Steel SV-07ХН3МД
Steel Sv-10GN3SMD
Sv-08GSMT steel
Steel Sv-08H15N23V7G7M2 (EP88)
Steel Св-08Х19Н10Г2Б (ЭИ898; Н-89)
Steel Sv-08X1Du
Steel Св-08Х20Н9С2БТЮ (EP156)
Steel Св-08Х25Н20С3Р1 (EP532)
Steel Sv-08HG2SDU
Sv-08HN2GMTA steel
Sv-09HNMTA steel
Sv-09HNMTAA steel
Sv-09HN4MDTA steel
Sv-10HN1MA steel
Sv-10HN2SMD steel
Sv-08GM steel
Sv-10GSM steel
Sv-10Nu steel
Steel Sv-10Kh16N25AM6 (EI395; H-66)
Steel Св-10Х16Н25М6АФ (ЗИ112)
Steel Sv-10H19N11M4F (EP647)
Sv-10H19H23G2M5FAT (EP868)
Steel Sv-10Х21Н11ФТ (EP854)
Sv-10X2M steel
Sv-10HGSN2MT steel
Sv-10KhMFTU steel
Sv-10KhMFTU-A steel
Sv-12M steel
Sv-12Kh2NMA steel
Steel Sv-06H15N35G7M6B (EP582)
Steel Sv-01Kh12N6M (ChS48)
Steel Св-01Х19Н18Г10АМ4 (EP690)
Steel Sv-03GKhN2MD
Steel Sv-03GKhN3MD
Steel Sv-03HN3MD
Sv-04N2GSTA steel
Sv-04N2GTA steel
Sv-04N3GMTA steel
Sv-04N3GSMTA steel
Steel Sv-04H19H11M3 (H-65)
Sv-04Cr19Ni (04Cr19N9) steel
Sv-04H20N10G2B (EP762)
Sv-06H14GMFBA steel
Steel Sv-08GN2SMD
Steel Sv-06Х21Н7БТ (EP500)
Sv-06Cr3G2SmFtu4 steel
Sv-06Kh8G2SMFtu4 steel
Steel Sv-07H22H13G5ST (ChS49)
Steel Sv-07Cr25H13 (H-71)
Steel Sv-07CGSN3MD
Steel Sv-07HN3MD
Sv-08 steel
Sv-08G1NMT steel
Sv-08G1S steel
Sv-08G2SM steel
Sv-08G2SNMT steel
Sv-08G2SNTYR steel
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | Св-07ХН3МД |
| Designation GOST Latin | Cb-07XH3MD |
| Transliteration | Sv-07HN3MD |
| The chemical elements | 07CrН3MoCu |
Description
Steel SV-07ХН3МД usedfor producing welding rod, welding, surfacing and production of electrodes.
Note
A steel alloy.
Standards
| Name | Code | Standards |
|---|---|---|
| Sectional and shaped rolling | В32 | TU 14-1-2203-77, TU 14-1-4054-85 |
| Welding and cutting of metals. Soldering, riveting | В05 | TU 14-1-4345-87 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | Al | Ti | Mo |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-4054-85 | 0.04-0.09 | ≤0.012 | ≤0.015 | 0.3-0.6 | 0.85-1.1 | ≤0.7 | 2.8-3.2 | The rest | 0.85-1.15 | ≤0.05 | 0.12 | 0.5-0.65 |
| TU 14-1-2203-77 | 0.04-0.09 | ≤0.012 | ≤0.015 | 0.3-0.6 | 0.85-1.1 | 0.15-0.35 | 2.8-3.2 | The rest | 0.85-1.15 | - | - | 0.5-0.65 |
Fe is the basis.
According to TU 14-1-4054-85 the chemical composition is given for steel grade Sv-07HN3MD-Sh. The titanium content is calculated. The nitrogen content in the rod must not be more than 0.015%. It is allowed to supply wire with a deviation from the norms of chemical composition in accordance with paragraph 3.5. GOST 2246, subject to other requirements of the Specification.
According to TU 14-1-2203-77 the chemical composition is given for the welding wire of the brand Sv-07HN3MD. In the steel, an increased content of phosphorus is allowed to be 0.0050%. In the steel, the determination of nitrogen and colored impurities - arsenic, lead, antimony and tin - is performed. The results of the control are optional.
According to TU 14-1-4054-85 the chemical composition is given for steel grade Sv-07HN3MD-Sh. The titanium content is calculated. The nitrogen content in the rod must not be more than 0.015%. It is allowed to supply wire with a deviation from the norms of chemical composition in accordance with paragraph 3.5. GOST 2246, subject to other requirements of the Specification.
According to TU 14-1-2203-77 the chemical composition is given for the welding wire of the brand Sv-07HN3MD. In the steel, an increased content of phosphorus is allowed to be 0.0050%. In the steel, the determination of nitrogen and colored impurities - arsenic, lead, antimony and tin - is performed. The results of the control are optional.
Technological properties
| Name | The value |
|---|---|
| Macrostructure and contamination | In the macrostructure of wire rod, are not allowed discontinuity of the metal caused by the presence of shrinkage, axial looseness, bubbles, cracks, delamination and inclusions. |
| Microstructure | Wire rod microstructure should be uniform. Padalka (martensitic and rotomachinery areas) is not allowed. |