Steel 05KH18N10T (0Х18Н10Т)
Steel 10Х15Н27Т3МР (EP700)
Steel 08Cr17T (EI645)
Steel 08Cr18Ni10 (EI119)
Steel 08Cr18Ni10T (EI914)
Steel 08X18T1 (0X18T1)
Steel 08Х20Н14С2 (ЭИ732)
Steel 09Cr18Ni10T (1Cr18Ni10T)
Steel 10Х13Г18Д (DI-61; 12Х13Г18Д)
Steel 06X18H10T (06X18H10)
Steel 12X17 (X17)
Steel 12Х20Н14С2 (ЭИ732)
Steel 13Х13С2М2 (ЭИ852)
Steel 15X25T (EI439)
Steel 15X28 (EI349)
Steel 20Х20Н14С2 (ЭИ211)
4X18H2M steel (EP378)
Steel 06X20H14C2
Steel 06Х18Г9Н5АБ (06Х18Г5Н5АБ; ЧС51)
Steel 06Х16Н2К5ФМБ (EP875; VNS-26)
05Cr18Ni10T (0Cr18Ni10T) steel
Steel 03X20Yu3NTB (KO-4)
Steel 03Cr18Ni10T (03Cr18Ni10T; Cr18Ni10T)
Steel 03Х17Н8Г5МФАБ (VNS-31)
Steel 03Х11Н8М2Ф (DI52)
Steel 01Х25ТБЮ (ChS76; 01Х25ТБ)
Steel 01X25T (ChS75)
Steel 01X25M2T (ChS78)
Steel 01X13MBSch (EP933)
Steel 01X18T (ChS74)
Steel 01X18M2T (ChS77)
Steel 01X18 (ChS86)
Steel 015Cr18M2B (EP882)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 05Х18Н10Т |
| Designation GOST Latin | 05X18H10T |
| Transliteration | 05H18N10T |
| The chemical elements | 05Cr18Н10Ti |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 0Х18Н10Т |
| Designation GOST Latin | 0X18H10T |
| Transliteration | 0H18N10T |
| The chemical elements | 0Cr18Н10Ti |
Description
05KH18N10T steel is used: for the manufacture of thin-sheet cold-rolled steel; bellows-expansion joints.
Note
Steel corrosion and heat-resistant austenitic class.
Steel 05KH18N10T has a high ability to deep drawing than steel grades 08KH18N10T and 12KH18N10T.
Standards
| Name | Code | Standards |
|---|---|---|
| Classification, nomenclature and general norms | В30 | GOST 5632-72 |
| Bulls. Blanks. Slabs | В31 | OST 3-1686-90, TU 14-1-4681-89 |
| Tapes | В34 | OST 5.9093-72, TU 14-1-4606-89 |
| Sheets and stripes | В33 | TU 14-105-451-86, TU 14-1-3874-84 |
| Sectional and shaped rolling | В32 | TU 14-11-245-88 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | V | Mo | W |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-3874-84 | ≤0.05 | ≤0.02 | ≤0.035 | 1.2-2 | 17-18.5 | ≤0.8 | 9-10.5 | The rest | ≤0.3 | ≤0.2 | ≤0.3 | ≤0.2 |
| GOST 5632-72 | ≤0.05 | ≤0.02 | ≤0.035 | 1-2 | 17-18.5 | ≤0.8 | 9-10.5 | The rest | ≤0.3 | ≤0.2 | ≤0.3 | ≤0.2 |
Fe is the basis.
According to GOST 5632-72, TU 14-1-3874-84 and TU 14-1-4606-89 the content of Ti% = 5С% - 0,6%.
According to TU 14-1-3874-84, according to the agreement between the consumer and the supplier, the steel is treated with synthetic slag (it is introduced by calculation of silicocalcals and cerium (misch metal) in an amount of 0.05-0.20% and 0.01-0.10% respectively, which chemical analysis is not determined). The residual content of aluminum in steel is not more than 0.10%. The ratio of chromium to nickel is not more than 1.8. By agreement of the parties, it is allowed to supply thick-gauge steel coils with the requirements for the mass fraction of carbon not more than 0.05%, manganese 1.20-2.00%. The rest of the elements are GOST 5632 for steel 08H18N10T.
According to GOST 5632-72, TU 14-1-3874-84 and TU 14-1-4606-89 the content of Ti% = 5С% - 0,6%.
According to TU 14-1-3874-84, according to the agreement between the consumer and the supplier, the steel is treated with synthetic slag (it is introduced by calculation of silicocalcals and cerium (misch metal) in an amount of 0.05-0.20% and 0.01-0.10% respectively, which chemical analysis is not determined). The residual content of aluminum in steel is not more than 0.10%. The ratio of chromium to nickel is not more than 1.8. By agreement of the parties, it is allowed to supply thick-gauge steel coils with the requirements for the mass fraction of carbon not more than 0.05%, manganese 1.20-2.00%. The rest of the elements are GOST 5632 for steel 08H18N10T.
Mechanical characteristics
| Section, mm | sT|s0,2, MPa | σB, MPa | d4 |
|---|---|---|---|
| Sheet cold rolled steel in the delivery state on the other 14-1-3874-84 (0.3-1.0 mm), THE 14-1-4606-89 (1.5-1.8 mm). Samples of the cross | |||
| ≤285 | 510-640 | ≥50 | |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| sT|s0,2 | Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB | Limit short-term strength |
| d4 | Elongation after rupture |