Steel 015Х14Н19С6Б (ЧС110)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
015Х14Н19С6Б |
| Designation GOST Latin |
015X14H19C6B |
| Transliteration |
015H14N19S6B |
| The chemical elements |
015Cr14Н19С6Nb |
| Name |
The value |
| Designation GOST Cyrillic |
ЧС110 |
| Designation GOST Latin |
ChC110 |
| Transliteration |
ChS110 |
| The chemical elements |
ZrС110 |
Description
015Х14Н19С6Б steel is used: for the manufacture of welded chemical equipment operating in the environment of concentrated nitric acid at temperatures up to +110 °C and other highly corrosive conditions and pressures up to 7600 kg/m3.
Note
Low carbon steel Nickel stainless steel austenitic.
Standards
| Name |
Code |
Standards |
| Thermal and thermochemical treatment of metals |
В04 |
STP 26.260.484-2004 |
| Sectional and shaped rolling |
В32 |
TU 14-1-4723-89, TU 14-1-4800-90 |
| Sheets and stripes |
В33 |
TU 14-1-4795-90, TU 14-1-4724-89 |
| Tapes |
В34 |
TU 14-1-4978-91 |
| Pipes steel and connecting parts to them |
В62 |
TU 14-3-1854-92 |
Mechanical characteristics
| Section, mm |
sT|s0,2, MPa |
σB, MPa |
d5, % |
| Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water or air from 1080 °C |
|
≥240 |
≥590 |
≥50 |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
Technological properties
| Name |
The value |
| Features of heat treatment |
The product of the steel subjected to quenching in water from 1050 °C. holding Time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm maximum thickness. |