Steel АЦ45Г2
Steel AC35G2
AC20X steel
Steel АЦ20ХГНМ
Steel АЦ20ХН3
Steel АЦ25ХГТ
AC30 steel
AC30X steel
АЦ30Х3МФ steel
АЦ30ХМ steel
AC35 steel
Steel АЦ18ХН2Т
AC35X steel
АЦ38ХС steel
AC40 steel
Steel AC40G
АЦ40Х steel
AC45 steel
Steel AC45G2
AC45X steel
AC50 steel
Steel AC50X
AC20CrNiM steel
A11 steel
A12 steel
A20 steel
A30 steel
A35 steel
A40G steel
AC12CrN steel
AC14 steel
AC14CrN steel
AC19CrN steel
AC20 steel
AC30CrM steel
AC35G2 steel
AC38CrHm steel
AC40 steel
AC40X steel
AC40CrNiM steel
AC45G2 steel
Steel ACS30CrM
АЦ18ХГТ steel
To access the entire list
Designation
Description
АЦ45Г2 steel is used: for the production of bars intended for the manufacture of automotive components by hot forming with subsequent machining.
Note
Calcium-containing steel of high machinability.
Standards
Chemical composition
Fe is the basis.
According to TU 14-1-3283-81 chemical analysis is given for steel grade AC45G2. In the designation of steel letters mean: A - automatic, C - calcium. The microalloying of calcium steel is carried out by silicocalcium and other calcium alloys at the rate of introduction of 0.030-0.090% calcium into a liquid metal. The mass fraction of calcium is not determined by chemical analysis. The presence of tungsten to 0.20%, molybdenum to 0.15%, titanium to 0.030% and vanadium to 0.050% is not a defect. In the finished bars, subject to the requirements of the technical specification, deviations in chemical composition are allowed: for carbon ± 0.010%, for manganese ± 0.050%, for silicon ± 0.020%, for chromium ± 0.020%, for nickel -0.050%, for sulfur and phosphorus + 0.0050% of each.
According to TU 14-1-3283-81 chemical analysis is given for steel grade AC45G2. In the designation of steel letters mean: A - automatic, C - calcium. The microalloying of calcium steel is carried out by silicocalcium and other calcium alloys at the rate of introduction of 0.030-0.090% calcium into a liquid metal. The mass fraction of calcium is not determined by chemical analysis. The presence of tungsten to 0.20%, molybdenum to 0.15%, titanium to 0.030% and vanadium to 0.050% is not a defect. In the finished bars, subject to the requirements of the technical specification, deviations in chemical composition are allowed: for carbon ± 0.010%, for manganese ± 0.050%, for silicon ± 0.020%, for chromium ± 0.020%, for nickel -0.050%, for sulfur and phosphorus + 0.0050% of each.