TU 14-1-394-72

USSR MINISTRY OF FERROUS METALLURGY

AGREED:

Main Directorate of Chemical Engineering

Ministry of Chemical

and oil engineering

" " 1972

 

UDC 669.14.018.8-413

Group B33

I APPROVE:

Deputy Chief of the Main

Technical Management

Ministries of Black

metallurgy of the USSR

SHEFTEL N.I.

" " 1972

THICK SHEET STEEL

HIGH ALLOY CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

(Replaces ChMTU 2780-51 and ChMTU/TsNIICM 222-59)

Introduction date: 30/04-73. For the period: Unlimited.

AGREED:

Chief Engineer of the Ural

chemical engineering plant

buildings

GLOBIN N.G.

"10" 08 1972

 

DEVELOPED BY:

Kuznetsk Metallurgical

plant

Chief engineer of the plant

KRITININ I.A.

" " 1972

1972

These technical conditions apply to the supply of thick-sheet, hot-rolled, high-alloy, corrosion-resistant steel with a thickness of over 50 to 75 mm.

1. ASSORTMENT

1.1. The sheet sizes are set according to the specification of the supplier plant, with a width of no more than 1000 mm, while the weight of the sheet should not exceed 950 kg. Permissible deviations in thickness in accordance with GOST 5681-57, in length and width plus 50 mm.

It is possible to supply sheets without cutting edges.

2. TECHNICAL REQUIREMENTS

2.1. Sheets are made of steel grades 2X13, X18N10T, 0X18N10T, X17N13M2T, 0X17N13M2T, X17N13M3T.

The chemical composition of steel must comply with GOST 5632-61.

2.2. Depending on the surface condition, sheets are supplied in two groups A and B according to GOST 7350-66.

2.3. The surface quality of the sheets must comply with the requirements of GOST 7350-66.

The stripping depth should not exceed 2 mm.

2.4. Sheets are supplied without editing.

2.5. Mechanical properties, susceptibility to intercrystalline corrosion and macrostructure must comply with GOST 7350-66.

2.6. At the customer's request, steel grades 0X18N10T and 0X17N13M2T are supplied with a yield strength (conditional) test at a temperature of 350°, which must be at least 18 kgf/ mm2 .

3. ACCEPTANCE RULES AND TEST METHODS

3.1. Sheets are presented for acceptance in batches consisting of sheets from the same heat and a homogeneous group of thicknesses within 10 mm.

          TU 14-1-394-72
         
Change Sheet Doc. No. Subp. Date
Developer.      

High-alloy thick sheet steel

corrosion resistant

Lit. Sheet Sheets
Checked             2 3
     
N. counter.      
Approved.      
Inv. No. Sub. and date Exchange inv. No. Inv. No. duplicate. Sub. and date
         

- 2 -

3.2. Tensile testing at a temperature of 350° is carried out in accordance with GOST 9651-61.

3.3. All other conditions regarding acceptance rules, testing methods, marking and packaging in accordance with GOST 7350-66.

Head of Technical

department of the Central Research Institute of the Humanitarian Mechanics

 

Registered:

October 30, 1972

/Kaplan A.S./

          TU 14-1-394-72 Sheet
          3
Change Sheet Doc. No. Subp. Date
Inv. No. Sub. and date Exchange inv. No. Inv. No. duplicate. Sub. and date
         

USSR MINISTRY OF FERROUS METALLURGY

CENTRAL ORDER OF THE RED BANNER OF LABOR

RESEARCH INSTITUTE OF FERROUS METALLURGY

named after I.P. BARDIN

107843, Moscow, B-5, 2-ya Baumanskaya st., bldg. 9/23. Phone 257-01-02. reference 1 - 00. For telegrams - Moscow

TsNIICHERMET Settlement account 240802 in the Bauman branch of the State Bank

No. TO/TU- 14-1-394 "23" April 1975

 

TO THE CHIEF ENGINEER OF THE KUZNETSK IRON AND STEEL WORKS

Comrade KRITININU I.N.

TO THE CHIEF ENGINEER OF THE URAL CHEMICAL PLANT

CHINESE MECHANICAL ENGINEERING

Comrade GLOBINU N.G.

TO THE CHIEF ENGINEER OF BELGOROD BOILER CONSTRUCTION

BODY FACTORY

Comrade GORBATENKO I.M.

DEPUTY CHIEF OF THE MAIN TECHNICAL DEPARTMENT

LENIYA WJC USSR

Comrade SHEFTELYU N.I.

TO THE CHIEF OF THE MAIN DEPARTMENT OF CHEMICAL

MECHANICAL ENGINEERING OF THE USSR MINISTRY OF CHEMISTRY AND OIL AND GAS

comrade KURAMZHIN A.V.

DEPUTY CHIEF OF SOYUZGLAVMETALL

Comrade ZUEV B.P.

TO THE MEMBER OF THE STATE COMMITTEE OF PRICES OF THE CM OF THE USSR

Comrade Ilyin A.I.

HEAD OF VIFS comrade MAKARCHUK I.N.

Research Institute of ECM

AMENDMENT LETTER

to TU 14-1-394-72 "High-alloy thick sheet steel

"corrosion resistant"

1. In paragraph 2.1, paragraph 2.6, replace the names of the grades: 2X13 with 20X13 (2X13); X18N10T with 12X18N10T (X18N10T); 0X18N10T with 08X18N10T (EI914); X17N13M2T with 10X17N13M2T (EI448); 0X17N13M2T with 08X17N13M2T; X17N13M3T with 10X17N13M3T (EI432).

2. In paragraph 2.1, replace the reference to GOST 5632-61 with GOST 5632-72.

3. In paragraph 3.2, replace the reference to GOST 9651-61 with GOST 9651-73.

Basis : GOST 5632-72 and GOST 9651-73 entered into force on 1.01.75.

Head of Technical Department /A.S. Kaplan/

Ministry of Ferrous Metallurgy of the USSR

OKP 09 8600

AGREED

Chief Engineer

VPO Soyuzkhimmash

USSR Ministry of Chemical Engineering

"29" 03 1979

 

UDC 669.15-41

Group B33

I APPROVE

Deputy Chief

Technical management

USSR Ministry of Ferrous Metallurgy

Yu.E. Kuznetsov

"2" 04 1979

THICK SHEET STEEL

HIGH ALLOY CORROSION RESISTANT

Technical conditions

TU 14-1-394-72

Change #1

Implementation date: 09.05.79

1. The validity period of the TU is limited until 01.05.83.

2. In paragraph 1.1, replace the reference to GOST 5681-57 with GOST 19903-74.

3. Clause 2.2 shall be amended as follows:

"Depending on the surface condition, sheets are supplied in three groups M4b, M5b and

M5g according to GOST 7450-77."

4. In paragraphs 2.3, 2.5 and 3.3, replace the reference to GOST 7350-66 with GOST 7350-77.

AGREED

Chief Engineer

Ural Chemical Plant

whom mechanical engineering

N.G. Globin

"14" 02 1979

Head of the standard laboratory

special steels

Central Research Institute of Human Microbiology

V. T. Ababkov

"21" 02 1979

 

DEVELOPED

Chief Engineer

Kuznetsk Metallurgical

plant

V.V. Makrushin

"10" 01 1979

REGISTERED in the Central Research Institute of the Black Sea: 04/09/79

Head of the Standardization Department

ferrous metallurgy

L.V. Meandrov

"2" 01 1979

Ministry of Ferrous Metallurgy of the USSR

   

I APPROVE:

Deputy Head of Technical

Administration of the USSR Ministry of Ferrous Metallurgy

Yu.E. Kuznetsov

«14» 04 1983

HIGH ALLOY THICK SHEET STEEL

CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #2

Introduction date: 12.06.83

The validity period of the technical conditions has been extended until 01.05.86.

Note: Wholesale prices are included in the reference book to the price list 01-02 edition 1980.

   

Developed by:

Head of the standardization laboratory

special steels TsNIIChM

V. T. Ababkov

« » 03 1983

Registered in the Central Research Institute of the Black Sea: 12.05.83

Head of the Standardization Department

ferrous metallurgy

V. T. Ababkov

Ministry of Ferrous Metallurgy of the USSR

AGREED:

Head of Technical

Management of the USSR Ministry of Chemical Machine Building

A.M. Vasiliev

"29" December 1984

 

I APPROVE:

Deputy Head of Technical

whom the USSR MCChM management

Yu.E. Kuznetsov

"29" 12 1984

HIGH-STRENGTH PLATE STEEL

CORROSION RESISTANT GLASS

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #3

Implementation date: 23.07.85

Section 2, paragraph 2.1. supplement with steel grades 08X22N6T and 08X21N6M2T.

The following note should be added to the TU: "Prices are approved by the USSR State Committee on Prices and are published in additional price lists."

Agreed:

Deputy Director of NIIKHIMMASH

Yu.I. Kipriyanov

 

DEVELOPED BY

Head of the laboratory of the st-

darting of special steels

Central Research Institute of Human Microbiology

V. T. Ababkov

" " 1984

Registered by TsNIIChM: 23.01.85

Head of the standardization department

ferrous metallurgy

V. T. Ababkov

Appendix to TU 14-1-394-72

with change #3

WHOLESALE PRICES

on high-alloy corrosion-resistant thick sheet steel

Steel grade Wholesale price in rubles per ton of sheets with thickness in mm
52-60 65-95

08Х21Н6М2Т

08Х22Н6Т

1590

1040

1640

1070

Note: 1. Wholesale prices are set for trimmed sheets of normal flatness in a heat-treated and etched condition M3b.

2. The general instructions of price list No. 01-10, 1980 edition, apply to this product.

Head of the Laboratory of Economics

justification of prices for new products

IE TsNIICHM A.I. Ilyin

Ministry of Ferrous Metallurgy of the USSR

OKP 09 8600

AGREED

Head of Technical

Management of the USSR Ministry of Chemical Machine Building

A.M. Vasiliev

" " June 1985

 

UDC 669.15-41

Group B 33

I APPROVE

Deputy Head of Technical

Management of the USSR World ChM

Yu.E. Kuznetsov

" " 07 1985

HIGH ALLOY THICK SHEET STEEL

CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #4

Introduction period:

The note to the TU shall be stated as follows: "Wholesale prices for products made of steel grades 08X22N6T and 08X21N6M2T according to the appendix."

AGREED

Deputy Director

NIIKHIMMASH

Yu.I. Kipriyanov

" " 1985

 

DEVELOPED BY

Head of the standard laboratory

special steels of the Central Research Institute of ChM

V. T. Ababkov

1985

Registered by TsNIIChM: 03.09.85

Head of the Standardization Department

ferrous metallurgy

V. T. Ababkov

" " 1985

USSR MINISTRY OF FERROUS METALLURGY

09 8600

AGREED:

Chief Engineer of the VPO "Soyuz-

Himmash" Ministry of Chemical Engineering of the USSR

"25" 12 1985

 

UDC 669.15-41

Group B33

I APPROVE:

Deputy Head of Technical

Management of the USSR World ChM

Yu.E. Kuznetsov

"17" 01 1986

HIGH-ALLOY THICK SHEET STEEL

CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #5

Introduction period:

AGREED:

Chief Engineer of the Ural

chemical engineering plant

buildings

N.G. Globin

"22" 10 1985

Head of the standardization laboratory

special steels of the Central Research Institute of Black Sea Mechanics

V. T. Ababkov

« 29 » 12 1985

 

DEVELOPED BY:

Chief Engineer of Kuznetsk

metallurgical plant

N.A. Fomin

« 29 » 12 1985

1. Clause 1.1. The second sentence shall be set out as follows: "Tolerances for thickness plus 0.6 mm, minus 1.5 mm, for length and width plus 50 mm."

2. Clause 3.2. Replace the reference GOST 9651-73 with GOST 9651-84.

Registered by TsNIIChM: 06.02.86

Head of the Department of Standardization of Black

metallurgy

V. T. Ababkov

1986

Ministry of Ferrous Metallurgy of the USSR

OKP 09 8600

Agreed

Head of the Main Technical Department

management of the Ministry of Heavy Machine Building

V.T. Shaturov

"14" 10 1986

Agreed

Deputy Chief

Chief Technical Officer

management of the Ministry of Chemical Machine Building

V.N. Ivanov

"16" 10 1986

 

UDC 669.15-41

Group B33

I approve

Deputy Chief

Technical management

USSR Ministry of Ferrous Metallurgy

Yu.E. Kuznetsov

"24" 08 1986

HIGH ALLOY THICK SHEET STEEL

CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #6

The deadline for introduction is 26.03.87

Agreed

Director of VNIPIokeanmash

B.P. Loktionov

« 29 » 12 1986

Director of VNIPIrudmash

V.G. Bovduy

"16" 09 1986

Deputy Director

Research Institute of Chemical Machinery

Yu.I. Kipriyanov

"20" 09 1986

Head of the standardization laboratory

special steels and alloys TsNIIChM

V. T. Ababkov

"23" 12 1986

 

Developed by

Director of the Institute of Quality

military steels of the Central Research Institute of the Black Sea Marine

S.A. Golovanenko

"26" 06 1986

Amendment No. 6 to TU 14-1-394-72

Section 2, paragraph 2.1 shall be supplemented with steel grade 09Х17Н7Ю.

The note to the technical specifications shall be set out as follows:

Wholesale prices for steel grade 09Х17Н7Ю products according to the appendix.

Registered by TsNIICHERMET:

Head of the Standardization Department

ferrous metallurgy

V. T. Ababkov

"26" 12 1986

Appendix to TU 14-1-394-72

with change #5

WHOLESALE PRICES

on high-alloy corrosion-resistant thick sheet steel

Steel grade Wholesale price in rubles per ton of sheets with thickness in mm
52-60 65-75
09Х17Н7Ю 937 975

Note: 1. Wholesale prices are set for trimmed sheets of normal flatness in

in heat-treated and etched condition M3b.

2. The "General Instructions" of the price list apply to this product.

№01-10 ed. 1980

Acting Head of the Laboratory of Excellence

development of pricing methodology

and the Institute's current price lists

Economy of the Central Research Institute of the Black Sea Microbiology

M.K. Sorokina

OKP 09 8600

APPROVED

in the prescribed manner

"29" 01 1987

AGREED

in the prescribed manner

with interested organizations

Right:

signature and seal

 

UDC

Group B33 0

HIGH ALLOY THICK SHEET STEEL

CORROSION RESISTANT

TECHNICAL SPECIFICATIONS

TU 14-1-394-72

Change #7

Valid from 10.05.87

until 10.05.87

1. Supplement section 2 "Technical requirements" with clause 2.7

"2.7. In sheets of steel grades 12Kh18N10T, 08Kh18N10T, 10Kh17N13M2T, 08Kh17N13M2T, 10Kh17N13M3T, the conditional yield strength is determined at a residual deformation of 1% / σ 1.0 /. The yield strength values must comply with the following standards of the table:

Steel grade 08Х18Н10Т

12Х18Н10Т, 10Х17Н13М2Т,

10Х17Н13М3Т, 08Х17Н13М2Т

σ 1.0 N/mm 2 /kgf/mm 2 /

not less than

250 /25/ 270 /27/

The results are optional and must be included in the certificate."

2. Supplement section 3 "Acceptance rules and testing methods" with clause 3.4:

"3.4. The conditional yield strength σ 1.0 is determined graphically using a tensile stress diagram with a recording scale along the elongation axis of at least 50:1. In the absence of appropriate equipment, it is permissible to determine σ 1.0 by recording a diagram with a scale along the elongation axis of at least 10:1."

REGISTERED 10.02.87

Ministry of Ferrous Metallurgy of the USSR

   

UDC 669.14.018.8-413

Group B 33

I APPROVE

Deputy Director of the Central Research Institute of Ferrous Metallurgy

12 V.A. Sinelnikov

"20" 01 1989

HIGH ALLOY THICK SHEET STEEL

CORROSION RESISTANT

Technical conditions

TU 14-1-394-72

Change #8

The term of introduction is from 23.03.89

AGREED:

Chief Engineer of the Kuznetsk Metallurgical Plant

Telegram No. 277128/174/3 dated 10.01.89.

Orzheh

Head of State Acceptance

Kuznetsk Iron and Steel Works

12 V.A. Skorokhodov

« 20 » 01 1989

Chief engineer of the Uralhimmash plant

Telegram No. 221303/277 dated 11.01.89.

Globin

Head of State Acceptance

Uralhimmash plant

Telegram No. 62-14- dated 11.01.89

Osokin

 

DEVELOPED BY:

Head of the standardization laboratory

special steels and alloys TsNIIChM

12 V.T. Ababkov

The validity period of the TU has been extended until 01.07.94.

   

The examination was conducted on 23.01.89

Head of the standardization laboratory special.

steels and alloys of the Central Research Institute of ChM

V. T. Ababkov

« 20 » 01 1989

Specifications (TU)

Our consultant will save your time

+49(1523) 72 15 100
E-mail:
Telegram:
WhatsApp:

Subscription

Special offers and discounts. :)