Steel 4Х13Н6ЛВФ (ЭП354)
Steel 16Х12В2ФТаР (EC181)
Steel 17Х18Н9 (2Х18Н9)
Steel 15Х16Н2АМ (EP479)
Steel 14Х20Н25В5МБ (LZhT)
Steel 14Х17Н2 (ЭИ268)
Steel 13Х16Н3М2АФ (VNS57)
Steel 12Х18Н9 (Х18Н9)
Steel 12Х12М1БФР (EP450)
Steel 11Х17Н
Steel 10Х25Н6АТМФ
Steel 10Х20Н33Б
10X18H9 steel
10X18N10T steel (EP502)
Steel 10Х12Н3М2БФ
Steel 10Х12Н20Т2 (EP452)
09Cr18Ni9 steel
Steel 09X17N (ChS130)
Steel 08Х20Н12АБФ
Steel 08X19H12TF
Steel 08Х16Н11М3
45X25H35BS steel
Steel CS 116-ID (EP753U-ID)
Steel 9Х13Н6ЛК4 (ЭИ928)
Steel 80X20NS (EP992)
Steel 50X25H35S2B
Steel 50Х25Н35В5К15С
Steel 50Х20Н35С2Б
Steel 50Kh15MFasch
Steel 4Х13Н6ЛВФ (EP354)
Steel 45Х28Н49В5С
Steel 08Cr13 (EI496)
Steel 45X25H20C2
Steel 45X25H20S
Steel 35Х24Н24Б
Steel 32Х13Н6К3М2БДЛТ (VNS-32; SES1)
Steel 30X23H7S
Steel 23Х15Н5АМ3 (18Х15Н6АМ3; VNS-9)
Steel 20Х13Н2ДМЮФ (DI96)
Steel 20X13 (02X13)
Steel 20Х12НМВБФАР (ЧС139)
Steel 02N15K10M5F5
Steel 03N18K8M3TU (ЗИ25)
Steel 03N18K1M3TU (ZI80)
Steel 03N17K10V10MT (EP836)
Steel 03N15K10M5F5 (EK169)
Steel 03N14Cr5M3Tu (OMC-2)
Steel 03N14H5M3T (EP777)
Steel 03N10Cr12D2T
Steel 02X8H22S6 (EP794)
Steel 02N18M3K3T (EK165; ČS101)
Steel 03N18K9M5TU (ChS4)
Steel 01N18K9M5T (EP637U)
Steel 015Cr18Nr15P30 (EP168B)
Steel 015Х18Н15Р26 (EP168А)
Steel 015Cr18Nr15P22 (EP167B)
Steel 015Cr18Nr15P17 (EP167A)
Steel 015Х18Н15Р13 (EP166Б)
Steel 015Cr18Nr15P09 (EP166A)
Steel 015N18M4TU (EP989; ČS5U)
Steel 015N18K13M5TU (EP948; ČS35)
Steel 05X12H2M
Steel 07Х25Н16АГ6Ф (EP750)
Steel 07Х15Н30В5М2 (ChS81)
Steel 07Х12НМФБ (ChS80)
Steel 07Х12НМБФ (EP609)
Steel 06Х16Н15М3БР (EP172)
Steel 06Х16Н15М2Г2ТФР (ЧС68)
Steel 06Х15Н6МВФБ (VNS16)
Steel 06X13H7D2 (EP898)
Steel 05Х12Н5К14М5ТВ (EP695)
Steel 08Х14Н2К3МФБ (EK93; VNS-51)
Steel 04Х16Н11М3Т (DI95)
Steel 03Х17Н14М3 (ЗИ66)
Steel 03Х13Н5М5К9 (VNL-6)
Steel 03Х12Н8МТю (ЗИ37)
Steel 03Х12Н8К5М2ТЮ (ЗИ90)
Steel 03Х11Н10М2Т1 (EP679)
Steel 03Х11Н10М2Т (EP678; VNS-17)
Steel 03N18M4TU (ChS25)
Steel 03N18M3TU (ChS5)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 4Х13Н6ЛВФ |
| Designation GOST Latin | 4X13H6LBF |
| Transliteration | 4H13N6LVF |
| The chemical elements | 4Cr13Н6BeWV |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ЭП354 |
| Designation GOST Latin | EP354 |
| Transliteration | EhP354 |
| The chemical elements | - |
Description
4Х13Н6ЛВФ steel is used: for the manufacture of parts friction devices and assemblies (axles, bearings, slide valve steam, etc.), operating at temperatures up to 400 °C.
Standards
| Name | Code | Standards |
|---|---|---|
| Sectional and shaped rolling | В32 | TU 14-1-506-73 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | V | Ti | W | Be |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-506-73 | 0.3-0.5 | ≤0.025 | ≤0.03 | ≤0.6 | 12-14 | ≤0.6 | 5.5-6.5 | The rest | 0.5-1 | ≤0.3 | 0.5-1 | 0.5-0.85 |
Fe is the basis.
According to TU 14-1-506-73, the chemical composition is given for steel grade 4Х13Н6ЛВФ-ВИ (ЭП354-ВИ).
According to TU 14-1-506-73, the chemical composition is given for steel grade 4Х13Н6ЛВФ-ВИ (ЭП354-ВИ).
Mechanical characteristics
| Section, mm | HRC |
|---|---|
| Bars on the other 14-1-506-73. Quenching in water from 1000 °C + Two to four fold aging at 460-470 °C With exposure for an hour | |
| ≥58 | |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| HRC | Rockwell hardness (indenter diamond spheroconical) |
Physical characteristics
| Temperature | r, кг/м3 | l, Вт/(м · °С) | a, 10-6 1/°С | С, Дж/(кг · °С) |
|---|---|---|---|---|
| 100 | 7740 | 19 | 124 | 460 |
A description of the physical symbols
| Name | Description |
|---|---|
| Е | The normal elasticity modulus |
Technological properties
| Name | The value |
|---|---|
| Forging temperature | The forging temperature of 850-1100 °C. |
| Features of production | Bars at 14-1-506-73 THAT are delivered in heat treated condition for the regime: Normalizing at 950 °C + High tempering at 680 °C for 26 hours, air cooling. The hardness of steel in heat-treated bars shall not exceed 30 units HRC. |