Alloy 03N18K8M5T-VD

Production

Alloy 03N18K8M5T-VD belongs to the group of martensitic-aging steels and fully meets the strict requirements of GOST. It is melted in induction open furnaces and subjected to vacuum arc remelting. Production is carried out according to technical specifications: 14-1-4479-88, 14-1-3140-81.

Percentage composition

Co C Al Fe Ni Mo Mn P Ti Si S
7,5-8,5 ≤0,03 ≤0,15 basis 17,7-19 4,2-5 ≤0,1 ≤0,01 0,2-0,4 ≤0,1 ≤0,01

The following types of rolled products are produced: rounds, sheets, tubes, wires, strips. Pipes can be seamless - solid drawn and welded - electro-welded. The production of a circle is carried out by stamping the metal under a certain prescribed shape. Circles can be used in the form of forgings, i.e. intermediate billets. During hot rolling and stamping, the temperature at the beginning of the process = 1170 °C, and at the end - about 900 °C. The steel is fairly easy to cut. Sheets and bars are supplied without heat treatment. The technical documentation for the supply of rolled metal products guarantees the quality control standards of the alloy:

- chemical composition of alloying elements;

- allowable content of impurities;

- Absence of bubbles, shrinkage looseness, slag inclusions, cracks;

- mechanical properties;

- ultrasonic test;

- Geometry and dimensions (allowable deviations, surface quality, curvature).

Physical properties at 20°C

- Thermal conductivity 0.19 - 10² W/(m - K).

- Specific weight 8.1 g/cm3

- Modulus of elasticity 19-20 - 10-4 N/mm2

- Hardness 200 NV MPa-1

- Specific resistance 0.38 - 0.4 Ohmxmm2/m.

- Specific heat capacity 0,504 - 103, J/(kg - K);

- Temperature coefficient of linear expansion 10.0-10.5x10-6/°C

- Saturation induction 8-14 kGc.

- Residual induction 5-8 kGc

- Poisson's ratio 0.250; at t° 96 °C 0.235.

Advantages of

High resistance to intergranular corrosion and to corrosion cracking in alkaline and chloride environments. Alloying promotes high-temperature strength and makes it possible to produce parts for power-type installations with this steel grade. It is used in the manufacture of high pressure tanks (vessels), as well as loaded parts, axles, bolts for fasteners. In the case of unstressed conditions it is possible to change this steel grade to another one with lower carbon content.

Welding

Alloy 03N18K8M5T-VD is welded by automatic and manual argon arc welding. During manual arc welding electrodes with a wire rod of steel Sv-03N18K8M5T-VD are used. Welding seams are not subject to formation of hot and cold cracks.

Use

Production of loaded parts for mechanical engineering and metallurgical equipment - axles, bolts for fasteners. Used in industrial chemistry for tanks (vessels) of high pressure, which operate in highly aggressive environments, at t° up to 80 °C.

Supplier

Are you interested in 03N18K8M5T-VD alloy? Alloy 03N18K8M5T-VD from the supplier "Auremo" meets GOST and international quality standards. Supplier "Auremo" offers to buy stainless steel on favorable terms, the price is optimal. We offer to buy stainless steel from the specialized warehouses of the supplier "Auremo" with delivery to any city. Wholesale customers the price - favorable. Always in stock stainless steel, price - optimal from the supplier. We are waiting for your orders.

Buy a bargain price.

Supplier "Auremo" offers to buy steel 03N18K8M5T-VD, the price - due to the technological features of production without the inclusion of additional costs. The company's website displays information about the latest arrivals of products. It is possible to buy products with non-standard parameters to order. The order price depends on the volume and additional terms of delivery. The supplier "Auremo" invites to buy stainless steel in bulk or by installments. We have the best price-quality ratio for the whole range of products. In this segment Auremo is a profitable supplier.