Alloy AMK
Alloy AMK
Alloy AMST
Alloy AH-2.5
Alloy AO12-1
Alloy AO20-1
Alloy AO3-7
Alloy AO6-1
Alloy AO9-1
Alloy AO9-2
Alloy ACM
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | АМК |
| Designation GOST Latin | AMK |
| Transliteration | AMK |
| The chemical elements | - |
Description
Alloy AMK applies: for bimetallic strip steel by rolling and subsequent punching of liners with a thickness of friction layer is less than 1 mm.
Note
The recommended modes of operation:
— load ≤ 50,0 Mn/m2 (500 kgf/cm2);
— sliding speed ≤ 20 m/s;
temperature ≤ 120 °C;
— recommended shaft hardness ≥ 250 HB.
On an antifriction layer of articles coated with a soft metal or a polymer antifriction coating thickness of from 0.003 to 0.03 mm. permitted by agreement with the consumer in technically justified cases to cover the product with a soft metal or polymer coating.
Standards
| Name | Code | Standards |
|---|---|---|
| Non-ferrous metals, including rare metals, and their alloys | В51 | GOST 14113-78 |
Chemical composition
| Standard | Mn | Si | Fe | Cu | Al | Ti | Sb | Mg | Te |
|---|---|---|---|---|---|---|---|---|---|
| GOST 14113-78 | ≤0.1 | 9-11 | ≤0.4 | 0.8-1.2 | The rest | ≤0.1 | ≤0.5 | ≤0.3 | ≤0.1 |
Al is the base.
According to GOST 14113-78, the content of other impurities, individually, should be ≤ 0.10%, and the total content of other impurities should be ≤ 0.30%.
According to GOST 14113-78, the content of other impurities, individually, should be ≤ 0.10%, and the total content of other impurities should be ≤ 0.30%.