| NP1A |
|
In equipment for manufacturing caustic soda, fluorine, liquid chlorine etc. at a temperature from -70 to +500°. Usually, pipes. 8,9 g/cm3.
|
48−0814−11/0−83, 13 083, 14−3-1591−88, 48−0815−84−92, 48−0815−80−92. |
| Nickel 201 |
|
In equipment for manufacturing caustic soda, fluorine, liquid chlorine etc. at a temperature from -70 to +500°. Usually, sheets, plates 8,9 g/cm3.
|
48−0814−11/0−83, 13 083, 14−3-1591−88, 48−0815−84−92, 48−0815−80−92. |
| EP516, H23N28М3DZТ |
06HN28МDT |
Welding equipment in a manufacture of sulphuric acid, phosphorus extraction acid, nitrophoska. In aggressive environment, it possesses an increased resistance to intercrystallite corrosion of welding seams in comparison with OZL-17U, 06HN28MDT. |
14−1-756−73, 5949−75, 5632−72, 7350−77 |
| H21N28W5MZBAR, EP126 |
HN28WMAB |
Parts of turbines. |
14−1-192−72, 14−1-21−71 |
| H20N32T, EP670 |
HN32T |
Pipes, offtake parts of processing heat-resistant units, ammoniacal manufacture with a long time of exploitation at temperature up to 850°. 8,16 g/cm3. |
24 982−81, 5632−72, 14−1-284−72, 14−1-489−76, 14−1-625−73, 14−1-4319−87, 14−1-2111−77 |
| EP912 |
HN35WB |
Corrosive-resistant steel for details of special techniques. |
14−1-4222−86 |
| EI612 |
HN35WT |
Turbine disks, blades, rotors, fasteners. |
14−1-1665−76, 14−1-272−72 |
| EI787 |
HN35WTJU |
Disks, blades of turbines, compressors. |
14−1-850−74, 14−1-1589−76 |
| EI703 |
HN38WT |
Details with a moderate loading. |
14−1-476−72 |
| HN45МWTJUBR, EP718 |
HN45МWTJUBR |
Details of special technique. |
14−1-3905−85 |
| EP747 |
HN45JU |
Thermocouple protection tube, firing conveying grid, details of burner units, rolling elements of kilns that burn ceramics, equipment for enamel roasting kilns that work at temperature 1250−1300° without mechanical loads. 7,7 g/cm3 OZL-35, OZL-25. |
24 982−81, 5632−72, 14−1-941−74, 14−1-4082−86, 14−1-2396−78,14−1-2075−87 |
| EP648 |
HN50WMTJUB |
Details of special techniques. |
14−1-3046−80 |
| EP969 |
HN50WMTJUBK |
Pipes, parts of gas transmission systems, graded details. |
14−1-131−527−82 |
| EP99 |
HN50MWKTJUR |
Heat-resisting alloy for details of special techniques. |
14−1-1476−75 |
| EI929 |
HN55WMTKJU |
Turbine blades. |
14−1-223−72/131−379−78 |
| EP666 |
HN55MBJU |
Brazed and stamp-welded products, with working temperatures from -253 up to +750° in the capacity of extrahigh tensile alloy in sea water and strong acid. Resistance to brittle behaviour in hydrogen. Workability to welding with various stainless steels. 8,8 g/cm3. |
14−1-2692−79, 14−1-2606−79, 14−1-2702−79, 14−1-3490−82, 14−1-3191−81 |
| EP109 |
HN56WMKJU |
Turbine blades. |
14−1-223−72 |
| EP199 |
HN56WMTJU |
Disks, structure blades, turbine details. |
14−1-1508−75 |
| EK62 |
HN56MBJUD |
Details of special techniques. |
14−1-5045−91, 14−1-3763−84 |
| EP795 |
HN58W |
Welding equipment in fluoric-nitric-acid solutions and in HNO3 solution. Welding with a help of electrodes FH-26, FH-13. Pickling baths. |
14−131−224−75, 3239−81, 5632−72, 14−131−756−88, 14−1-4363−87, 14−1-4362−87, 14−1-2715−79. |
| EI618 |
HN60WMTJUR |
Details of special techniques. |
14−1-1322−75 |
| EI868 |
HN60WT |
Engine details. Afterburners, combustion chambers, details with a working temperature of not more than 1100°. 8,35 g/cm3. |
14−131−224−75, 3239−81, 5632−72, 14−131−756−88, 14−1-4363−87, 14−1-4362−87, 14−1-2715−79. |
| EP367 |
HN60M |
Details of special techniques. |
14−1-2693−79 |
| EI559A |
HN60JU |
|
|
| EP708 |
HN62WMJUT |
Details of special techniques. |
14−1-1018−74 |
| EI867, HN62WMKJU |
HN62MWKJU |
Disks, blades of turbines. |
14−1-223−72, 14−1-402−72 |
| EP567, 0H15N65M16W |
HN65MW |
In manufacture of chemical equipment in hard oxidation-reduction environment; in petrochemical, chemical, paper-and-pulp industries. A temperature is from -70 up to +500°. |
3239−81, 5632−72, 14−1-2475−78, 14−1-3239−81,14−3-1227−83, 14−1-1215−75 |
| EP760 |
HN65MWU |
Heat interchangers, reactors, columns; in manufacture of epoxide resins, colloidal silvers, spirit of verdigris, vinyl acetate, mineral fertilizers, ethyl benzene etc. at a temperature from -70 up to +500°. OZL-21. 8,9 g/cm3. |
3239−81, 5632−72, 14−1-2230−77, 14−1-3587−83, 14−1-4870−90, 14−1-3768−84, 14−3-1320−85, 14−3-1227−83, 14−1-2240 |
| EI445 |
HN67WMTJU |
Heat interchangers, reactors, columns; in manufacture of epoxide resins, colloidal silvers, spirit of verdigris, vinyl acetate, mineral fertilizers, ethyl benzene etc. at a temperature from -70 up to +500°. OZL-21. 8,9 g/cm3. |
3239−81, 5632−72, 14−1-2230−77, 14−1-3587−83, 14−1-4870−90, 14−1-3768−84, 14−3-1320−85, 14−3-1227−83, 14−1-2240 |
| EP202 |
HN67MWTJU |
Details of special techniques. |
14−1-592−73 |
| EI652 |
HN70JU |
Details of combustion chambers and afterburners - pockets, diffusers, screens etc. with a small loading and temperature of not more than 1200°. 7,9 g/cm3. Point of melting is 1400°. Class of nichrome and aluminium. Heating resistor elements. |
5632−72, 24 982−81, 14−1-833−71, 12 766.4−77, 14−1-493−72, 14−1-1497−75, 14−1-810−73 |
| EI602 |
HN75MBTJU |
Parts of gas-line arrangements, equipments. |
14−1-3721−84 |
| EI869 |
HN75TBJU |
|
|
| EI437A |
HN77TJU |
Aircraft industry. |
14−1-75−71/402−72/764−73 |
| EI437B |
HN77TJUR |
Details of aircraft engines, turbine blades, disks. |
14−1 -402−72/1465−75/223−72 |
| EI437BU |
HN77TJURU |
|
|
| EI435 |
HN78T |
Details of aircraft engines. Essential floating parts with an operating temperature of not more than 1100°: flame tubes, combustion chambers, thermocouple protection tubes, main flues 8,4 g/cm3. OZL-25B, OZL-25, CT-28. |
24 982−81, 5632−72, 14−1-895−74, 14−1-1671−76, 14−1-975−74,14−1-2752−79, 14−1-4009−85, 14−1-4319−87, 14−1-4319−87, 14−1-3942−85 |
| EI607A |
HN80TBJU |
Disks, structure blades, turbine details. |
14−1-1358−74 |
| EP516 |
03HN28MDT |
Manufacture of welding equipment for sulphuric acid of various concentration up to 80 °C. |
GOST 5949−75, GOST 5632−72; ТC 14−1-756−73; GOST 7350−77 |
| EP982 |
N65M |
Welded chemical equipment that is exploited in a very aggressive environment of reconstructive type. |
ТC 14−1-2674−79; ТC 14−1-3281−81; ТC 14−131−685−86; ТC 14−1-2879−80; ТC 14−1-4673−89; ТC 14−1-4719−89; ТC 14−1-4202−87; ТC 14−3-1478−87 |
| EP814A |
N70MFW |
Manufacture of chemical welded equipment (heat interchangers, drum-type reactors) that is exploited at very high temperatures in chloride environment. |
ТC 14−3-1227−83; ТC 14−1-2230−77; ТC 14−1-4684−89; ТC 14−1-2260−77; GOST 5632−72 |
| NP1A |
NP1A |
Manufacture of chemical welded equipment; manufacture of chloride, liquid chloride, caustic soda etc. |
ТC 48−0815−80−92; ТC 14−3-1591−88; ТC 48−0814−11/0−83; ТC 48−0815−84−92 |
| NP1A-ID |
NP1A-ID |
Manufacture of chemical welded equipment; manufacture of chloride, liquid chloride, caustic soda etc. |
ТC 48−0815−80−92; ТC 14−3-1591−88; ТC 48−0814−11/0−83; ТC 48−0815−84−92 |
| EP937 |
HN40MDB |
Application in the form of non-magnetic welding wrought material; in chemical equipment that is used in very aggressive environments. |
ТC 14−1-2149−77; ТC 14−1-2131−77; ТC 14−1-2121−77 |
| EP543U |
HN40MDTJU |
Manufacture of chemical welded equipment (centrifugal separator, centrifuges etc.). |
ТC 14−1-1214−82; ТC 14−1-1754−76; ТC 14−1-3639−83; ТC 14−1-3190−81; ТC 14−1-4042−85; ТC 14−1-3546−83; ТC 14−1-3528−83 |
| EP795 |
HN58W |
Manufacture of chemical welded equipment that is exploited in azotic acid solution as well as in composition of fluorine ions (f.e. in pickling fluorine-nitric-acid solutions). |
GOST 5632−72; ТC 14−1-2715−79; ТC 14−131−224−75; ТC 14−1-4362−87; ТC 14−131−756−88; ТC 14−1-4363−87 |
| EP758U |
HN63MB |
Manufacture of chemical welded equipment (in chemical, paper-and-pulp, petrochemical industries; in safety and pollution prevention equipment etc.). |
ТC 14−1-4881−90; ТC 14−3-1478−87; ТC 14−1-4202−87; ТC 14−131−755−85; ТC 14−1-4289−87; ТC 14−1-4734−89 |