Steel 5KHV2SF
9X1 steel
Steel 9X5VF
Steel 9G2F (EI972)
Steel 95Kh6M3F3ST (EK80)
Steel 90KhF (9Kh1F; 9KhF)
8XF steel
Steel 8Kh6NFT (85Kh6NFT)
Steel 8X4V2MFS2 (EP761)
Steel 8X3
Steel 8H1A
7CrNiM steel
7ХГ2ВМФ steel
7X3 steel
Steel 7X15VMFSN (ChS93)
7H2MFA steel
6HS steel (EI325)
6XVG steel
X12VMF steel
CGS steel
CVCGF steel
CVG steel
CV4F steel
X9VMF steel
Steel Х6ВФ (ЭИ808)
X12F1 steel
X12MF steel
6XV2S steel
X12 steel
Steel X
B2F steel
9KhFM steel
9XS steel
Steel 9KhVG
Steel 9X6F2ARSTG (EC15)
Steel 3X3M3F (EI76)
4XMF steel
4XMNFS steel
Steel 4Х5МФС (4Х5МФСА)
Steel 4Х5МФ1С (EP572)
Steel 4X5V2FS (EI958)
4X4VMFS steel (DI22)
4X3VMF steel (ZI2)
Steel 4Х2В5МФ (ЭИ959)
4KhMFS (40KhSMF) steel
3X2MNF steel
13X steel
Steel 12X1 (EP430)
Steel 11KhF (11Kh)
Steel 11Х4В2МФ3С2 (DI37)
Steel 05X13H6M2
Steel 05Х12Н6Д2МФСГТ (DI80)
Steel 6Х7В7ФМ (ЭИ161)
4HS steel
Steel 50X14MF (ЗИ128)
Steel 55CM5FA
Steel 55Kh7VSFM (55Kh7VSMF)
Steel 5Х2МНФ (DI32)
Steel 5Х3В3МФС (DI23)
5XANMF steel
5KhV2SF steel
Steel 5KhNV (5KhNVL)
5KhNVS steel
5CrNiM steel
6X3MFS steel (EP788)
6X4M2FS steel (DI55)
6X6V3MFS steel (EP569)
6X6M1F steel
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 5ХВ2СФ |
| Designation GOST Latin | 5XB2CF |
| Transliteration | 5HV2SF |
| The chemical elements | 5CrW2СV |
Description
5KHV2SF steel is used: for the manufacture of knives cold metal cutting; dies, punches and crimp matrix in cold metal working; woodworking tools for continuous operation.
Standards
| Name | Code | Standards |
|---|---|---|
| Sheets and stripes | В33 | GOST 4405-75, TU 14-131-971-2001 |
| Sectional and shaped rolling | В32 | GOST 5950-2000, GOST 14955-77 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Cu | V | Ti | Mo | W |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| GOST 5950-2000 | 0.45-0.55 | ≤0.03 | ≤0.03 | 0.15-0.45 | 0.9-1.2 | 0.8-1.1 | ≤0.4 | ≤0.3 | 0.15-0.3 | ≤0.03 | ≤0.2 | 1.8-2.3 |
Mechanical characteristics
| Section, mm | sT|s0,2, MPa | σB, MPa | d5, % | y, % | kJ/m2, кДж/м2 |
|---|---|---|---|---|---|
| Rolled steel. Quenching in oil at 880 °C + Vacation at 450 °C (aging for 2 hours) | |||||
| ≥1570 | ≥1668 | ≥6 | ≥15 | ≥280 | |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| sT|s0,2 | Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB | Limit short-term strength |
| d5 | Elongation after rupture |
| y | The relative narrowing |
| kJ/m2 | Toughness |