Cast iron Achs-6
Cast iron AChV-1
Cast iron AChV-2
Cast iron AChK-1
Cast iron AChK-2
Cast iron AChS-1
Cast iron AChS-2
Cast iron ASF-3
Cast iron AChS-4
Cast iron AChS-5
Cast iron AChS-6
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | АЧС-6 |
| Designation GOST Latin | AChC-6 |
| Transliteration | AChS-6 |
| The chemical elements | - |
Description
Cast iron Achs-6 applies: for the production of castings, working in friction at temperatures up to 300 °C in pair with the shaft, not subjected to heat treatment.
Note
Grey antifriction cast iron with lamellar graphite.
Standards
| Name | Code | Standards |
|---|---|---|
| Cast iron | В11 | GOST 1585-85 |
Chemical composition
| Standard | C | S | P | Mn | Si | Fe | Pb |
|---|---|---|---|---|---|---|---|
| GOST 1585-85 | 2.2-2.8 | ≤0.12 | 0.5-1 | 0.2-0.6 | 3-4 | The rest | 0.5-1 |
Fe is the basis.
Technological properties
| Name | The value |
|---|---|
| Microstructure | Perlite or pearlitic-ferritic. Graphite: a form - ПГф1, ПГф2, ПГф4, ВГф5; size - ПГД15 - ПГД180; distribution - ПГр1 - ПГр3. Perlite: footprint - P-П85; dispersion - ПД0,3 - ПД1,6. Fosfina the eutectic (nature of distribution) - ФЭр2, ФЭр3. Cementite is not allowed. |
| terms of Use | The use of castings made of cast iron notificationname in friction requires careful installation, providing the pair of the friction surfaces and the absence of bias; continuous lubrication, permitting true and significant heating of the friction units; increase of the gap compared to the established bronze 15-30%, in the presence of significant heating osetreni in the work - up to 50%; running at idle and progressively higher loads. At a pressure of P≤9,0 MPa sliding speed V must be ≤4.0 m/s and the product P·V ≤ 9,0 MPa·m/s. |