Welded wire 07Х19н10б SV-07H19N10B, aisi 347
Equivalent
| Grade | analogue | W. Nr. | Aisi Uns | En | Order |
|---|---|---|---|---|---|
| 07Х19Н10Б | H-64 | ~347 | Buy from stock, view availability |
Relevance
Welding wire brand SV-07Х19Н10Б (SV-07Х19Н10Б-e) produce according to RD 03−613−03, GOST 2246−70 and technical conditi. 1220−005−84 823 540−2010. This wire is used for welding of products from corrosion-resistant chromium-Nickel steel grades 08KH18N12B, 08KH18N10T, 08KH18N12T and they are the same that operate in aggressive conditions, if the weld metal does not impose strict requirements for resistance to intergranular corrosion. This wire is also used for welding structures critical components of austenitic steels: 12Х18Н12Т, Х16Н13Б, Х20Н12Т-L, 12KH18N9T, and they are the same, operated at temperatures of 570−650°C, high pressure. Welding wire brand SV-07Х19Н10Б used for welding (welding) and the manufacture of electrodes of different types (OzL-7, TSN-12M, DH-15, CL-11).
The percentage composition of (GOST 2246−70)| C | Si | Mn | Ni | S | P | Cr | Nb |
| 0.05 — 0.09 | ≤ 0.7 | 1.5 — 2 | 9 — 10.5 | ≤ 0.018 | ≤ 0.025 | 18.5 — 20.5 | 1.2 — 1.5 |
The wire components of the ferritic phase is regulated with the agreement of the parties.
Supply
In rolls of 85−100 kg, frame, metal coil К415, K300, plastic spools D200, 300. Produced wire diameter: 0.8 mm; 1.2; 1 mm; 1,6, 2 mm and 3 mm (allowable under the order production of the required size).
Mechanical characteristics
Temporary tear resistance of high-alloy, alloy wire corresponds fully to all norms.
| The diameter, in millimeters | Temporary resistance to the rupture eof elektrodovin kgf/mm2(MPa) | Temporary resistance to rupture in kgf/mm2 (MPa) wire for surfacing |
|---|---|---|
| SV. 2,0 | 637−931 (65−95) | 686−1029 (70−105) |
| 2,0 | 686−980 (70−100) | 784−1176 (80−120) |
| 1,6 | 686−980 (70−100) | 882−1274 (90−130) |
| 0,8−1,5 | - | 882−1323 (90−135) |
Maximum deviations, with respect to the diameter of the wire conform to the following:
| Wire. The diameter, in millimeters | surfacing (welding) of | surfacing (welding) to |
|---|---|---|
| 0,8 | -0,07 | |
| 1,2−1,5 | - | -0,09 |
| 4,0; 5,0; 6,0 | -0,12 | -0,16 |
| 1,6; 2,0 | -0,06 | -0,12 |
| 2,5; 3,0 | -0,09 | -0,12 |
Position during the welding process
N45, B1, G, H1, 2, L1, 2.
Welding-technological characteristics
The welding of metal welding wire is carried out in argon (inert gas). This improves the quality of formation of the filling, root, face layers of the weld and stabilizes the arc.
Mechanical properties of weld metal (submerged arc welding)
| Brand of welding wire | Temporary resistance at break σ B, in MPa | Relative elongation, % | Yield limit, σ T, MPa | The viscosity of the shock, in j/cm2 KCU |
|---|---|---|---|---|
| SV-07Х19Н10Б | 620,5 | 34 | 389,8 | 112,5 — 122,4 |
The metal of the weld seam is not prone to intergranular corrosion.
To buy, best price
Supplier «Auremo» offers to buy welding wire wholesale or retail. Wide application the welding wire due to high quality and affordable price. Absolute control of all stages of the technological process allows the company «Auremo» to supply guaranteed quality products. Buy welding wire 07Х19н10б SV-07Х19Н10Б, aisi 347 today. The introduction of modern technologies gives the possibility of a basic range of metal to take orders for manufacture of products for individual orders for non-standard settings. We have the best ratio price-quality.