Wire, pipe, sheet of aluminum AMG6H
|Grade||analogue||W. Nr.||Aisi Uns||En||Order|
|AMg6N||Buy from stock, view availability|
Sections and sheets of AMG6H grade are made from aluminum wrought alloy. The abbreviation AMG6H stands for:
- 6- the percentage of magnesium in the aluminum alloy;
- n - hardened.
Percentage composition (GOST 4784-97)
|≤0.4||≤0.4||0.5 - 0.8||0.02 - 0.1||91.1 - 93.68||≤0.1||0.0002 - 0.005||5.8 - 6.8||≤0.2||≤ 0.1|
Manganese, due to its properties, refines the structure, thereby increasing corrosion resistance and strength. Magnesium and copper are used to impart strength to the alloy. Manganese, because of its properties, refines the structure, thereby increasing resistance to corrosion and strength. In addition to the above elements, silicon and iron are also used in the composition. Fe is considered a harmful impurity, reduces strength and ductility. Si helps to reduce the harmful effects of iron by binding it to a certain extent. Due to the alloying, products of this grade are characterized by excellent ductility in processing and excellent resistance to cracking. Semiproducts are well machined and satisfactorily welded by contact and argon arc welding. Casting properties are improved by the addition of silicon.
The material becomes very hard through cold working, and ductility and workability are obtained through annealing and annealing. Excellent ductility is obtained after annealing and considerable self-strengthening after aging. Annealing. The alloy is heated to 500°C and upon cooling it acquires the ductility of pure aluminum. After the aging process, hardness and toughness become the leading properties. It takes about 24 hours at 20 degrees Celsius to accomplish natural aging. Artificial aging requires higher temperatures, but much less time. Upon completion of hardening, AK5 becomes a fairly reliable material that can be used at high loads.
- heat resistance;
- suitability for roller and spot welding;
- excellent electrical and thermal conductivity;
- low specific weight;
- reasonable price.
- low rate of cracking;
- resistance to vibration loading.
This material has hardness up to 65 MPa, average strength and high anticorrosive qualities. Due to such characteristics the sheet of AMG6H grade is widely used in industry. It is used in wagon production, shipbuilding and construction. Production of the sheet itself is regulated by the requirements
Mechanical engineering, aircraft manufacturing, high-speed trains, residential or industrial construction. The preferred use of this alloy is due to its greater hardness compared to aluminum. Alloy AMG6H is one of the main in the manufacture of pipes, profiles, sheets, wires and forgings. Tube of this brand is used for fragments of building structures, laying pipelines for special purposes.
|Mark .||Wall thickness in millimeters||Diameter in millimeters||Price per p.m.|
|AMG6H pipe||1 - 12||6 - 155||negotiated|
|Dural pipe D16T||1 - 12||6 - 155
|Dural tube D16||1 - 12||6 - 155
Where to buy a round, wire, tube, sheet, strip of aluminum AMG6H wholesale or in installments? Supplier "Auremo" offers to buy a circle, wire, tube, sheet, strip of aluminum AMG6N today on favorable terms. Large selection of semi-finished products in stock. Conformity to GOST and international quality standards, the price - the best from the supplier. Buy today. Wholesale customers price - favorable.
Buy, favorable price
Auremo" offers to buy aluminum on favorable terms. We have the widest range of products for large-scale productions in stock. We have attractive terms and for retail buyers. Always available in round tube, wire, sheet, strip aluminum AMG6H, price - due to the technological features of production without the inclusion of additional costs. Quality meets GOST and international standards. Optimal price from the supplier. Buy today. We are waiting for your orders.