High speed steel
Equivalent
| Grade | analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| Р6М5 | ~1.3343 | sw7m | hs6-5-2 | Buy from stock, view availability | |
| Р12Ф3 | EP597 | 1.3318 | sw12 | Buy from stock, view availability | |
| Р9 | Buy from stock, view availability | ||||
| Р8М3К6С | Buy from stock, view availability | ||||
| Р8М3 | Buy from stock, view availability |
Technical characteristics
Brand high speed steel produced in accordance with the norms of GOST 19 265−73. It is used in the manufacture of cutting tools, which is designed for high speed cutting mode. High speed brand alloyed with tungsten, molybdenum, vanadium, cobalt, which provides high heat resistance, red hardness, wear resistance. Brand R6M5, R12F3, Р8М3К6С, Р8М3, Р8М5, P9 used for the production of high speed tool. Favorably great heat resistance, have a high estimated hardness.
Marking
Following the letter «R» number indicates the average tungsten content (by weight percentage, the letter is skipped). Then the letters M, K, f indicate the percentage of molybdenum, cobalt, vanadium.
Percentage composition
| Mark | Mn | Si | C | Ni | Cr | P | S | Mo | Co | V | W | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| R18 | to 0.5 | to 0.5 | 0.73 — 0.83 | to 0.4 | 3.8 — 4.4 | to 0.03 | to 0.03 | to 1 | to 0.5 | 1−1,4 | 17 — 18.5 | |
| R6M5 | to 0.5 | to 0.5 | 0.82 — 0.9 | to 0.4 | 3.8 — 4.4 | to 0.03 | up to 0.025 | 4.8 — 5.3 | to 0.5 | 1.7 — 2.1 | 5.5 — 6.5 | |
| R9K5 | to 0.5 | to 0.5 | 0.9 — 1 | to 0.4 | 3.8 — 4.4 | to 0.03 | to 0.03 | to 1 | 5,0−6,0 | 2.3 — 2.7 | 9,0−10,0 | |
| R6M5K5 | to 0.5 | to 0.5 | 0.84 — 0.92 | to 0.4 | 3.8 — 4.3 | to 0.03 | to 0.03 | 4.8 — 5.3 | 4.7 — 5.2 | 1.7 — 2.1 | 5.7 — 6.7 | |
| Hardness after annealing the material R18 | Hardness after annealing the material R9K5 | Hardness after annealing the material R6M5 | Hardness after annealing the material R6M5K5 |
|---|---|---|---|
| HB 10 -1 = 255 MPa | HB 10 -1 = 269 MPa | HB 10 -1 = 255 MPa | HB 10 -1 = 269 MPa |
Alloying
Alloying has a multifaceted effect on the quality of the steel. Chromium increases resistance to corrosion. The Nickel gives the alloy ductility; tungsten — wear resistance, red hardness. Vanadium increases the resistance to shock load and abrasion. Molybdenum alloy imparts red-hardness, strength, opposition to oxidation at high temperature. The proportion of manganese is above 1% increases the impact strength, wear resistance. Titanium increases the stability, corrosion resistance.
Supplier
Supplier «Auremo» offers to buy wholesale high speed steel or in installments. Large selection in stock. Compliance with GOST and international quality standards. Always in stock high speed steel price — the best from the vendor. Wholesale customers price — discount Buy high speed steel today.
Buy at best price
The company «Auremo» — the supplier of high speed steel in the countries of Eastern and Central Europe. The experience of our company will allow You to easily buy high-speed steel on favorable terms. The quality complies with GOST and international standards. In the directory given unlimited choice of products. Always in the presence of circle, rod of high speed steel, price depends on order volume and additional conditions of delivery. Wholesale customers — the price is preferential. Connected experienced managers — will help to quickly buy a high speed steel in bulk or in installments. We invite you to partnership.