Alloy 15Х25Н40М2ВТ

Designation

Name The value
Designation GOST Cyrillic 15Х25Н40М2ВТ
Designation GOST Latin 15X25H40M2BT
Transliteration 15H25N40M2VT
The chemical elements 15Cr25Ni40Cu2ВTe

Description

Alloy 15Х25Н40М2ВТ used: for the manufacture of pipes tsentrobezhnolityh for the manufacture of the coils of the tubular furnace installations production of ammonia, hydrogen, ethylene, carbon disulphide, etc., operating in the temperature range 760−1060 °C and a pressure of 3.92 MPa (40 kgf/cm2); seamless hot — and cold-drawn pipes used in the production of ammonia, hydrogen, methanol, ethylene, carbon disulphide etc.

Standards

Name Code Standards
Pipes steel and connecting parts to them В62 TU 1333-047-00220302-02, TU 1320-003-18648658-00

Chemical composition

Standard C S P Mn Cr Si Ni Fe Cu As Al V B Ti Mo Zn Sn Pb W Zr
TU 1333-047-00220302-02 0.1-0.25 ≤0.025 ≤0.025 0.05-1.55 24-27 1.195-1.95 38-41 The rest ≤0.2 ≤0.01 0.0005-0.1 0.0005-0.1 0.0005-0.01 0.2-0.6 1-3.1 ≤0.01 ≤0.01 ≤0.01 0.2-0.8 0.0005-0.05
Fe is the basis.

Mechanical characteristics

sT|s0,2, MPa σB, MPa d5, %
Seamless pipes hot and cold-of an external diameter 25-168 mm. Quenching in water or air from 1100-1150 °C
≥206 ≥500 ≥25
Tsentrobezhnolityh pipe outer diameter 85-320 mm. Quenching in water or air from 1100-1150 °C
≥196 ≥441 ≥15

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture