Alloy ХН57КВЮТМБРЛ (ЧС88У)
Alloy ZhS3LS
Alloy KhN63MYUTBV (SZHL-800; EK112)
Alloy KhN58KTVYUMBL (ChS104)
Alloy KhN58KVTYUMBL (ChS70; CH25)
Alloy KhN57KVYUTMBRL (ChS88U)
Alloy KhN57KVYUTMBL (ChS88)
Alloy KhN57VMTYUBL (ChS91)
Alloy KhN54MVTYUL (ChS94)
Alloy CrN35Zh14AMTL
Alloy LK4
Alloy L114
Alloy ZhS6K
Alloy ZhS3DK
Alloy VZHL2M
Alloy VZHL15
Alloy B56
Alloy B3K
Alloy Biduloid
Alloy 45X26H33S2B2
Alloy 45Х26Н23С2Б2
Alloy 12XH28MDTL (EI629)
Alloy 06Х20Н10М3Д3С4Л (06Х20Н10М3Д3С4)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ХН57КВЮТМБРЛ |
| Designation GOST Latin | XH57KBJuTMBPL |
| Transliteration | HN57KVYuTMBRL |
| The chemical elements | CrNi57CoВAlTeCuBeHg |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ЧС88У |
| Designation GOST Latin | ChC88U |
| Transliteration | ChS88U |
| The chemical elements | ЧPb88У |
Description
Alloy ХН57КВЮТМБРЛ used: for the production of cast bars in a vacuum-induction remelting for the manufacture by the method of directional solidification of shaped castings of parts of power engineering, operating at temperatures up to 1150 °C.
Note
High-temperature Nickel-based alloy with hafnium.
Standards
| Name | Code | Standards |
|---|---|---|
| Sectional and shaped rolling | В32 | TU 14-1-4828-90 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | N | As | Al | B | Ti | Mo | Sb | Pb | Bi | Nb | W | Ce | Zr | Co | Y | Hf |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-4828-90 | 0.04-0.09 | ≤0.008 | ≤0.008 | ≤0.3 | 15.4-16.3 | ≤0.3 | The rest | ≤0.9 | ≤0.1 | ≤0.01 | ≤0.0005 | 2.8-3.3 | 0.06-0.1 | 4.2-5 | 1.6-2.3 | ≤0.0005 | ≤1.0E-5 | ≤5.0E-5 | 0.1-0.3 | 4.7-5.9 | 0.015 | 0.05 | 10-11.5 | 0.03 | 0.2-0.4 |
Ni is the basis.
According to TU 14-1-4828-90 the chemical composition is given for the alloy KhN57KVYUTMBLL-VI (ChS88U-VI). Zirconium, yttrium and cerium are introduced into the metal by calculation and chemical analysis are not determined. It is possible to estimate the mass fraction of arsenic in points on the scale of spectral analysis - the mass fraction of arsenic should be no more than 1 point.
According to TU 14-1-4828-90 the chemical composition is given for the alloy KhN57KVYUTMBLL-VI (ChS88U-VI). Zirconium, yttrium and cerium are introduced into the metal by calculation and chemical analysis are not determined. It is possible to estimate the mass fraction of arsenic in points on the scale of spectral analysis - the mass fraction of arsenic should be no more than 1 point.
Technological properties
| Name | The value |
|---|---|
| Features of production | Cast bars on the other 14-1-4828-90 are supplied with a diameter of 95 mm with a solid abrasive Stripping. On the surface of bars allowed in: oxide films, contamination, inclusion of foreign metal as well as afloat, increasing the size of bars. Quality control of the surface subjected to each rod according to agreed standards. |