Alloy SV-08Х25Н60М10 (ЭП606)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
Св-08Х25Н60М10 |
| Designation GOST Latin |
Cb-08X25H60M10 |
| Transliteration |
Sv-08H25N60M10 |
| The chemical elements |
08Cr25Ni60Cu10 |
| Name |
The value |
| Designation GOST Cyrillic |
ЭП606 |
| Designation GOST Latin |
EP606 |
| Transliteration |
EhP606 |
| The chemical elements |
- |
Description
Alloy SV-08Х25Н60М10 used: for the production of welding wire designed for mechanized welding of dissimilar heat-resistant steels with high-alloy heat-resistant steels and welding of hardened steels without subsequent heat treatment in construction, metallurgy, oil extraction, medicine, heavy engineering, operating in the temperature range 550−600 °C; the manufacture of electrodes ANZHR-1.
Note
High-alloyed high-temperature Nickel-based alloy.
Standards
| Name |
Code |
Standards |
| Welding and cutting of metals. Soldering, riveting |
В05 |
TU 14-1-4968-91, TU 14-4-568-74, TU 14-1-773-73, TU 14-1-2461-78 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
Ti |
Mo |
| TU 14-1-4968-91 |
≤0.1 |
≤0.015 |
≤0.015 |
1-2 |
23.5-26.5 |
≤0.4 |
58.5-61.5 |
The rest |
- |
9-11 |
| TU 14-4-568-74 |
≤0.11 |
≤0.016 |
≤0.023 |
1.4-2.6 |
22-26 |
≤0.4 |
57-61.5 |
The rest |
≤0.1 |
8.8-11 |
Ni is the basis.
According to TU 14-1-4968-91, the chemical composition is given for the alloy Sv-08X25N60M10 (EP606).
According to TU 14-4-568-74, the chemical composition is given for the welded weld metal made by the ANZhR-1 welding electrode manufactured from the Sv-08Kh25N60M10 alloy (EP606).
Mechanical characteristics
| σB, MPa |
d5, % |
kJ/m2, кДж/м2 |
| Weld, the weld electrode brand ANZHR-1 in the initial state on the other 14-4-568-74 |
| ≥610 |
≥25 |
≥1177 |
Description mechanical marks
| Name |
Description |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
| kJ/m2 |
Toughness |
Technological properties
| Name |
The value |
| Microstructure |
The content of ferritic phase in the wire is governed only by agreement of the parties. |
| Features of production |
Wire on the other 14-1-4968-91 diameter up to 2.0 mm inclusively, supplied in cold-worked condition with a compression no more than 50% and over 2.0 mm supplied in heat treated condition. |