Brass L85
Brass LO70-1
Brass LMZA57-3-1
Brass LMzAJKS70-7-5-2-2-1
Brass LMZh57-1,5-0,75
Brass LMtsKA58-2-1-1
Brass LMtsKNS58-3-1,5-1,5-1
Brass LMtsKNSA58-3-1,5-1,5-1
Brass LMtsSKa58-2-2-1-1
Brass LMsh68-0,05
Brass LN65-5
Brass LNKMts49-10-0,3-0,2
Brass LNKoMts49-9-0,2-0,2
Brass ЛНМц60-9-5
Brass LO60-1
Brass LO62-1
Brass LKS65-1,5-3
Brass LO90-1
Brass LOK59-1-0.3
Brass LOMNA49-0,5-10-0,4-0,4
Brass Lomsh70-1-0.04
Brass Lomsh70-1-0.05
Brass LS58-2
Brass LS58-3
Brass LS59-1
Brass LS59-1B
Brass LS59-2
Brass LS60-1
Brass LS63-3
Brass LS64-2
Brass LS74-3
Brass LA85-0.5
Brass L59
Brass L60
Brass L63
Brass L66
Brass L68
Brass L70
Brass L72
Brass L75mk
Brass L80
Brass L85
Brass L90
Brass L96
Brass LA77-2
Brass LA77-2u
Brass LMZ58-2
Brass LAJ60-1-1 (LAJ60-1-1L)
Brass LAZHMTS52-2-1-1,5-1
Brass LAMsh77-2-0,04
Brass LAMSh77-2-0,05
Brass LAN59-3-2
Brass LANKMZ 75-2-2,5-0,5-0,5 (alloy 156)
Brass LAF94-0,5-0,15
Brass LZMc59-1-1
Brass LZhS58-1-1
Brass LC62-0.5
Brass LK75B
Brass LCAN80-1-1,9-5,8
Brass ЛКАНМЦ75-2-2,5-0,5-0,5
Brass LCBO62-0,2-0,04-0,5
Designation
| Name |
The value |
| Designation GOST Cyrillic |
Л85 |
| Designation GOST Latin |
L85 |
| Transliteration |
L85 |
| The chemical elements |
Л85 |
Description
Brass L85 is used: for the manufacture of semi-finished products (strips, sheets, strips, tubes, profiles); products for various industrial purposes; wire for parts for electrical engineering; medals and badges.
Note
Simple (double) brass.
Brass L85 is very well deformed in a cold state, especially by drawing; not prone to stress corrosion cracking; suitable for forging, stamping, and enameling.
Standards
| Name |
Code |
Standards |
| Tapes |
В54 |
GOST 15527-2004, GOST 2208-2007 |
| Non-ferrous metals, including rare metals, and their alloys |
В51 |
GOST 28873-90 |
| Sheets and stripes |
В53 |
GOST 931-90 |
Chemical composition
| Standard |
P |
Fe |
Cu |
Zn |
Sb |
Pb |
Bi |
| GOST 2208-2007 |
≤0.01 |
≤0.1 |
84-86 |
The rest |
≤0.005 |
≤0.03 |
≤0.002 |
Cu is the basis.
According to GOST 15527-2004, GOST 2208-2007 the amount of other elements should be ≤ 0.30%. For antimagnetic brass, the mass fraction of iron should not exceed 0.030%.
Mechanical characteristics
| σB, MPa |
d10 |
Brinell hardness number, MPa |
HV, MPa |
| Sheets and strip, cold-rolled in the state of delivery according to GOST 931-90, strips and sheets according to GOST 2208-2007 (samples) |
| 250-360 |
≥38 |
≥65 |
≥70 |
| 320-430 |
≥12 |
≥95 |
≥105 |
| ≥390 |
≥3 |
≥110 |
≥125 |
Description mechanical marks
| Name |
Description |
| σB |
Limit short-term strength |
| d10 |
Elongation after rupture |
| HV |
The Vickers hardness |
Physical characteristics
| Temperature |
Е, ГПа |
r, кг/м3 |
l, Вт/(м · °С) |
R, НОм · м |
| 20 |
105 |
8750 |
1524 |
47 |
A description of the physical symbols
| Name |
Description |
| l |
Coefficient of thermal conductivity |