Steel 04Х13Н4АГ20 (ЧС52)
Steel 12Х11В2МФ (ЭИ756)
Steel 08Х21Н6М2Т (EP54)
Steel 10Х12Н3М2ФА (ЦД-М)
Steel 10Х12НД (0Х12НД)
Steel 10Х13Г12БС2Н2Д2 (DI59)
Steel 10X18G14AN4 (EP197; X18G14AN4)
Steel 10Х32Н8 (EP263; Х32Н8)
Steel 10Х9МФБ (DI82)
08X14F steel
Steel 12X13 (1X13)
Steel 12X18H10T (X18H10T)
Steel 12Х18Н12Т (Х18Н12Т)
12X18H9SMR steel (EP414; Х18Н9СМР)
Steel 12Х18Н9Т (Х18Н9Т)
Steel 16Х20К6Н2МВФ (EP768; VNS-22)
Steel 19Х20Н4АМ3Д2С (EC7)
Steel 90G29Yu9VBM (DI38; 90G29Yu9VMBF; DI38F)
Steel 03Х24Н6АМ3 (ЗИ130)
Steel 015Х14Н19С6Б (ChS110)
Steel 015Х20Н25Г2Б (EP754)
Steel 02Х24Н6АМ3 (DI91)
Steel 03N18K9M5T (EP637; MS200)
Steel 03Х16Н15М3Б (026Х16Н15М3Б; ЭИ844Б)
Steel 03Х18Н9Т (Х18Н9Т)
Steel 03Х19Н15Г6М2АВ2 (ChS39)
Steel 03Х21Н32М3Б (EP864; ČS33)
Steel 08Х20Н5АГ12МФ (DI8)
Steel 03Х9К14Н6М3Д (EP921; 03Х9К14Н6М3ДФ)
Steel 04Х11Н9М2Д2 (EP832; 04Х11Н9М2Д2ТЮ)
Steel 04Х13Н4АГ20 (ChS52)
Steel 04Х14К13Н4М3ТВ (EP767)
Steel 05Х15Н9Г6АМ (ChS31)
Steel 05Х21Н12Г2БРч (DI94)
Steel 07X13AG20 (ChS46)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 04Х13Н4АГ20 |
| Designation GOST Latin | 04X13H4AG20 |
| Transliteration | 04H13N4AG20 |
| The chemical elements | 04Cr13Н4NMn20 |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ЧС52 |
| Designation GOST Latin | ChC52 |
| Transliteration | ChS52 |
| The chemical elements | ZrС52 |
Description
04Х13Н4АГ20 steel is used: for the production of hot rolled flats, intended for the manufacture of parts of power engineering and aerospace technology, operating at temperatures from -210 °C to +400 °C almost without limit resource exploitation.
Note
Vysokoorganizovannaja low carbon corrosion-resistant heat-resistant and heat-resistant austenitic steel.
Standards
| Name | Code | Standards |
|---|---|---|
| Sheets and stripes | В33 | TU 14-1-2508-78 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | N | B | Ca | Ce |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-2508-78 | ≤0.07 | ≤0.025 | ≤0.035 | 19-22 | 12-14.8 | ≤0.6 | 3.8-5.3 | The rest | 0.08-0.18 | ≤0.003 | ≤0.1 | ≤0.1 |
Fe is the basis.
According to TU 14-1-2508-78 cerium, boron and calcium are introduced into the steel by calculation and chemical analysis is not determined.
According to TU 14-1-2508-78 cerium, boron and calcium are introduced into the steel by calculation and chemical analysis is not determined.