° 290°С) — 48,0 MPa (6960 pounds per square inch).
6) Ultimate shearing strength (t° 230 °C, 3.60 min + 8 sec / 446°F, 100000 hours) is 35,0 MPa (5080 pounds per square inch)
7) Module of material elasticity is 83.0 HPa (12000 KSI);
8) Compression strength (permanent change of form — 0.1%, at room temperature) is 97.0 MPa (14100 pounds per square inch)
Thermal properties
Heat conductivity (at 20 ° C / 68 ° F) is 72,0 V / mK (500 BTU в / hr. ft². °F)
C83600 alloy badly undergoes modification of heat treatment. It has stress-relieving temperature of 260 °C (500°F).