Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ЛР1 |
| Designation GOST Latin | LP1 |
| Transliteration | LR1 |
| The chemical elements | BeB1 |
Description
Cast iron LR1 applies: for further melting in iron shops in the production of iron castings.
Note
Foundry pig iron, refined magnesium.
Standards
| Name | Code | Standards |
|---|---|---|
| Cast iron | В11 | GOST 4832-95 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Fe | Al | V | Ti | Pb | Mg |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| GOST 4832-95 | 3.4-4.5 | ≤0.01 | ≤0.12 | ≤1 | ≤0.04 | 3.2-3.6 | The rest | ≤0.005 | ≤0.05 | ≤0.06 | ≤0.005 | ≤0.019 |
Fe is the basis.
According to GOST 4832-95, cast iron is divided into 3 groups according to the manganese content: I group ≤0.30%, II group 0.30-0.50%, III group 0.50-1.00%; by the content of phosphorus is divided into 2 classes: class A ≤0,080%, class B ≤0,12%; on the content of sulfur is divided into 2 categories: 1 category ≤0.0050%, 2 category ≤0.010%. Cast iron may be produced with a mass fraction of silicon of more than 3.60%.
According to GOST 4832-95, cast iron is divided into 3 groups according to the manganese content: I group ≤0.30%, II group 0.30-0.50%, III group 0.50-1.00%; by the content of phosphorus is divided into 2 classes: class A ≤0,080%, class B ≤0,12%; on the content of sulfur is divided into 2 categories: 1 category ≤0.0050%, 2 category ≤0.010%. Cast iron may be produced with a mass fraction of silicon of more than 3.60%.