Alloy ХН57ВКЮТМБЛ (ЖС6)
Alloy KhN66VMTYUB (EI698MP; VZH136)
Alloy KhN67VMTU (EP202; KhN67MVTU)
Alloy KhN65KMVYUB (EP800)
Alloy CrN65VMYUTL (EI893L)
Alloy KhN65VMTU (EI893)
Alloy CrN65VMMBU (EP914; VZH131)
Alloy CrN65VBMYu (EP902)
Alloy KhN62MVKYu (EI867)
Alloy KhN62VMYUT (EP708)
Alloy KhN62VMKU (EI867)
Alloy KhN62BMKTU (EP742)
Alloy CrN62BMVY (EP709)
Alloy KhN60MYUVT (EP539)
Alloy KhN60MVTU (EP487)
Alloy KhN60M (EP367; 06Kh15N60M1)
Alloy KhN60KMYUVTB (EC9)
Alloy CrN60KMYUBVTF (EP962)
Alloy KhN60KVYUMB (EP957)
Alloy KhN59VG (EK82)
Alloy KhN58MBYUD (EK61)
Alloy KhN58MBYu (EK171; VZH159)
Alloy KhN58VMKYR (EP238)
Alloy KhN57MTVU (EP590)
Alloy KhN73MBTU (EI698)
Alloy EP539LMU
Alloy ChS70
Alloy ChS104
Alloy CNK7
Alloy KhN80TBY (EI607; KhN80T1BY (EI607A))
Alloy KhN80 (EI334)
Alloy KhN77TURU (EI437BU)
Alloy KhN77TUR (EI437B)
Alloy KhN75TBU (EI869)
Alloy KhN75VMU (EI827)
Alloy CrN75VMFU (EI827)
Alloy KhN57MKYUVTBR (EP958)
Alloy KhN71MTYUB (EI698P)
Alloy KhN70MVU (EI828)
Alloy KhN70MVTYUB (EI598)
Alloy KhN70VMYUT (EI765)
Alloy CrN70VMFTU (EI826)
Alloy CrN70VMTUF (EI826; CrN70VMTUF)
Alloy KhN70VMTU (EI617)
Alloy KhN70 (EI442)
Alloy KhN68VMTYUK (EP693)
Alloy KhN67MBYu (EP782)
Alloy VZHL12E
Alloy ZhS6KP
Alloy ZhS30
Alloy ZhS3
Alloy ZhS16
Alloy BC9L
Alloy BC4LM
Alloy BC4L
Alloy VZHL2
Alloy VZhL18
Alloy VZHL16
Alloy VZHL14H (VZHL14)
Alloy ZhS6U
Alloy VZHL12U
Alloy VZhL1
Alloy 67H26M (EI639; NIMO-25)
Alloy 58NHVKTBU (EP877; ХН58VCBTU)
Alloy 50H6MFA
Alloy 50H3CU (EP967)
Alloy 3MI3U
Alloy 10X20H77TU
Alloy 03Х20Н45М4БЧ (ChS42)
Alloy 03X20H45M4BRZ (ChS43)
Alloy KhN52KVMTYUB (EP975P)
Alloy KhN56MBYUD (EK62)
Alloy KhN56VMTU (EP199; VZh101)
Alloy KhN56VMKU (EP109)
Alloy KhN55MVU (EP454)
Alloy KhN55MVTs (ChS57)
Alloy KhN55MBYu (KhN63M9B2u; EP666)
Alloy KhN55VMTFKU (EI929)
Alloy KhN55VMTKU (EI929)
Alloy KhN54KVMTYUB (EP962P)
Alloy KhN53KVMTYUB (EP741P)
Alloy KhN57VKYUTMBL (ZhS6)
Alloy KhN51MTYUKFR (EP220)
Alloy KhN51KVMTYUB (EP741NP)
Alloy KhN50KVMTYUB (BB750)
Alloy KhN50VMTYUB (EP648)
Alloy KhN50VMTKFY (EP57)
Alloy KhN45MVTYUBR (EP718)
Alloy Kh15N60Yu3A (EP548)
Alloy H95S3Yu (EP711)
Alloy H95G (EP18)
Alloy H70M (EP495)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ХН57ВКЮТМБЛ |
| Designation GOST Latin | XH57BKJuTMBL |
| Transliteration | HN57VKYuTMBL |
| The chemical elements | CrNi57ВCoAlTeCuBe |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | ЖС6 |
| Designation GOST Latin | ZhC6 |
| Transliteration | GS6 |
| The chemical elements | FePb6 |
Description
Alloy ХН57ВКЮТМБЛ used: for the production of cast bar billets (LPZ), intended for subsequent remelting, forging and casting parts of gas turbines.
Note
Heat-resistant wrought Nickel-chromium alloy.
Standards
| Name | Code | Standards |
|---|---|---|
| Test methods. Packaging. Marking | В39 | OST 1 90181-75 |
| Bulls. Blanks. Slabs | В31 | TU 14-1-3315-81 |
| Castings with special properties (cast iron and steel) | В83 | TU 4110-78269737-002-2006 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Al | B | Ti | Mo | Pb | Bi | Nb | W | Ce | Zr | Co | Y |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-3315-81 | 0.13-0.2 | ≤0.01 | ≤0.015 | ≤0.4 | 8-9.5 | ≤0.4 | The rest | ≤1 | 5.1-6 | ≤0.035 | 2-2.9 | 1.2-2.4 | ≤0.001 | ≤0.0005 | 0.8-1.2 | 9.5-11 | ≤0.02 | ≤0.04 | 9-10.5 | ≤0.01 |
Ni is the basis.
According to TU 14-1-3315-81, the chemical composition is presented for an alloy of the brand ХН57ВКЮТМБЛ-ВИ (ЖС6У-ВИ). Cerium, zirconium and yttrium are introduced into the metal by calculation and chemical analysis is not determined. The deviation in the forest is +0.0030%.
According to TU 14-1-3315-81, the chemical composition is presented for an alloy of the brand ХН57ВКЮТМБЛ-ВИ (ЖС6У-ВИ). Cerium, zirconium and yttrium are introduced into the metal by calculation and chemical analysis is not determined. The deviation in the forest is +0.0030%.
Mechanical characteristics
| Section, mm | σB, MPa | d5, % |
|---|---|---|
| Cast rod stock (LPZ) on the other 14-1-3315-81. Heating to 1210±10 °C (exposure 4 h), air cooling | ||
| ≥833 | ≥3 | |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| σB | Limit short-term strength |
| d5 | Elongation after rupture |
Technological properties
| Name | The value |
|---|---|
| Workability by cutting | Alloy low machinability. |
| Macrostructure and contamination | In the fracture of cast bar billets (LPZ) on the other 14-1-3315-81 not allowed: oxide films, gas bubbles and shells, foreign non-metallic inclusions. The presence of podnasadochnogo looseness in the bars is not a rejection symptom. On the surface of rods permitted: rabiza, the color of the tint, clean the sink and Nikitiny. The quality of the bends and the surface of the bars shall conform to the standards agreed with VIAM. |