BARS AND STRIPS OF CORROSION RESISTANT AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS

TU 14−1-3564−83
(Instead of TU 14−1-1498−75)

Validity from 01.09.1983
before 09/01/1988

These specifications apply to hot-rolled and forged steel grades 12X13.20X13, 08X18H10T (EI914), 14X17H2, 12X18H10T, 12X18N9E, 09X16N4B (EP56), 10X17N13M2T (EI 448), 12X25N16G835 steel grades 12Х13, 20Х13, 14Х17Н2, 08Х18Н10Т (ЭИ914), 12Х18Н9Е, 12Х18Н10Т, 09Х16Н4Б (EP56). Steel is smelted in open electric furnaces.

1. VARIETY

1.1. In terms of shape, size and limit deviations, steel must meet the requirements of the following standards:

hot rolled round bars — GOST 2590−71

hot rolled square rods — GOST 2591−71

— GOST 4693−77

— OST 14−13−75

forged rods — GOST 1133−71

hot-rolled strips — GOST 4405−75

hot rolled hexagonal rods — GOST 2879−69

calibrated round bars — GOST 7417−75

calibrated hexagonal rods — GOST 8560−78

round bars with a special surface finish — GOST 14955−77

4 strength class

Notes:

1. Hot-rolled square rods with a size of 100 mm or less in accordance with GOST 2591−71 are supplied with blunt corners. Dullness should not exceed 0.15 of the side of the square.
2. Calibrated rods are supplied by the «Serp and Molot» plant.

1.2. Bars and strips are supplied according to the specialization of the supplying plant.

2. TECHNICAL REQUIREMENTS

2.1. The chemical composition of steel, maximum deviations from the norms of chemical composition, as well as the content of residual elements must comply with the requirements of GOST 5632−72 with the following changes:

2.1.1. In steel grades 12X13, 20X13, the sulfur content is not more than 0.020%;

2.1.2. The chemical composition of steel grades 09X16N4B (EP56) in accordance with the requirements of Table 1.

Table 1

Note:

1. In the finished product, the following chemical composition deviations are allowed:

• on chromium + 0.1%
• nickel ± 0.05%

2. The content of residual elements must comply with GOST 5632−72.

2.2. Bars and strips, depending on the order, must be delivered heat treated or not heat treated.

Steel grades 12Х13, 20Х13, 14Х17Н2 and 09Х16Н4Б (EP56) are supplied only in a heat-treated state (after annealing or high tempering).

2.3. The hardness of steel supplied in the annealed condition must comply with the standards of GOST 5949−75. The hardness of steel grade 14X17H2 should be no more than 302 HB (diameter of the indent according to Brinell is not less than 3.5 mm).

2.4. Mechanical properties of steel grades 12X13, 08X18H10T, 12X18H9T, 10X17H13M2T (EI448) must comply with the standards of GOST 5949−75; steel grades 20Х10, 14Х17Н2, 09Х16Н4Б (EP56), 12Х18Н10Т and 12Х25Н16Г7АР (ЭИ835) to the norms of Table 2.

table 2

Note:

• To determine the mechanical properties, the following are subjected to heat treatment: for steel grades 20X13, 14X17H2, 12X25N16G7AR (EI835) — workpieces with a diameter or thickness of 25 mm or finished rods, if their section is not more than 25 mm, for grade 12X18H10T — finished samples with an allowance for grinding.
• For steel grade 09Kh16N4b (EP56), quenching at a temperature of 1150 ± 10 ° C, holding for 5−5.5 hours, air cooling, tempering at a temperature of 600−620 ° C is carried out in blanks, square. 20−25 mm. Then, finished samples are made with an allowance for grinding, which are subjected to further heat treatment according to modes in accordance with the heat treatment option. It is allowed to carry out complete heat treatment in the workpieces of the cr., Sq. 20−25 mm.
• The option of heat treatment of 09Kh16N4B steel samples is specified in the order, and in the absence of instructions, at the discretion of the supplier.
• The KCV characteristic for the steel assortment supplied by the Serp and Molot plant is not determined.

2.5. The surface of the bars must comply with the requirements of GOST 5949−75.

Hot rolled and forged rods are supplied with an etched surface upon customer’s request.

2.6. Bars and strips cut on presses and under hammers may be handed over with crumpled ends; burrs at the ends of the rods should be cleaned.

2.7. The macrostructure of steel when checked on etched transverse templates should not have residues of a shrinkage cavity, bubbles, captivity, cracks, fistulas, foreign metal and slag inclusions visible without the use of magnifying devices.

Allowable defects of the macrostructure should not exceed:

central porosity — 2 points for steels 12Х13, 14Х17Н2, 12Х25Н16Г7АР;

-1 points — for other brands;

point heterogeneity — 3 points;

liquation square — - 2 points for steels of grades 12Х13, 14Х17Н2, 12Х25Н16Г7АР;

— 1 point — for other brands.

Note: Increased or decreased etching of the center zone is not a rejection sign.

2.8. Steel grades 08Х18Н10Т, 12Х18Н10Т, 12Х18Н9Т and 10Х17Н13М2Т should not have a tendency to intergranular corrosion.

2.9. At the request of the customer, specified in the order, in steels of grades 12X18H10T, 10X17H13M2T, 12X25N16G7AR (EI835), intended for operation at high temperatures, the austenitic grain size is determined. Control standards as agreed by the parties.

3. RULES OF ACCEPTANCE, TEST METHODS, LABELING, PACKAGING, DOCUMENTATION AND TRANSPORTATION

3.1. Acceptance rules, test methods, labeling, packaging and documentation must comply with the requirements of GOST 5949−75.

3.2. To check the quality of steel, the following is selected from the batch: for testing the hardness — 5% of rods, but not less: for sizes up to 40 mm — 10 bars, from 41 to 100 mm — 5 bars and more than 100 mm — 3 bars from the number presented in the batch.

3.3. Control of the mechanical properties of rods larger than 100 mm is carried out on samples cut from reforged samples with a size of square meters. 90−100 mm.

3.4. The mechanical properties of 09X16N4B steel on transverse samples are determined for square bars with a cross section of more than 80 mm, and for round bars — more than 100 mm.

3.5. Testing of metal for impact strength on specimens of type I (KCU) and type II (KCV) in accordance with GOST 9454−78 is carried out for a square and a strip with a size of 12 mm and more, a circle and a hexagon with a size of 16 mm and more.

3.6. When retesting the mechanical properties, all the strength and ductility characteristics provided for by this specification are determined, regardless of the results of the initial test.

In case of unsatisfactory results of retesting any of the samples, the batch is rejected.

3.7. The supplier plant is allowed not to check the macrostructure and the tendency to MCC, provided that its quality is guaranteed to the requirements of these technical specifications, indicating in the certificate «Conforms to TU».

3.8. Determination of the grain size of steel is carried out in accordance with GOST 5639−65 on longitudinal samples, heat-treated according to the mode for determining the mechanical properties, by any of the methods specified in the standard.

3.9. If a batch of metal is handed over according to the results of repeated tests, the results of the initial tests are also indicated in the certificate.

3.10. The indication of the bar size in the marking sign is optional.

3.11. Metal products are transported by all types of transport in accordance with the rules of transportation in force for this type of transport, and the conditions for loading and securing goods, approved by the USSR Ministry of Railways.

Note: Wholesale prices are shown in Appendix 2.

Registered at TsNIICHM
«16» .05. 1983 year

Head department of standardization
ferrous metallurgy V. T. Ababkov

LIST OF REFERENCE DOCUMENTS TO TU 14−1-3564−83

Appendix 2 to TU14−1-3564−83
In prices since 01.01.1982

Wholesale prices for bar steel and steel with special surface finish of the following brands:

1. Bar steel

1. Bar steel

1. Steel with special surface finish

Agreed: Head. cost department,
profitability and pricing IE TsNIICHM

L.N. Shevelev

Appendix No. 2 to TU 14−1-3564−82
(instead of TU 14−1-1498−75)
from 01.01.82

WHOLESALE PRICES

for calibrated steel grades 12X13, 20X13, 14X17H2
08Х18Н10Т (ЭИ914), 12Х18Н9Т, 12Х18Н10Т, 09Х16Н4Б (EP56)

Calibrated steel diameter in mm	Wholesale price of calibrated steel round in 1U
	12X13	20X13	14Х17Н2	108Х18Н10Т (ЭИ 914)	12Х18Н9Т	12X18H10T	09X16N4B (EP56)
3.0	1100	1030	1210	1740	1540	1650	1490
3.1−3.5	1060	981	1160	1690	1490	1600	1440
3.6−4.0	1020	941	1120	1650	1450	1560	1400
4.1−4.5	996	921	1100	1630	1430	1540	1380
4.6−5.0	986	881	1090	1620	1420	1530	1370
5.2−5.8	953	911	1060	1590	1390	1500	1340
6.0−6.3	916	849	1020	1550	1350	1460	1300
6.5−7.0	896	830	999	1530	1330	1440	1280
7.1−7.3	875	810	978	1510	1310	1420	1260
8.0−8.8	859	795	961	1500	1290	1410	1240
9.0−9.6	546	783	948	1480	1280	1390	1230
10.0−10.8	534	772	936	1470	1270	1360	1220
11.0−11.8	824	763	926	1460	1260	1370	1210
12.0−12.8	814	754	917	1450	1250	1360	1200
13.0−13.8	809	749	912	1440	1240	1350	1190
14.0−14.8	801	741	903	1440	1240	1350	1180
15.0−15.8	793	733	895	1420	1230	1330	1180
16.0−16.8	785	726	887	1420	1220	1330	1170
17.0−17.8	777	719	879	140	1210	1320	1160
18.0−19.5	770	712	872	1400	1200	1310	1150
20.0−21.5	761	703	862	1390	1190	1300	1140
22.0−24.0	748	691	849	1380	1180	1290	1130
25.0−30.0	732	676	832	1350	1160	1260	1110
31.0−40.0	717	663	817	1340	1140	1240	1090
41.0−50.0	702	649	801	1317	1120	1230	1070
52.0−70.0	694	641	792	1310	1110	1220	1070
71.0−100.0	690	637	788	1300	1110	1210	1060

Calibrated square steel costs 2% more. Calibrated hex steel, priced 5% more expensive. Price list 01−08, page 170. Calibrated steel with accuracy class and surface finish group WU is priced 3% cheaper. VSH ^and more expensive by 10%. Price list 01−08, p. 170.

AGREED:
Head laboratory of the current
IECHM pricing AI Ilyin.

FORM 31A

Appendix 3 to TU 14−1-3564−83

The calculation of the codes was checked:
Art. Ing. department of standardization
TsNIICHM E.P. Rakhmanova

FORM 31A

Appendix 3 to TU 14−1-3564−83

The calculation of the codes was checked:
Art. Ing. department of standardization
TsNIICHM E.P. Rakhmanova

FORM 31A

Appendix 3 to TU 14−1-3564−83

The calculation of the codes was checked:
Art. Ing. department of standardization
TsNIICHM E.P. Rakhmanova

FORM 31A

Appendix 3 to TU 14−1-3564−83

The calculation of the codes was checked:
Art. Ing. department of standardization
TsNIICHM E.P. Rakhmanova

CHANGE REGISTRATION SHEET

VIFS No. TU 14−1-3564−83

Title of the document	No. and date of issue of the document	What points of the TU have been changed	Registration number of the VIFS document Date / Number

Ministry of ferrous metallurgy of the USSR

UDC
Group

AGREED BY: Chief engineer of the organization PO Box R-6761 _________ Yu.N. Redkin «___" ______ 1984

APPROVED: Deputy Head of the Technical Department of the MFM SSR __________ Yu.N. Kuznetsov «___" ______ 1984

BARS AND STRIPS OF CORROSION RESISTANT AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS

TU 14−1-3564−83

Change No. 1

Introduction date: 07.19.84.

Add the introductory part with the words:

• «The technical level indicators established by these technical specifications are provided for the highest quality category.»
• P. p. 1.1. Note: Clause 2 shall be deleted.

Agreed: Deputy director of the enterprise PO Box A-1147 No. 7111−1498 Yu.G. BUSHUEV from 03.11.83.

Designed by: Head of the technical department of VPO «Soyuzspetsstal" _______ M.P. Kolyasnikov Head laboratory of standardization special. steels and alloys TSNIICHM _______ V.T. Ababkov from 09.11.83

Registered at TsNIICHM: 03/19/84
Head department of standardization of ferrous metallurgy

V.T. Ababkov

Gold metal plant
Rotaprint CLAP
Order No. 439
Circulation 80 copies.
04.24.84

Ministry of ferrous metallurgy of the USSR

UDC
Group B32

AGREED BY: Chief engineer of the organization PO Box R-6761 _________ Yu.N. Redkin «___" ______ 1986

APPROVED: Chief Engineer of VPO Soyuzspetsstal __________ A.G. Korobov «___" ______ 1986

BARS AND STRIPS OF CORROSION RESISTANT AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS

TU 14−1-3564−83

Change No. 2

Introduction date: 21.10.86.

Section 1 «Range» clause 1.1. add note 2 as amended:

• «Note: 2. Calibrated steel of a hexagonal section with an inscribed circle diameter from 5 to 8 mm inclusive, manufactured by the Hammer and Sickle plant, is supplied in a roll.»

Clause 1.1. supplement with sub-clause 1.1.1 as follows:

• «1.1.1. For calibrated hexagonal rods according to the dimensions supplied:
• a) in cold-worked condition — in accordance with GOST 8560−78, quality h11;
• b) in a thermally treated state — in accordance with table.

Table

In section 3, paragraph 3.8, the reference to GOST 5639−65 shall be replaced by GOST 5639−82.

Section 3 shall be supplemented with clause 3.12 as amended:

• «3.12. The dimensions of the finished product are checked with a GOST 6507−79 micrometer, a GOST 2216−84 bracket, and a GOST 166−80 caliper; curvature — with a GOST 882−75 probe; length — with tape measure GOST 7502−80 «.

AGREED: Deputy director enterprises PO Box A-1147 ____________ Yu.G. Bushuev «7» 04 1986	DEVELOPED: /Chief Engineer plant «Hammer and Sickle" _______ V.A. Pogonchenkov «13» 03 1986
Chief of BOS-8 ____________ Yu.N. Skachkov «2» 04 1986
Head laboratory standardization of special steels and alloys TsNIIchermet _________ V.T. Ababkov «___" _____ 1986

Registered in TsNIICHM: 07.21.86
Head department of standardization of ferrous metallurgy

V.T. Ababkov

Gold metal plant
Rotaprint CLAP
Order No. 439
Circulation 80 copies.
04.24.84

OKP 096300 V32
096400
OKK 114100
115200

MINISTRY OF FERROUS METALLURGY OF THE USSR Moscow administration Central Research Institute ferrous metallurgy named after I.P. Bardeen TsNIIchermet _______________________________________ 107843, Moscow, 2nd Baumanskaya, 9/23 Tel. 267−01−02, ref. 100 for telegrams: Moscow, TsNIIchermet Telstape: Niobium 133305 Calc. Account 240802 in the Bauman branch of the State Bank 08/28/88 No. T4-T-3564 No. __________ dated ___________ Ch. Ing. Votkinskiy machine building. H-yes 23410 Votkinsk, Udm. ASSR Ch. engineer of the plant «Sibelektrostal" 60050 Krasnoyarsk Ch. to the engineer of the production of PO box A-1950 26000 Ustinov Ch. to the engineer of the production p / I A-1298 96066 Leningrad Ch. to the engineer of the production p / I B-8171 10033 Saratov Ch. engineer of Dneprovsky «Giprommashobogaschenie» — 320095 Dnepropetrovsk. «Soyuzglavmetizsnabsbyt" 103062 Moscow

Deputy early Chief Scientific, Technical and Technological Directorate of the MCHM USSR Beginning department of balances and wholesale metal rolling of the USSR Gossnab Member of the USSR State Committee for prices Beginning production-tech. Dept. Ukrglavmetalla MCSM NIIEChM Ch. engineer of the Zlatoust Metallurgical Plant 456203 Zlatoust, Chelyab. region Ch. engineer of the plant «Hammer and Sickle" 111024 Moscow Deputy director of the company PO Box A-1147 141070 Kaliningrad, M.O. Ch. to the engineer of the production p / I R-6761 125833 Moscow Ch. engineer of the plant «Dneprospetsstal" 330062 Zaporozhye Ch. to the engineer of the production p / I M-5246 123231 Moscow Ch. engineer of the plant «Elektrostal" 144002 Electrostal, M.O. Ch. management of special steel and alloys of the USSR MCHM Ch. engineer of the Kulebakinsky Metallurgical Plant 607010 Kulebaki, Gorkov. Region Ch. Ing. p / i M-5740 -310068 Kharkiv

I C E N I E No. 3

On the extension of the validity period of Technical conditions 14−1-3564−83

«Bars and strips of corrosion-resistant and heat-resistant steel.»

Specifications 14−1-356481 extended until 09/01/93

Basis: Letters: «Hammer and Sickle» No. 7/402 dated 05/11/88, PO Box A-1147 No. 011−368 dated 05/19/88, Sumy machine building. MPO No. 58−285 of 04.04.88, p / y box G-4725 No. 11/491 of 15.04.88, Zlatoust. Metkomb-t No. 03 / TU-1−3564 dated 04/07/88, Moscow. Mechanical engineering. According to No. 04/308 of 06.06.88.

Head department of standardization
ferrous metallurgy V.T. Ababkov

Registered by TsNIMCHM: 07/15/88

238974/03 08/23/1988
Use N.V. Nadrova
265−72−45

Ministry of ferrous metallurgy of the USSR

OKP 096300 Group B32
096400
OKK 114100
115200

BARS AND STRIPS FROM CORROSION RESISTANT
AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS
TU 14−1-3564−83

Change No. 4

Introduction period from: 08.04.89

Agreed: And about. director of the enterprise PO Box A-1147 of the organization PO Box VPO 731 __________ Yu.G. Bushchuev «21» 07 198 _ Chief engineer of the plant «Hammer and sickle" __________ V.A. Pogonchenkov «04» 11 1988

Designed by: Chief Engineer Zlatoust Metallurgical Plant _________ Yu.I. Pyatinin «17» 11 1987 Head of Gospriyemka Zlatoust Metallurgical Plant _________ IN AND. Ivanov November 16, 1987

To remove the limitation on the validity of the technical conditions.

Supplement the introductory part with examples of symbols.

Examples of symbols:

Hot-rolled steel, round, 50 mm in diameter, normal rolling accuracy (B) in accordance with GOST 2590−71, grade 12X13, for hot working by pressure (loading a.), Heat-treated

circle

Hot-rolled steel, square, with a square side of 50 mm, normal rolling accuracy (B) in accordance with GOST 2591−71, grade 12X18H10T, for cold machining (subdivision b)

square

Calibrated steel, hexagonal, with an inscribed circle diameter of 20 mm, with a maximum deviation of h11 in accordance with GOST 8560−78, in a cold-worked state, grade 12X18H9T

hexagon

1. In paragraph 1.1, the reference to GOST 4693−77 shall be replaced with a reference to OST 14−2-205−87.
2. Clause 2.2. State the second paragraph in the wording:

«Steel grades 12X13 and 20X13 are supplied only in a heat-treated state (after annealing or high tempering). Steel grades 14Х17Н2 and 09Х16Н4Б (EP56) are supplied after double heat treatment (annealing followed by high tempering.

Note: For calibrated rods of steel grade 14X17H2, double heat treatment (annealing + high tempering) in a rolling stock is allowed.

In table 2, the designation of the unit of measurement of ultimate tensile strength and yield strength MPa (kgf / mm ²) is replaced by N / mm ² (kgf / mm ²).

Section 2 shall be supplemented with clause 2.10 in the wording: «2.10. The contamination of the steel with hair strands identified on ready-made children by the consumer must comply with the norms of TU 14−1-336−72. «

Section 3. The name of the section shall be supplemented with the word «storage».

Section to supplement paragraphs 3.13. as amended: «3.13. Storage of products in accordance with the requirements of GOST 7566−81 «.

Note: Appendix No. 2 «Wholesale prices for high-grade steel and steel with special surface finish» add: All rationing of hair lines on finished parts at the consumer’s place and for the supply of steel with double heat treatment, surcharges are charged in accordance with the price list No. 01−08−1980.

The examination was carried out: 02/09/89
Head laboratory of standardization
special steels and alloys
V.T. Ababkov

Ministry of ferrous metallurgy of the USSR

OKP 096300 Group B32
096400
OKK 114100
115200

BARS AND STRIPS FROM CORROSION RESISTANT
AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS
TU 14−1-3564−83

Change No. 5

Introduction period from: 06.02.90

Agreed: Deputy director TSNIIMVMOM __________ Yu.G. Bushchuev «__" _____ 1989

Designed by: Chief Engineer Zlatoust Metallurgical Plant _________ Yu.I. Pyatinin «18» .07.1989 Head of State Reception at ZMZ _________ IN AND. Ivanov «19» .07.1989

Exclude the requirement for quality category from the introduction.
In paragraph 1.1 and Appendix 1, references to OST 14−13−75 and OST 14−2-205−87 should be replaced with a reference to TU 14−14492−88, from 01.01.90, references to GOST 2590−71 and GOST 2591−71 replace, respectively, with references to GOST 2590−88 and GOST 2591−88.
In paragraph 1.1 after GOST 14955−77, instead of «4 classes of accuracy», write «quality h11».
Note 1 to clause 1.1. exclude.
Clause 2.5 shall be supplemented with a paragraph: «by agreement of the parties, hot-rolled and forged rods are supplied in a turned or stripped condition."
Appendix 2 on wholesale prices for bar steel shall be supplemented with «for the supply of hot-rolled and forged rods in a turned or stripped condition, a surcharge is made in accordance with the price list No. 01−08 p.184».

The examination was carried out: 06.12.89
Head laboratory of standardization
special steels and alloys
V.T. Ababkov

OKP 096300 096400 OKK 114100 115200

Group B32 APPROVED: Director of the Center for Standardization and certification of metal products FSUE TsNIIChermet them. I.P. Bardeen Chairman of TC 375 __________ V.T. Ababkov August 03, 2004

BARS AND STRIPS FROM CORROSION RESISTANT
AND HEAT RESISTANT STEEL

TECHNICAL CONDITIONS
TU 14−1-3564−83

Change No. 7

The holder of the original — TsSSM FSUE TsNIIChermet im. I.P. Bardeen

The term of introduction is from: 01.11.2004.

AGREED: Institute Director metal materials OJSC «Composite" _________ A.V. Logunov

DEVELOPED: Chief Engineer JSC «Metallurgical plant «Electrostal" ________ V.N. Popov

1. Clause 1.1 Note 2 shall be deleted. Replace «GOST 4693−77» with TU 14−1-4492−88 «.

2. Clause 2.1 Replace the words «maximum deviations» with «permissible deviations».

3. Clauses 2.1, 2.1.1 Replace the word «content» with «mass fraction».

4. Clause 2.3 Replace the words «Hardness of steel, …» with «Hardness of bars …».

5. Clause 2.4 Replace the words «Mechanical properties of steel …» with «Mechanical properties of bars made of steel grades …», hereinafter in the text.

Table 2. Replace the dimension of ultimate strength and yield strength «MPa (kgf / mm ²)» by «N / mm ² (kgf / mm ²)».

6. Clause 2.8 Replace the words «…must not have a tendency to intergranular corrosion …» by «…must be resistant to intergranular corrosion …».

7. Clause 3.6 The second paragraph shall be stated in the wording:

«It is allowed to carry out tests (no more than once) of mechanical properties according to the modified mode of heat treatment of samples (within the table).

In this case, the test is considered primary with the determination of all characteristics.

In case of receiving unsatisfactory test results on at least one sample, the batch is rejected. «

8. Clause 3.7, 3.9. Replace the words «certificate» with «quality document».

9. To exclude the note to technical conditions for prices.

10. Appendix 1 «liver ND, which are referenced in the text of the technical specifications» to replace the attached.

11. Appendix 2 «Form 3.1A» shall be replaced with the attached one.

12. Change No. 1 and notification No. 3 to cancel.

Expertise carried out by the Center
FSUE TsNIIChermet named after I.P. Bardeen

August 02, 2004

/ Deputy Director of the Center for Standardization and
certification of metal products

V.D. Khromov.

Appendix 1
(reference)

List of referenced documents to which there are links
in the text of technical specifications

Appendix 2
(required)

Form 3.1A

Appendix 2
(required)

Form 3.1A

Appendix 2
(required)

Form 3.1A

Appendix 2
(required)

Form 3.1A