Steel 08H18N10 (ЭИ119)

Steel 10Х15Н27Т3МР (EP700) Steel 08Cr17T (EI645) Steel 08Cr18Ni10 (EI119) Steel 08Cr18Ni10T (EI914) Steel 08X18T1 (0X18T1) Steel 08Х20Н14С2 (ЭИ732) Steel 09Cr18Ni10T (1Cr18Ni10T) Steel 10Х13Г18Д (DI-61; 12Х13Г18Д) Steel 06X18H10T (06X18H10) Steel 12X17 (X17) Steel 12Х20Н14С2 (ЭИ732) Steel 13Х13С2М2 (ЭИ852) Steel 15X25T (EI439) Steel 15X28 (EI349) Steel 20Х20Н14С2 (ЭИ211) 4X18H2M steel (EP378) Steel 06X20H14C2 Steel 06Х18Г9Н5АБ (06Х18Г5Н5АБ; ЧС51) Steel 06Х16Н2К5ФМБ (EP875; VNS-26) 05Cr18Ni10T (0Cr18Ni10T) steel Steel 03X20Yu3NTB (KO-4) Steel 03Cr18Ni10T (03Cr18Ni10T; Cr18Ni10T) Steel 03Х17Н8Г5МФАБ (VNS-31) Steel 03Х11Н8М2Ф (DI52) Steel 01Х25ТБЮ (ChS76; 01Х25ТБ) Steel 01X25T (ChS75) Steel 01X25M2T (ChS78) Steel 01X13MBSch (EP933) Steel 01X18T (ChS74) Steel 01X18M2T (ChS77) Steel 01X18 (ChS86) Steel 015Cr18M2B (EP882)

Designation

Name The value
Designation GOST Cyrillic 08Х18Н10
Designation GOST Latin 08X18H10
Transliteration 08H18N10
The chemical elements 08Cr18Н10
Name The value
Designation GOST Cyrillic ЭИ119
Designation GOST Latin EI119
Transliteration EhI119
The chemical elements -

Description

08X18H10 steel is used: for the manufacture of chemical equipment; pipes and fittings furnace fittings; heat exchangers, muffles, retorts, pipes, manifolds, exhaust systems, spark electrodes incendiary spark, welding machines and vessels chemical engineering, operating at temperatures from -196 °C to +600 °C medium activity; objects of consumption in the household; vehicles and parts in the food industry; welded products operating in environments of higher aggressiveness than steel 12X18H10T without limit pressures up to +600 °C; cold-rolled steel and roll-formed profiles, intended for the manufacture of oblivi and frame of body of passenger cars; the wire woven grids with square cells of micron size, used for control and separation of materials by particle size, filtration of liquids, gases and other purposes.

Note

Steel corrosion and heat-resistant.
Unstabilized chromium-Nickel steel of austenitic class.
The recommended maximum operating temperature for a long time +800 °C.
Temperature intense scaling in air +850 °C.
Steel is unstable in sulfur-containing environments and is used when cannot be applied, Nickel-free steel.

Standards

Name Code Standards
Sheets and stripes В23 GOST 103-2006
Sectional and shaped rolling В22 GOST 1133-71, GOST 2590-2006, GOST 2591-2006, GOST 2879-2006
Test methods. Packaging. Marking В09 GOST 11878-66
Steel alloy wire В73 GOST 18143-72, TU 14-173-64-95
Metal forming. Forgings В03 GOST 25054-81
Sheets and stripes В33 GOST 4405-75, GOST 5582-75, GOST 7350-77, GOST Р 51393-99, TU 108-930-80, TU 14-105-451-86, TU 14-1-1009-74, TU 14-1-2186-77, TU 14-1-3199-81, TU 14-1-4780-90
Tapes В34 GOST 4986-79, TU 14-1-1370-75, TU 14-1-3502-82, TU 14-1-4606-89
Classification, nomenclature and general norms В30 GOST 5632-72
Sectional and shaped rolling В32 GOST 5949-75, GOST 7417-75, GOST 8559-75, GOST 8560-78, GOST 14955-77, GOST 18907-73, TU 14-1-1534-76, TU 14-11-245-88
Pipes steel and connecting parts to them В62 GOST 9940-81, GOST 9941-81, TU 14-158-135-2003, TU 14-3-1654-89
Bulls. Blanks. Slabs В31 OST 3-1686-90, TU 14-1-1213-75, TU 14-1-1214-75, TU 14-1-565-84
Thermal and thermochemical treatment of metals В04 STP 26.260.484-2004
Metal nets В76 TU 14-4-507-99

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu V Ti Mo W
TU 108-930-80 ≤0.08 ≤0.02 ≤0.035 ≤2 17-19 ≤0.8 9-11 The rest ≤0.5 ≤0.2 ≤1 ≤0.5 ≤0.2
TU 14-1-4780-90 ≤0.08 ≤0.02 ≤0.035 ≤2 17-19 ≤0.8 9-11 The rest ≤0.3 ≤0.2 ≤0.5 ≤0.3 ≤0.2
Fe is the basis.
According to TU 14-1-2186-77 for steel smelted with electroslag remelting the content of S ≤ 0.015%.

Mechanical characteristics

Section, mm sT|s0,2, MPa σB, MPa d5, % d4 d y, %
Cold-rolled steel strip of 0.05-2.00 mm according to GOST 4986-79 on delivery
0.2-2 - ≥740 - ≥12 - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥210 ≥570 ≥60 - - ≥70
Cold-rolled steel strip of 0.05-2.00 mm according to GOST 4986-79 on delivery
0.2 - ≥740 - ≥6 - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥110 ≥410 ≥46 - - ≥69
Cold-rolled steel strip of 0.05-2.00 mm according to GOST 4986-79. Quenching in water or air from 1050-1080 °C (samples)
0.2-2 - ≥530 - ≥40 - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥98 ≥380 ≥45 - - ≥69
Cold-rolled steel strip of 0.05-2.00 mm according to GOST 4986-79. Quenching in water or air from 1050-1080 °C (samples)
0.2 - ≥530 - ≥20 - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥96 ≥360 ≥44 - - ≥70
Hot rolled sheet (of 1.5-3.9 mm) and cold rolled (0,7-3,9 mm) steel according to GOST 5582-75. Without heat treatment
≤3.9 - ≥930 ≥10 - - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥82 ≥330 ≥39 - - ≥58
Hot rolled sheet (of 1.5-3.9 mm) and cold rolled (0,7-3,9 mm) steel according to GOST 5582-75. Without heat treatment
≤3.9 - 740-930 ≥25 - - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥76 ≥290 ≥37 - - ≥44
Hot rolled sheet (of 1.5-3.9 mm) and cold rolled (0,7-3,9 mm) steel according to GOST 5582-75. Quenching in water or air from 1050-1080 °C
- ≥205 ≥510 ≥45 - - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥74 ≥235 ≥35 - - ≥36
Hot rolled sheet (4,0-50,0 mm) and cold rolled (4,0-5,0 mm) steel according to GOST 7350-77. Annealing in air or in water 1050-1100 °C
- ≥205 ≥510 ≥43 - - -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥73 ≥185 ≥31 - - ≥28
The wire is heat-treated in the delivery condition according to GOST 18143-72 (elongation, % at rated sample length of 100 mm is specified for the wire of the 1st class in brackets are for 2nd class). Quenching in air, oil or water with 1020-1100 °C
0.2-1 - 590-880 - - ≥25 (≥20) -
Rolled steel. Quenching in water with 1000-1120 °C
- ≥69 ≥150 ≥30 - - ≥18
The wire is heat-treated in the delivery condition according to GOST 18143-72 (elongation, % at rated sample length of 100 mm is specified for the wire of the 1st class in brackets are for 2nd class). Quenching in air, oil or water with 1020-1100 °C
1.1-6 - 510-830 - - ≥25 (≥20) -
Cold drawn wire in the delivery state according to GOST 18143-72
0.2-3 - 1130-1470 - - - -
3.4-6 - 1080-1420 - - - -
The cold rolled sheets and decks cold-shaped sections heat-treated in the delivery condition according to GOST R 51393-99. Quenching in water or air from 1050-1080 °C
- ≥205 ≥510 ≥45 - - -
Bars of polished, processed on a given strength (TS) according to GOST 18907-73
1-30 - 640-780 - - ≥20 -
Bars hot rolled and forged GOST 5949-75 + Forgings up to 100 mm. Hardening in air, oil or water with 1020-1100 °C
≥196 ≥470 ≥40 - - ≥55
Bars hot rolled and forged at STP 26.260.484-2004. Quenching in water from 1050-1100 °C
≥200 ≥480 ≥40 - - ≥55
Pre-painted steel sheet heat-treated (softening) on the other 14-1-3199-81
0.5-3 ≥274.4 ≥529.2 ≥45 - - -
Tubes in the delivery condition, without heat treatment
- - ≥510 ≥40 - - -
- - ≥529 ≥37 - - -

Description mechanical marks

Name Description
Section Section
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
d4 Elongation after rupture
d Elongation after rupture
y The relative narrowing

Physical characteristics

Temperature Е, ГПа r, кг/м3 l, Вт/(м · °С) R, НОм · м a, 10-6 1/°С С, Дж/(кг · °С)
0 196 7850 17 800 - -
20 196 7850 17 800 - -
100 - - - - 16 504
200 - - - - 17 -
300 - - - - 17 504
400 - - - - 18 -
500 - - - - 18 -
700 - - - - 18 -

A description of the physical symbols

Name Description
Е The normal elasticity modulus
r Density
l Coefficient of thermal conductivity
R UD. the resistivity
a The coefficient of linear expansion
С Specific heat

Technological properties

Name The value
Weldability Without restrictions. Welding method: SMAW - electrodes OzL-8, OzL-12 on wires 02Х19Н9, CCC, ESW. Recommended subsequent heat treatment. Welded joints made by other methods, in addition to spot welding, prone to intergranular corrosion.
Forging temperature Start - 1200 °C, the end - 850 °C. the cross Sections up to 300 mm are cooled in stacks on the air.
Features of heat treatment Steel used for products, not subjected to welding is designed to work in environments do not cause intergranular corrosion. To increase the resistance against General corrosion and eliminate the tendency to intergranular corrosion and to improve the ductility of the workpiece material is subjected to annealing regime: heating to 1050-1100 °C, cooling in water. The holding time at the heating for hardening to products with a wall thickness up to 10 mm - 30 min, over 10 mm - 20 min + 1 min per 1 mm maximum thickness.

Our consultant will save your time

+49(1523) 72 15 100
E-mail:
Telegram:
WhatsApp:
Ask a question

Subscription

Special offers and discounts. :)
stainless steel hexagon, copper plate, Titanium pipe, Inconel 601, B-16 Babbitt