Steel 07Х13АГ20 (ЧС46)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
07Х13АГ20 |
| Designation GOST Latin |
07X13AG20 |
| Transliteration |
07H13AG20 |
| The chemical elements |
07Cr13NMn20 |
| Name |
The value |
| Designation GOST Cyrillic |
ЧС46 |
| Designation GOST Latin |
ChC46 |
| Transliteration |
ChS46 |
| The chemical elements |
ZrС46 |
Description
07Х13АГ20 steel is used: for the manufacture of rolled products, tubular billets and pipes designed for production of equipment of chemical industry, working in a slightly aggressive media.
Note
Steel is non-magnetic, Nickel-free austenitic.
Steel heat-resistant and heat-resistant to +600 °C.
Standards
| Name |
Code |
Standards |
| Thermal and thermochemical treatment of metals |
В04 |
STP 26.260.484-2004 |
| Bulls. Blanks. Slabs |
В31 |
TU 14-1-3159-81, TU 14-1-3248-81 |
| Sectional and shaped rolling |
В32 |
TU 14-1-3243-81 |
| Sheets and stripes |
В33 |
TU 14-1-3342-82, TU14-1-2640 |
| Pipes steel and connecting parts to them |
В62 |
TU 14-3-1322-85, TU 14-3-1323-85 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
N |
B |
Ca |
Ce |
Mg |
| TU 14-1-3159-81 |
≤0.07 |
≤0.025 |
≤0.035 |
19-22 |
12-14 |
≤0.6 |
≤1 |
The rest |
0.08-0.18 |
≤0.003 |
≤0.1 |
≤0.1 |
≤0.01 |
Fe is the basis.
According to TU 14-1-3159-81, the mass fractions of nitrogen, boron, magnesium, cerium and calcium are calculated. Deviations are allowed: by mass fraction of nitrogen ± 0.020%, nickel + 0.30%, manganese ± 0.20%, chromium + 0.50%. Mass fraction of residual elements - according to GOST 5632.
Mechanical characteristics
| Section, mm |
sT|s0,2, MPa |
σB, MPa |
d5, % |
kJ/m2, кДж/м2 |
| The billet according to TU 14-1-3159-81. The longitudinal samples. Quenching in water or air at 950-1000 °C |
| 20-25 |
≥343 |
≥637 |
≥40 |
≥591 |
| Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water or air with 1030-1070 °C |
|
≥350 |
≥670 |
≥40 |
- |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
| kJ/m2 |
Toughness |
Technological properties
| Name |
The value |
| Macrostructure and contamination |
The macrostructure of the workpiece on the other 14-1-3159-81 (when checking for cross etched Templeton) should not be visible without using the magnifying devices podnasadochnogo looseness, cracks, foreign non-metallic microflute, cellular and subcortical bubbles, bundles. The defects allowed must not exceed: on a point inhomogeneity 2 points, according to the Central porosity - 2 points, exudation square - 2 points. Contamination of the metal blanks must not exceed 2 points - sulphides, oxides, stroke, non-deformable silicates, plastic silicates; 3 points - nitrides and carbonitrides. |
| Microstructure |
The contents of alpha phase in the billet on the other 14-1-3159-81 should not exceed 2.0 points. |
| Features of heat treatment |
Steel products for equipment of chemical industry termoobrabotannyj according to mode: heating to 1050±20 °C, the holding time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm max thickness cooling products with wall thickness up to 10 mm in the air, over 10 mm in water. |