Brass LS59-1V
Brass LO70-1
Brass LMZA57-3-1
Brass LMzAJKS70-7-5-2-2-1
Brass LMZh57-1,5-0,75
Brass LMtsKA58-2-1-1
Brass LMtsKNS58-3-1,5-1,5-1
Brass LMtsKNSA58-3-1,5-1,5-1
Brass LMtsSKa58-2-2-1-1
Brass LMsh68-0,05
Brass LN65-5
Brass LNKMts49-10-0,3-0,2
Brass LNKoMts49-9-0,2-0,2
Brass ЛНМц60-9-5
Brass LO60-1
Brass LO62-1
Brass LKS65-1,5-3
Brass LO90-1
Brass LOK59-1-0.3
Brass LOMNA49-0,5-10-0,4-0,4
Brass Lomsh70-1-0.04
Brass Lomsh70-1-0.05
Brass LS58-2
Brass LS58-3
Brass LS59-1
Brass LS59-1B
Brass LS59-2
Brass LS60-1
Brass LS63-3
Brass LS64-2
Brass LS74-3
Brass LA85-0.5
Brass L59
Brass L60
Brass L63
Brass L66
Brass L68
Brass L70
Brass L72
Brass L75mk
Brass L80
Brass L85
Brass L90
Brass L96
Brass LA77-2
Brass LA77-2u
Brass LMZ58-2
Brass LAJ60-1-1 (LAJ60-1-1L)
Brass LAZHMTS52-2-1-1,5-1
Brass LAMsh77-2-0,04
Brass LAMSh77-2-0,05
Brass LAN59-3-2
Brass LANKMZ 75-2-2,5-0,5-0,5 (alloy 156)
Brass LAF94-0,5-0,15
Brass LZMc59-1-1
Brass LZhS58-1-1
Brass LC62-0.5
Brass LK75B
Brass LCAN80-1-1,9-5,8
Brass ЛКАНМЦ75-2-2,5-0,5-0,5
Brass LCBO62-0,2-0,04-0,5
Designation
| Name |
The value |
| Designation GOST Cyrillic |
ЛС59-1В |
| Designation GOST Latin |
LC59-1B |
| Transliteration |
LS59-1V |
| The chemical elements |
ЛPb59-1В |
Description
Brass LS59−1V is used: for the manufacture of long products (bars), intended for the production of nuts, bolts, gears, gear wheels, bushings by machining.
Note
Lead brass.
Standards
| Name |
Code |
Standards |
| Tapes |
В54 |
GOST 15527-2004 |
| Bars |
В55 |
GOST 2060-2006, GOST Р 52597-2006, GOST 31366-2008 |
| Non-ferrous metals, including rare metals, and their alloys |
В51 |
GOST 28873-90 |
Chemical composition
| Standard |
P |
Fe |
Cu |
Zn |
Sb |
Pb |
Bi |
| GOST 2060-2006 |
≤0.02 |
≤0.5 |
57-61 |
The rest |
≤0.01 |
0.8-1.9 |
≤0.003 |
Cu is the basis.
According to GOST 15527-2004, GOST 2060-2006, the sum of other elements should be ≤ 1.50%. In brass, the mass fraction of nickel is allowed up to 1.0% due to the mass fraction of copper, which is not taken into account in the sum of other impurities.
Mechanical characteristics
| Section, mm |
σB, MPa |
d5, % |
d10 |
Brinell hardness number, MPa |
HV, MPa |
| Rods are supplied according to GOST 2060-2006 (longitudinal samples) |
| 10-50 |
≥360 |
≥22 |
≥18 |
- |
80-140 |
| 55-180 |
≥360 |
≥22 |
≥18 |
- |
70-140 |
| 3-50 |
≥330 |
≥25 |
≥22 |
≥80 |
80-140 |
| 13-20 |
≥390 |
≥15 |
≥12 |
≥100 |
121-170 |
| 21-40 |
≥390 |
≥18 |
≥15 |
≥100 |
121-170 |
| 3-12 |
≥410 |
≥10 |
≥8 |
≥100 |
121-170 |
| 3-12 |
≥490 |
≥7 |
≥5 |
≥130 |
≥171 |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
| d10 |
Elongation after rupture |
| HV |
The Vickers hardness |
Physical characteristics
| Temperature |
Е, ГПа |
r, кг/м3 |
l, Вт/(м · °С) |
R, НОм · м |
| 20 |
105 |
8500 |
1047 |
66 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
| l |
Coefficient of thermal conductivity |
| R |
UD. the resistivity |