Steel SV-10НЮ
Steel Sv-10GN3SMD
Sv-08GSMT steel
Steel Sv-08H15N23V7G7M2 (EP88)
Steel Св-08Х19Н10Г2Б (ЭИ898; Н-89)
Steel Sv-08X1Du
Steel Св-08Х20Н9С2БТЮ (EP156)
Steel Св-08Х25Н20С3Р1 (EP532)
Steel Sv-08HG2SDU
Sv-08HN2GMTA steel
Sv-09HNMTA steel
Sv-09HNMTAA steel
Sv-09HN4MDTA steel
Sv-10HN1MA steel
Sv-10HN2SMD steel
Sv-08GM steel
Sv-10GSM steel
Sv-10Nu steel
Steel Sv-10Kh16N25AM6 (EI395; H-66)
Steel Св-10Х16Н25М6АФ (ЗИ112)
Steel Sv-10H19N11M4F (EP647)
Sv-10H19H23G2M5FAT (EP868)
Steel Sv-10Х21Н11ФТ (EP854)
Sv-10X2M steel
Sv-10HGSN2MT steel
Sv-10KhMFTU steel
Sv-10KhMFTU-A steel
Sv-12M steel
Sv-12Kh2NMA steel
Steel Sv-06H15N35G7M6B (EP582)
Steel Sv-01Kh12N6M (ChS48)
Steel Св-01Х19Н18Г10АМ4 (EP690)
Steel Sv-03GKhN2MD
Steel Sv-03GKhN3MD
Steel Sv-03HN3MD
Sv-04N2GSTA steel
Sv-04N2GTA steel
Sv-04N3GMTA steel
Sv-04N3GSMTA steel
Steel Sv-04H19H11M3 (H-65)
Sv-04Cr19Ni (04Cr19N9) steel
Sv-04H20N10G2B (EP762)
Sv-06H14GMFBA steel
Steel Sv-08GN2SMD
Steel Sv-06Х21Н7БТ (EP500)
Sv-06Cr3G2SmFtu4 steel
Sv-06Kh8G2SMFtu4 steel
Steel Sv-07H22H13G5ST (ChS49)
Steel Sv-07Cr25H13 (H-71)
Steel Sv-07CGSN3MD
Steel Sv-07HN3MD
Sv-08 steel
Sv-08G1NMT steel
Sv-08G1S steel
Sv-08G2SM steel
Sv-08G2SNMT steel
Sv-08G2SNTYR steel
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | Св-10НЮ |
| Designation GOST Latin | Cb-10HJu |
| Transliteration | Sv-10NYu |
| The chemical elements | 10НAl |
Description
Steel SV-10НЮ used: for the production of welding wires for electroslag and automatic submerged arc welding steel of the type 12KHM.
Note
A steel alloy.
Standards
| Name | Code | Standards |
|---|---|---|
| Sectional and shaped rolling | В32 | TU 14-1-2203-77 |
| Welding and cutting of metals. Soldering, riveting | В05 | TU 14-1-2219-77 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | Al | Ti | Ce |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-2219-77 | ≤0.1 | ≤0.03 | ≤0.03 | 0.4-0.7 | ≤0.25 | ≤0.03 | 1.5-1.9 | The rest | ≤0.25 | 0.1-0.25 | ≤0.1 | - |
| TU 14-1-2203-77 | ≤0.1 | ≤0.03 | ≤0.03 | 0.4-0.7 | ≤0.25 | ≤0.03 | 1.5-1.9 | The rest | ≤0.25 | 0.1-0.25 | ≤0.1 | 0.1 |
Fe is the basis.
According to TU 14-1-2219-77 the chemical composition is given for steel grade Sv-10NYu. Permissible deviations from the chemical composition: carbon ± 0.010%, manganese ± 0.040%, silicon ± 0.070%, nickel ± 0.050%, aluminum ± 0.020%. Cerium is introduced in the form of ferrocerium at a rate of 1 kg per 1 ton of liquid metal and its residual content is not determined.
According to TU 14-1-2203-77, the chemical composition is given for the S-10NYu welding wire. In rod, not intended for copper-clad wire, the copper content should not exceed 0.25%, and at the request of the consumer - not more than 0.20%. Cerium is introduced by calculation at 0.10%.
According to TU 14-1-2219-77 the chemical composition is given for steel grade Sv-10NYu. Permissible deviations from the chemical composition: carbon ± 0.010%, manganese ± 0.040%, silicon ± 0.070%, nickel ± 0.050%, aluminum ± 0.020%. Cerium is introduced in the form of ferrocerium at a rate of 1 kg per 1 ton of liquid metal and its residual content is not determined.
According to TU 14-1-2203-77, the chemical composition is given for the S-10NYu welding wire. In rod, not intended for copper-clad wire, the copper content should not exceed 0.25%, and at the request of the consumer - not more than 0.20%. Cerium is introduced by calculation at 0.10%.
Mechanical characteristics
| Section, mm | σB, MPa |
|---|---|
| The welding wire of the highest quality cold-worked state beyond 14-1-2219-77 | |
| 3 | 736-981 |
| 4 | 589-834 |
| 5 | 539-785 |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| σB | Limit short-term strength |
Technological properties
| Name | The value |
|---|---|
| Macrostructure and contamination | In the macrostructure of wire rod, are not allowed discontinuity of the metal caused by the presence of shrinkage, axial looseness, bubbles, cracks, delamination and inclusions. |
| Microstructure | Wire rod microstructure should be uniform. Padalka (martensitic and toostonedtocare areas) is not allowed. |
| Features of production | The welding wire first quality class on the other 14-1-2219-77 supplied in cold-worked condition, without determining the mechanical properties. |