TU 14-1-223-72

MINISTRY OF FERROUS METALLURGY OF THE USSR


UDC 609.14.083.4−422−122−4
Group B32

Agreed:

Deputy Chief of the Chief
Technical Office

(Stroganov G.B.)
No. 084/108 dated 02/14/1972

ODR 3159−72 / 3

I approve:
Deputy Chief of the Chief

Of the MCHM Technical Office
(Shertel N.I.)
13/03−1972

High-temperature alloy rods for blades,
melted in vacuum furnaces

Technical conditions
TU 14−1-223−72
(Instead of ChMTU / TsNIICHM 1317−65)

Agreed:

Deputy Head of VIAM

(Sklyarov N.M.)

Head of the VIAM laboratory
(Glezer M.D.)
02.21.72 g.

Order 494
100 copies

Designed by:
Head laboratory
standardization TSNIICHM

(Kolyasnikova R.I.)

Committee of standards
measures and measuring instruments
at the Council of Ministers of the USSR
Registered on «16» .06.1972
according to the book of accounting for number 89624

1972 year

Sheet 1
TU 14−1-223−72

These specifications apply to hot-rolled bars made of heat-resistant alloys, melted in vacuum electric furnaces. EI598, EI437B, EI867, EI929, EP220, EP539, EP57, EP109 and EP238 alloys are smelted in vacuum arc electric furnaces, EI617 alloy in vacuum induction electric furnaces, EI826 alloy — both in vacuum arc and induction furnaces according to the order.

1. VARIETY

1.1. Alloys are supplied:

a) in the form of turned rods with a diameter of 20 to 40 mm. Dimensions are specified in the order;

b) in the form of hot-rolled rods with dimensions and tolerances according to table 1.

Table 1

steel grade Tolerances in mm in diameter:
20−32 mm 33−44 mm

KhN70VMTYu (EI617)

KhN70VMTYUB (EI598)
KhN77TYUR (EI437B)

KhN70VMFTU (EI826)

+1.0

-0.5

+1.5

-1.0

KhN62VMTYu (E867)

KhN55VMTFKYUR (EI929)

± 1.0 ± 1.5

KhN51VMTYUKFR (EP220)

KhN50VMTKFYU (EP57)

KhN58VMKYUR (EP238)

ХН60МЮВТ (ЭП539)

-

+1.5

-2.0

KhN56VMKYU (EP109)

+1.0

-2.0

+1.5

-2.5


Note: EP109 alloy is supplied with a diameter of 32 mm and above.

Sheet 2
TU 14−1-223−72

1.2. The ovality of hot rolled bars should not exceed the diameter tolerance. The curvature of the bars should not exceed 6 mm per 1 running meter. m.

1.3. The length of the rods must be a multiple of the size of the workpiece part (the multiplicity is negotiated in the order), but not less than 500 mm.

2. TECHNICAL REQUIREMENTS

2.1. The chemical composition of the alloys must meet the requirements of table. 2.

2.2. Bars are supplied thermally untreated.

2.3. Mechanical properties determined on heat-treated control samples must meet the requirements of table. 3.

2.4. A conclusion on the long-term strength of a batch of bars is given after the test time specified for each grade of alloy. The supplier plant continues testing one of the samples until destruction: for vacuum arc metal from every fifth heat, for induction metal from every 10th heat.

2.5. The hardness of the metal, determined on control samples, heat-treated according to the modes specified in table. 3, must meet the requirements of table. 4.

Table 4

Alloy grade Brinell hardness (indentation diameter), mm
EI671 3.3−3.7
EI598 3.3−3.7
EI437B 3.40−3.8
EI826 3.3−3.7
EI929 3.3−3.6
EI867 3.25−3.6
EP57 3.25−3.6
EP109 3.2−3.5
EP238 3.25−3.5
EP220 3.3−3.6
EP539 3.3−3.6

Sheet 3
TU 14−1-223−72

2.6. On the surface of the bars, there should be no captivity, cracks, flaws, sunsets, shells and slag inclusions.

The surface quality of the turned rods must meet the agreed standards.

On the surface of hot-rolled bars, local defects must be removed by gently scraping. The depth of cleaning of defects should not bring the rods beyond the minus deviation. Without stripping, individual small risks, dents and ripples are allowed within half the tolerance, counting from the face value.

2.7. The macrostructure of steel should not have traces of a shrinkage cavity, bubbles, cracks, fistulas, slag inclusions and voids visible without the use of magnifying devices.

The macrostructure of rods of all alloys provided for by these specifications and tested on heat treated macrotemplates must meet the requirements of the attached macrostructure scale.

Considered unacceptable: for vacuum-arc metal photos 15, 16, 17, 18, 21a, 21b, 22, 24, 25, 28a, 28b, 29, 30, 31, 32, 33, 34; for vacuum induction — photos 15, 16, 17, 18, 24, 25, 29, 30, 31, 32, 33, 34.

2.8. Fractures of thermally treated samples must meet the requirements of the fracture scale:

by the type of fractures — vacuum arc metal — 1−2 points, vacuum induction metal — 1−3 points and
by bundle — 1 point.

Note.
1. Defects subject to cleaning in accordance with clause 20 are not taken into account.

2. The consumer is given the right to reject, at the expense of the supplier, workpieces that have delamination and

Sheet 4
TU 14−1-223−72

other discontinuities identified by ultrasonic testing that do not fit into the norms on the scale of the macrostructure and the scale of fractures. In this case, the consumer plant, at the request of the supplier, is obliged to cut the workpieces selected by the supplier plant in an amount of at least 5 pieces from the submitted batch to confirm the presence of defects detected by the ultrasonic inspection by control of the macrostructure.

2.9. Regardless of the results of the inspection of bars, the consumer plant is given the right to reject finished parts at the expense of the supplier if defects of metallurgical origin are found on them after pickling — cracks, slag inclusions, hair lines and discontinuities visible to the naked eye.

3. RULES OF ACCEPTANCE AND TEST METHODS

3.1. Bars are presented for acceptance in batches from the same heat and diameter of the same size. The batch weight must be at least 150 kg. Delivery of lots of smaller weight is made with the consent of the consumer.

Note. Vacuum-arc melting is completed from no more than 10 ingots melted in a mold of the same cross-section, with an identical electric mode from the electrodes of the same initial melting.

3.2. If necessary, a control chemical analysis of any bar from those presented in the batch is carried out.

3.3. The dimensions and surface condition of all rods are monitored individually.

3.4. The control of mechanical properties is carried out in the finished grade on 2 samples for each type of test, taken from different

Sheet 5
TU 14−1-223−72

batch rods. Control samples are cut along the fiber from the center (along the axis) of rods with a diameter of up to 32 mm, inclusively and from the middle of the radius of rods with a diameter of more than 32 mm.

3.5. The control of the macrostructure and fracture is carried out on two samples, heat treated according to the regime provided in table. 3.

Samples are cut from two bars of each batch-melt for each type of tests, and samples for fracture control are taken in the transverse direction of the fiber (longitudinal fracture), and for control of the macrostructure — in the longitudinal direction of the fiber.

3.6. Long-term strength tests at high temperatures are performed in accordance with GOST 10145−62 on samples with a diameter of 5 mm, short-term tests — in accordance with GOST 9651−61 .

3.7. If the results of any test are unsatisfactory, a repeated test is carried out for this type of control on a double number of samples taken from the same rods. In case of unsatisfactory results of repeated testing of at least one sample, the melting batch is rejected.

The supplier plant is given the right to present the melt again after 100% control of the bars according to the indicator for which unsatisfactory results were obtained.

Note. Repeated and arbitration tests for determining long-term strength are performed on 2 samples according to the modes provided for in Table. 3.

4. MARKING, PACKAGING AND DOCUMENTATION

4.1. All bars must be stamped with the name of the supplying plant, alloy grade, heat number. Bars with a diameter of less than 30 mm are allowed to be branded with the conventional heat number with its decoding in the certificate.

Sheet 6
TU 14−1-223−72

The metal of vacuum-arc remelting should be branded additionally with the letters «VD», vacuum-induction — «VI».

4.2. The certificate establishing the compliance of this batch with the requirements of these technical specifications is signed by the quality control department of the supplying plant and the representative of the technical acceptance of the MAP.

Note. The certificate also includes the data of the primary tests, if the batch is recognized as suitable according to the results of the secondary test.

REGISTERED:
April 19, 1972

ZAV. TECHNICAL DEPARTMENT MFM USSR

/ A.S. KAPLAN /

Sheet 7
TU 14−1-223−72
table 2

Alloy grade Chemical composition,%
Carbon Silicon Manganese Chromium Nickel Titanium Aluminum Tungsten Molybdenum Vanadium Cobalt Iron Sulfur Phosphorus Boron Cerium Other elements
no more no more
KhN70VMTYu
/ ЭИ617 /
0.04−0.10 0.60 0.50 13.0−16.0 Main 1.80−2.30 1.70−2.30 5.0−7.0 2.0−4.0 0.10−0.50 - 5.0 0.010 0.015 0.02 0.02  
KhN70MVTYUB
/ ЭИ598 /
0.04−0.10 0.60 0.50 16.0−19.0 « 1.90−2.80 1.00−1.70 2.0−3.50 4.0−6.0 - - 5.0 0.010 0.015 0.01 0.02 Niobium 0.50 * 1.30
KhN77TYUR
/ EI437B /
0.04−0.08 0.60 0.40 19.0−22.0 « 2.40−2.80 0.60−1.00 - - - - 1.0 0.007 0.015 0.01 0.02 Lead n.b. 0.001

KhN70VMFTU

/ ЭИ826 /

0.04−0.10 0.60 0.50 13.0−16.0 « 1.70−2.20 2.40−2.90 5.0−7.0 2.5−4.0 0.20−1.00 - 5.0 0.009 0.015 0.02 0.02  
KhN55VMTFKYU
/ ЭИ929 /
0.04−0.10 0.50 0.50 9.0−12.0 « 1.4−2.0 3.6−4.5 4.5−6.5 4.0−6.0 0.20−0.80 12.0−16.0 5.0 0.010 0.015 0.02 -  
KhN62VMU
/ ЭИ867 /
n.b. 0.10 0.60 0.30 8.5−10.5 « - 4.2−4.9 4.3−6.0 9.0−11.5 - 4.0−6.0 4.0 0.010 0.015 0.02 0.02  
ХН50ВМТКФЮ
/ EP57 /
0.10−0.14 0.50 0.50 9.0−12.0 « 2.0−2.8 3.7−4.7 5.0−7.0 4.0−6.0 0.20−0.80 14.0−16.0 5.0 0.010 0.015 0.02 -  
KhN56VMKYU
/ EP109 /
n.b. 0.10 0.60 0.30 8.5−10.5 « - 5.4−6.2 6.0−7.5 6.5−8.0 - 11.0−13.0 1.5 0.010 0.015 0.02 0.02  

KhN58VMUFR

/ EP238 /

n.b. 0.08 0.40 0.30 7.5−9.0 « - 6.1−6.7 6.0−8.0 3.0−5.5 - 13.5−16.0 1.0 0.010 0.015 0.02 0.02  
KhN51VMTYUKFR
/ EP220 /
n.b. 0.08 0.50 0.50 9.0−12.0 « 2.2−2.9 3.9−4.8 5.0−7.0 5.0−8.0 0.2−0.8 14.0−16.0 3.0 0.009 0.015 0.02 -  

KhN60KYuVT

/ EP539 /

0.04−0.09 0.50 0.50 17.0−19.0 « 2.0−3.0 3.0−4.0 2.5−4.0 5.0−7.0 - - 4.0 0.010 0.015 0.02 0.02  

Note.
1. In all alloys, the presence of antimony, tin, bismuth, arsenic is allowed no more than 1 point of the spectral analysis scale.
2. Boron and cerium according to the instructions are introduced into the metal by calculation and are not determined by chemical analysis. In the alloys of the EI929 and EP57 grades, the introduction of cerium up to 0.02% is allowed by calculation.
3. For all grades of alloys, the content of residual copper is not more than 0.07%.
4. At the request of the consumer, specified in the order, the alloy of grade EI929 is supplied with a carbon content in the range of 0.08−0.12%, and in this case the alloy is marked with the code EI929A.

Sheet 8
TU 14−1-223−72

Table 3

Alloy grade Heat treatment of control samples High temperature short burst tests Long-term durability
Test temperature Tensile strength Relative Test temperature Constantly applied voltage Test time per hour, not less
    Elongation Constriction
° C kgf / mm 2 % ° C kgf / mm 2  
  σ in δ 5 ψ
1 2 3 4 five 6 7 eight nine
KhN70VMTYu (EI617) Heating to a temperature of 1190 ± 10 °, holding for 2 hours, cooling in air, heating to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 16 hours. at a temperature of 800 + 10 °, air cooling 800 70 7 ten 850 20 60
KhN70MVTYUB (EI598) Heating up to a temperature of 1200 ± 10 °, holding for 5 hours, cooling in air. Heating to a temperature of 1070 ± 10 °, holding for 8 hours, cooling in air and aging for 16 hours. at a temperature of 800 ± 10 °, air cooling 800 70 ten fourteen 800 28 50
KhN77TYUR Heating to a temperature of 1080 ± 10 °, holding for 8 hours, cooling in air and aging for 16 hours. at a temperature of 700 ± 10 °, air cooling 700 75 fifteen 20 700 46 40

Sheet 9
TU 14−1-223−72
(continuation of table 3)

1 2 3 4 five 6 7 eight nine
KhN70VMFTU-VD (EI826-VD) Heating up to a temperature of 1210 ± 10 °, holding for 2 hours, cooling in air. Heating up to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 16 hours. at a temperature of 800 ± 10 °, air cooling 850 60 eight 12 850 27 50
KhN70VMFTU-VI (EI826-VI) Also 850 65 12 18 850 27 75
KhN55VMTFKYU (EI929) Heating up to a temperature of 1220 ± 10 °, holding for 2 hours, cooling in air. Heating to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 8 hours. at a temperature of 850 ± 10 °, air cooling 900 58 eight 12 900 25 40
KhN62VMKYU (EI867) Heating to a temperature of 1220 ± 10 °, holding for 4−6 hours, cooling in air and aging for 8 hours. at a temperature of 950 ± 15 °, air cooling 900 58 eight 12 900 22 50
KhN60VMTKFYu (EP57) Heating up to a temperature of 1220 ± 10 °, holding for 4 hours, cooling in air. Heating up to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 2 hours. at a temperature of 950 ± 10 °, air cooling 900 60 nine 12 900 26 50

Sheet 10
TU 14−1-223−72
(continuation of table 3)

1 2 3 4 five 6 7 eight nine
KhN56VMKYU (EP109) Heating to a temperature of 122 ± 10 °, holding for 4−6 hours, cooling in air and aging for 8 hours. at a temperature of 950 ± 25 °, air cooling 900 65 4 eight 900 27 50
KhN51VMTYUKFR (EP220) Heating up to a temperature of 1220 ± 10 °, holding for 4 hours, cooling in air. Heating up to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 2 hours. at a temperature of 950 ± 10 °, air cooling 950 50 6 nine

940

Option I

900
Option II

22

Option I

28

Option II

40

Option I

50

Option II

ХН60МЮВТ (ЭП539) Heating up to a temperature of 1220 ± 10 °, holding for 2 hours, cooling in air. Heating up to a temperature of 1050 ± 10 °, holding for 4 hours, cooling in air and aging for 16 hours. at a temperature of 800 ± 10 °, air cooling 850 65 7 ten 900 20 50
KhN58VMKYUR (EP238) Heating to a temperature of 122 ± 10 °, holding for 4 hours, cooling in air and aging for 8 hours. at a temperature of 950 ± 25 °, air cooling 950 50 4 eight 940 22 50

Note:
1. During repeated tests, it is allowed to carry out repeated aging or increase the aging time (during heat treatment of new control samples) by no more than two times.

Sheet 11
TU 14−1-223−72
(continuation of table 3)

2. Heat treatment of the EI929 alloy is allowed to be carried out according to the following regime: heating up to 1200 ± 10 °, holding for 4 hours, air cooling. Heating up to 1050 ± 10 °. exposure for 4 hours, cooling in air and aging for 2 hours at 950 ± 10 °, cooling in air.
3. Bars of Ø32 mm and less from alloy EI929 are allowed to be passed with a long-term strength test at 900 ° — 22 kgf / mm 2 — 50 hours.
4. The variant of testing the long-term strength of EP220 alloy is specified in the order. In the absence of such a clause, tests are carried out according to option II. If unsatisfactory test results are obtained according to option II, repeated and arbitration tests are carried out according to option I.

MINISTRY OF FERROUS METALLURGY OF THE USSR
CENTRAL ORDER OF LABOR RED BANNER
SCIENTIFIC RESEARCH INSTITUTE OF FERROUS METALLURGY
THEM. I.P. BARDINE

107843, Moscow, B-b, 2nd Baumanskaya st., 9/23. Phone 267−01−02, ref. 1−00. For telegrams — Moscow
TSNIICHERMET Current account 240802 in the Bauman branch of the State Bank

No.TO-TU 14−1-223−72
AT 3

March 28, 1975

GL. ENGINEER OF ELECTROSTAL PLANT
T. ZHUCHIN V. N.

TO THE CHIEF ENGINEER OF ZLATOUSTOVSKY PLANT

TOV. N. N. Uchaev

TO THE CHIEF ENGINEER OF THE CHELYABINSK METAL PLANT

TOV. O. A. LABUNOVICH

TO THE CHIEF ENGINEER OF THE PLANT «DNEPROSPETSSTAL"
TOV. N. V. STETSENKO

TO THE CHIEF ENGINEER OF SIBELECTROSTAL METROL Plant

TOV. V. V. PONOMARENKO

HEAD OF LAB 26 VIAM

TOV. Berenson V.F.

REPLACE. HEAD OF THE DEPARTMENT OF THE MAP USSR
TOV. G. B. STROGANOV

REPLACE. HEAD OF THE MAIN TECHNICAL DEPARTMENT OF THE MFM USSR
TOV. N. I. SHEFTEL

REPLACE. HEAD OF THE UNION

TOV. B. P. Zuev

TO A MEMBER OF THE STATE COMMITTEE OF THE PRICE OF THE USSR Council of Ministers

TOV. A. I. ILYIN

HEAD OF VIFS

NIEChM

AMENDMENT LETTER
to TU 14−1-223−72 «Bars for blades made of heat-resistant alloys,
melted in vacuum furnaces «

  • In clauses 1.1 (Table 1), 2.1 (Table 2) and 2.3 (Table 3), replace the brand name KhN70VMFTU (EI826) with KhN70VMTYUF (EI826); KhN62MKYu (EI867) on KhN62MVKYu (EI867); KhN55VMTFKYUR (EI929) on KhN55VMTKYu (EI929).
  • In clause 3.6, the reference to GOST 9651−81 shall be replaced by GOST 9651−73 .

Reason: Entry into force from 01.01.75 GOST 9651−73, GOST 5637−72 and the decision of the Ministry of Aviation Industry and the Ministry of Chermet on 01.21.

Head technical department / A.S. Kaplan /

Ministry of ferrous metallurgy of the USSR


AGREED:

CHIEF ENGINEER CHIEF
TECHNICAL MANAGEMENT

Stroganov G.B.
June 23, 1975

UDC 609.14.083.4−422−122−4
Group B32

APPROVED:
REPLACE. CHIEF CHIEF

TECHNICAL MANAGEMENT MFM
SHERTEL N.I.
July 8, 1975

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM
OVENS

TECHNICAL CONDITIONS
TU 14−1-223−72

CHANGE # 2

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
1975 for No. 65185

Introduction date: 18.09.75

In section 1. Assortment, the note to table 1 shall be stated in the following edition:
«Note: EP109 alloy is supplied with a diameter of 24 mm and above.»

Agreed:

Deputy Head of VIAM

Sklyarov N.M.

Head laboratory number 8 TSNIICHM

Kolyasnikova R.I.

1975 65185

Designed by:
And about. chief engineer
plant «Electrostal"
Kosyev L.K.

REGISTERED: 18.08.75
Head technical department / A.S. Kaplan /

AGREED:

CHIEF ENGINEER CHIEF
TECHNICAL MANAGEMENT

/ G. B. STROGANOV /
«10» .12.1975

APPROVED:
CHIEF ENGINEER GLAVSPETSSTAL MFM

/ V. S. KULTYGIN /
«18» .12.1975

BARS FOR BLADES FROM HEAT RESISTANT ALLOYS MELTED OUT
IN VACUUM FURNACES

Technical conditions
TU 14−1-223−72

Change No. 3

Introduction date: 02.01.76

  • Table 4 points 2.5. for the EP539 alloy, set the Brinell hardness (dia. otp.) 3.20−3.60 mm instead of 3.30−3.60 mm.
  • Table 2, clause 2.1. to add note 5 in the following edition:
    «For EP539 alloy, carbon deviation minus 0.02% is allowed.»

Agreed:

Chief engineer of the plant
«Elektrostal"
/ Zhuchin V.N. /
12.12.75 g.

Head laboratory TsNIICHM

/ Kolyasnikova R.I. /

Designed by:
Deputy Head of VIAM
/ Sklyarov N.M. /
Head of laboratory

/ Berenson V.F. /

REGISTERED: 02.12.75
Head by the technical department of TsNIICHM A.S. Kaplan

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
13176 under No. 74577

Ministry of ferrous metallurgy of the USSR


AGREED:

Chief engineer chief
technical management

Stroganov G.B.
«20». 06.1976

UDC

Group B32

APPROVED:
Chief Engineer of VPO
«Soyuzspetsstal"
Kultygin V.S.
«___" _____ 1976

Heat-resistant blade rods
alloys melted in vacuum furnaces

Technical conditions
tu 14−1-223−72

Change No. 4

Introduction period: 06.08.76.

  • In table 3, in the part of grade ХН70МВТЮБ-ВД (ЭИ 598-ВД), make the following change:
    at a test temperature of 800 ° C, take the test time in hours at least 55 instead of 50.
  • Section 3.6. Replace the reference GOST 9651−61 with GOST 9651−73 .
  • Section 4 shall be supplemented with clause 4.3.
    «4.3. When assigning a Quality Mark to a product, the Quality Mark is designated in accordance with GOST 1 .9−67. «

Calculation of prices in accordance with the appendix to TU 14−1-223−72 with amendment No. 4.

Agreed:

Deputy Head of VIAM

Sklyarov N.M.

Head of the VIAM laboratory
Berenson V.F.

Head laboratory number 8 TSNIICHM

Kolyasnikova R.I.

Designed by:
Chief engineer of the plant
«Elektrostal"
Zhuchin V.N.

REGISTERED TSNIICHM: 06.07.76
Head department of standardization
ferrous metallurgy L. V. Meandrov .

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
07.76 under No. 84289

23.7.76. 84289

Appendix to TU 14−1-223−72
with rev. No. 4

CALCULATION OF PRICES

Wholesale prices for high-grade steel grade EI598-VD are calculated using the normative-parametric method in accordance with clause 13 of the «General Instructions» to the price list 01−02, part 1.

K steel according to TU 14−1-223−72 with rev. No. 4 has the following additional requirements:

  • The test time for mechanical properties at a temperature of 800 ° C is taken in n.m. hours. 55 instead of 50.
  • When assigning a quality mark to products, the metal is additionally marked with the State quality mark in accordance with GOST 1 .9−67.

Wholesale prices for section steel grade EI598-VD according to TU 14−1-223−72 with rev. No. 4 to keep at the level of list prices according to TU 14−1-223−72, price list 01−02, part 1, pp. 102−103.

steel grade Technical conditions Wholesale price in rubles per ton. section steel size, in mm
20−21 22−24 25−30 31−40 41−50
KhN70MVTYUB-VD (EI598-VD) TU 14−1-223−72 with rev. No. 4 9870 9850 9820 9810 9800


Note:

1) Prices are based on normal length steel.
2) The above steel is subject to the «General instructions» of price list 01−02.

Calculation of wholesale prices
COMPOSED BY:
Plant «Electrostal"
Chief Engineer
V.T. Pankratov
May 31, 1976.

Calculation of wholesale prices
AGREED:
VIAM

Deputy Of the chief

N. M. Sklyarov

«___" ____ 1976

Wholesale prices agreed:

And about. head department of cost, profitability 05.06.76
and pricing of IECHM I. Martynov.

cd
May 28, 1976

Ministry of ferrous metallurgy of the USSR


AGREED:

Chief engineer chief
technical management

Stroganov G.B.
«16» .08.1976

UDC

Group B32

APPROVED:
Chief Engineer of VPO
«Soyuzspetsstal"
Kultygin V.S.
«12» .08.1976

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM
OVENS

Technical conditions
tu 14−1-223−72

Change No. 5

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
06.10.76 for No. 89549

Introduction date: 08.10.76

  • The term of validity of the TU is extended until 01/01/83.
  • Clause 3.6. Replace GOST 9651−61 with GOST 9651−73 .

AGREED:

Deputy Head of VIAM

Sklyarov N.M.

Head of the VIAM laboratory
Berenson V.F.

Head laboratory of standardization
TsNIICHM

Kolyasnikova R.I.

DEVELOPED:
Chief Engineer
plant «Electrostal"
Zhuchin V.N.

Registered by TsNIICHM: 09/08/76

Head department of standardization
ferrous metallurgy L. V. Meandrov .

6.10.76 89549

1976 year

Ministry of ferrous metallurgy of the USSR


AGREED:

Chief of the Chief
technical management of the USSR Ministry of Aviation Industry

A.G. Bratukhin

«__" ____ 1981

UDC

Group B32

APPROVED:
Chief Engineer of VPO
«Soyuzspetsstal» MCHM USSR
V.S. Kultygin
«29» .12.1981

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM
OVENS

TECHNICAL CONDITIONS
tu 14−1-223−72

Change No. 7

Introduction date: 28.03.82

1. Clause 2.7. The second paragraph shall be adopted in a new edition:
«The macrostructure of rods of all alloys is checked on heat-treated macro-templates according to GOS 22838−77 and must comply with the requirements of table. five.

Table 5

Scale name Scale no. Score, not worse
General banded heterogeneity 3 12
Variegated macrostructure 4 1, 2, 3 left
A variegated macrostructure with a common banded heterogeneity five 12
Grain size in the macrostructure 6 1, 2, 3

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
82.04.02 No. 89624/07

2

2. Clause 2.7 shall be supplemented with notes 1 and 2.

Note 1. For rods for hot working by pressure, the uneven-grain macrostructure (scale 4) should be no worse: 1 (both), 2 (left) and 3 (left) points.

Note 2. Until 07/01/83, when unsatisfactory results are obtained or in disputable cases, the assessment of the macrostructure is carried out according to the macrostructure scales attached to TU 14−1-223−72.

Considered unacceptable: for vacuum-arc metal photos 15, 16, 17, 18, 21a, 21b, 22, 24, 25, 28a, 28b, 29, 30, 31, 32, 33, 34; for vacuum induction — photos 15, 16, 17, 18, 24, 25, 29, 30, 31, 32, 33, 34.

3. Clause 2.8 shall be adopted as amended and supplemented with note No. 3:

«Fractures of thermally treated samples should not exceed according to GOST 22838−74:

by the general banded heterogeneity — damn. 3 «a"
delamination is not allowed.

«Note 3. Until 07/01/83, upon receipt of unsatisfactory results or in disputable cases, the assessment of the breaks is carried out according to the scales attached to TU 14−1-223−72».
In terms of the type of fractures, they should not exceed: for a vacuum-arc metal 1−2 points, for a vacuum-induction metal 1−3 points and for delamination (for high-pressure and VI metal) — 1 point.

4. Clause 3.5. The first paragraph is to be adopted as amended: «Control of the macrostructure and fracture is carried out according to GOS T22838−77 on two samples, thermally treated according to the regime provided in table. 3.

5. The term of the TU was extended until 01.01.87.

Agreed:

Deputy Head of VIAM

N.M. Sklyarov

«30» .12.1981

Head of the VIAM laboratory
V.F. Berenson

«29» .12.1981

Designed by:
Head laboratory of standardization
specialist. steel TSNIICHM
V.T. Ababkov
«24» .12.1981
Head of the Technical Department
MCHM USSR
M.P. Kolyasnikov
«26» .12.1981

Registered by TsNIICHM: 31.12.81

Head department of standardization
ferrous metallurgy V.T. Ababkov
«____" _______ 1981

OKP

APPROVED BY
manufacturer
«11» .09.1981


AGREED:

with the base organization
on standardization
«18». 03.1982
with the customer
«08» .09. 1981 year
Right: ______

UDC

Group B32

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM
OVENS

TECHNICAL CONDITIONS
tu 14−1-223−72

(Amendment No. 8)

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
82.05.11 No. 89624/08

Introduction date: 17.04.82

1. In table 1, in terms of the assortment of alloy KhN62MVYu (EI867) add hot-rolled rods with a diameter of 13−16 mm with maximum deviations in diameter:

  • Ø13 mm ± 0.75−1.0 mm;
  • Ø14 mm ± 1.0 mm.

2. To add a note to Clause 3.5:
«Bars with a diameter less than Ø20 mm on the fracture of heat-treated samples is not controlled.»

3. Calculation of prices according to the appendix to TU 14−1-22−72 with amendment No. 8.

Registered: 17.03.82

Appendix to TU 14−1-223−72
with change No. 8
in prices from 01.01.82

WHOLESALE PRICES
for high-grade steel grade ХН65МВКЮ (ЭИ867) -ВД

steel grade Technical conditions Wholesale price in rubles per ton of section steel, size in mm
13 fourteen fifteen sixteen
KhN62MKVYU (EI867) -VD Rev. to TU 14−1-223−72 18000 17970 17910 17880

Hot-rolled bars are subject to «General surcharges and discounts"
price list No. 01−08, ed. 1980 year

Head cost department,
profitability and pricing of IECHM
L.N. Shevelv
February 12, 1982

Ministry of ferrous metallurgy of the USSR


AGREED:

Chief of the Chief
technical management of the USSR Ministry of Aviation Industry

A.G. Bratukhin

«07» .07.1983

UDC

Group B32

APPROVED:
Chief Engineer of VPO
«Soyuzspetsstal» MCHM USSR
N.I. Drozdov
«01» .08.1983

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM FURNACES

TECHNICAL CONDITIONS
tu 14−1-223−72

Change No. 9

Introduction date: 10.12.83

Extend the validity period of Note 2 to clause 2.7 of the Technical Conditions until 01.01.85 .

Agreed:

Deputy Head of VIAM

E. B. Kachanov

«30» .12.1981

Head of laboratory
steels and alloys TSNIICHM
V.T. Ababkov

«29» .12.1981

Designed by:
Plant «Electrostal"
Chief Engineer

K. Ya. Fedotkin
22.06.83 g.

Registered by TsNIICHM: 11/15/83.

Head department of standardization
ferrous metallurgy V.T. Ababkov

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
84.01.25 for No. 89624/09

Ministry of ferrous metallurgy of the USSR


AGREED:

Chief of the Chief
technical management
MAP USSR

A.G. Bratukhin

«30» .11.1984

UDC

Group B32

APPROVED:
Chief Engineer of VPO
«Soyuzspetsstal"
MCHM USSR
N.I. Drozdov
«30» .12.1984

BARS FOR SHOVELS FROM HEAT RESISTANT
ALLOYS MELTED IN VACUUM FURNACES

TECHNICAL CONDITIONS
tu 14−1-223−72

Change No. 10

Introduction date: 12.02.85

1. To supplement the introduction with a paragraph as amended:

«Indicators of the technical level established by these technical specifications meet the requirements of the highest quality category."

2. Clause 1.1. Subparagraph «a» shall be reworded:

a) in the form of turned rods with a diameter of 20 to 40 mm, taking into account the specialization of rolling mills. Dimensions are specified in the order.

Maximum deviations in the diameter of the turned rods should not exceed ± 0.4 mm.

STATE
COMMITTEE OF STANDARDS
Council of the USSR Ministry
Registered and entered in the register
state registration
84.11.26 for No. 89624/10

2
Change No. 10
to TU 14−1-223−72

Table 1 should be supplemented with new dimensions for hot-rolled bars of the following alloys:

Alloy grade Limit deviations in diameter, mm
Ø45 Ø55
KhN70VMTYUF-VD (EI826-VD)    
KhN70VMTYUF-VI (EI826-VI) ± 1.5  
ХН60МЮВТ (ЭП539)

+1.5

-2.5

 
ХН70МВТЮЬ (ЭИ598)   ± 1.5
ХН62МВКЮ (ЭИ867)  

+1.5

-2.5

ХН55ВМТКЮ (ЭИ929)    


Set maximum deviations in diameter for hot-rolled rods Ø33−44 mm of alloy KhN61VMTYUKFR (EP220) to + 1.0−4.0 mm.

3. Clause 1.3 shall be stated in the wording:

«The length of the bars must be at least 500 mm or a multiple of the length of one part (the multiplicity is specified in the order).

4. Clause 2.3 table 3. Write in the columns:

  Tensile strength Constantly applied voltage
  σ in
n / mm 2
kgf / mm 2)
n / mm 2
kgf / mm 2)
KhN70VMTYu (EI617) 690 (70) 200 (20)

3
Change No. 10
to TU 14−1-223−72

KhN70VMTYu (EI617) 690 (70) 200 (20)
KhN70VMTYUB (EI 598) 690 (70) 270 (28)
KhN77TYUR (EI437B) 740 (75) 450 (46)
KhN70VMTYUF-VD (EI826-VD) 590 (60) 260 (27)
KhN70VMTYUF-VI (EI826-VD) 640 (65) 260 (27)
ХН55ВМТКЮ (ЭИ929) 570 (58) 250 (25)
ХН62МВКЮ (ЭИ867) 570 (58) 220 (22)
KhN50VMTKFYu (EI57) 590 (60) 250 (26)
KhN56VMKYU (EP109) 640 (65) 260 (27)
KhN51VMTYUKFR (EP220) 490 (50) 220 (22)
ХН60МЮВТ (ЭП539) 640 (65) 200 (20)
KhN8VMKYUR (EP238) 490 (50) 220 (22)

5. Extend the validity period of Note 2 to Clause 2.7 and Note 3 to Clause 2.8 until 01.01.87.

6. Clause 4.1 shall be reworded:

«All bars must be stamped with the heat number, brand and trade mark of the plant»:
— each bar with a diameter of 30 mm or more;
— with a diameter less than 30 mm — 10% of the bars of the batch-melting, but not less than 10 bars.

Marking is applied at a distance of no more than 50 mm from the end of the bar, with a diameter of up to 30 mm, bars with a diameter of 30 mm and more are branded at the end.

Bars are allowed to be branded with the conventional heat number with its decoding in the quality document.

4
Change No. 10
to TU 14−1-223−72

The metal of vacuum-arc remelting should be branded additionally with the letters «VD», vacuum-induction «VI».

7. Introduce section 5.

«five. TRANSPORTATION AND STORAGE
5.1. Transportation and storage according to GOST 7566−81 .
Note: The wholesale price is set according to the attachment. «

AGREED:

Deputy Head of VIAM

N.M. Sklyarov

Head of the VIAM laboratory

V.F. Berenson

«30» .12.1981

Head laboratories for special
steels and alloys TSNIICHM
V.T. Ababkov

DEVELOPED:
Plant «Electrostal"
Chief Engineer

K. Ya. Fedotkin

Registered by TsNIICHM: 11/12/84

Head department of standardization
ferrous metallurgy V.T. Ababkov

five
application
to TU 14−1-223−72 with rev. ten

WHOLESALE PRICES
for high-grade steel grades according to TU 14−1-223−72 with rev.

Alloy grade Brand code Wholesale price in rubles per ton. bar steel in mm
13 fourteen fifteen sixteen 20−21 22−24 25−30 31−40 41−50 52−70
1 2 3 4 five 6 7 eight nine ten eleven 12
KhN70VMTYUF-VI (EI826-VI) 8855 18000 17970 17910 17880 10290 10230 10130 10,050 9960 9950
KhN70VMTYUF-VD (EI826-VI) 8855 11950 11880 11760 11670 11560 11550
KhN60MYuVT-VD (EI539-VD) 8834 9300 9240 9150 9070 8970 8960
KhN70MVTYUB-VD (EI598-VD) 8854 10860 10780 10690 10600 10500 10490
KhN62MVKYU-VD (EI867-VD) 8841 17770 17670 17500 17360 17210 17200
KhN55VMTKYU-VD (EI929-VD) 8824 19830 19710 19530 19380 19200 19190
KhN51VMTYUKFR-VD (EI220-VD) 882023 20260 20140 19950 19800 19620
Alloy grade Brand code NCHP tn. bar steel in mm
13 fourteen fifteen sixteen 20−21 22−24 25−30 31−40 41−50 52−70
1 2 3 4 five 6 7 eight nine ten eleven 12
KhN70VMTYUF-VI (EI826-VI) 8855 997 978 950 930 906 895
KhN70VMTYUF-VD (EI826-VI) 8855 979 956 924 901 874 862
KhN60MYuVT-VD (EI539-VD) 8834 982 958 924 896 866 854
KhN70MVTYUB-VD (EI598-VD) 8854 988 964 933 908 880 868

6
application
to TU 14−1-223−72 with rev. ten

KhN62MVKYU-VD (EI867-VD) 8841 1390 1350 1360 1340 1300 1270 1230 1190 1150 1140
KhN56VMTKYU-VD (EI929-VD) 8824 1310 1280 1230 1200 1160 1140
KhN55VMTKYU-VD (EI929-VD) 8823 1310 1270 1230 1200 1160 1140


Notes:

  • When supplying section steel Ø20−40 mm in a turned condition (at the request of the customer), an additional charge of 18% will be charged. Pr-nt No. 01−08, p. 184 and pr-nt NCHP No. 01−08−1980 / 8, p. 212.
  • Wholesale prices and LSPs are determined for steel of unmeasured length. When delivering section steel of multiple length (at the request of the customer), an additional 4% surcharge will be charged. Pr-nt No. 01−08, p. 183 and pr-nt NCHP No. 01−08−1980 / 8, p. 210.

Wholesale prices agreed
Head laboratory of the current
IECHM pricing

A.I. Ilyin