Brass Lc40mc3zh (ЛМцЖ55-3-1)

Brass LSdh Brass ЛЦ40Сd (ЛС59-1ЛД) Brass LC40S (LS59-1L) Brass ЛЦ40Мц3Ж (ЛМцЖ55-3-1) Brass ЛЦ40Мц3А Brass ЛЦ40Мц1,5 (ЛМц58-2L) Brass LC40AJ Brass ЛЦ38Мц2С2 Brass ЛЦ37Мц2С2К Brass LC30A3 (LA67-2,5) Brass ЛЦ25С2 Brass LC23A6Zh3Mz2 Brass ЛЦ16К4 (ЛК80-3L) Brass ЛЦ14К3С3 Brass LC10 (L90L) Brass LSch LSd brass LS Brass Brass VOC Brass LMZSCA Brass LMZSC Brass LMZS (LMZS58-2-2) Brass LMZKA Brass LMZh LKS Brass Brass LK2 Brass LK1 Brass LC Brass LAMZ (LAMZ66-6-3-2) Brass LA

Designation

Name The value
Designation GOST Cyrillic ЛЦ40Мц3Ж
Designation GOST Latin LTs40Mts3Zh
Transliteration LTs40Mts3G
The chemical elements ЛZn40Mn3Fe
Name The value
Designation GOST Cyrillic ЛМцЖ55-3-1
Designation GOST Latin LMtsZh55-3-1
Transliteration LMtsG55-3-1
The chemical elements ЛMnFe55-3-1

Description

Brass Lc40mc3zh used: for the manufacture of casting parts for shipbuilding, ship engineering and instrumentation; casting a simple configuration of parts critical applications and the reinforcement of naval shipbuilding, working at temperatures up to +300 °C; massive parts, propellers and blades for the tropics.

Note

Brass manganese-iron.

Standards

Name Code Standards
Non-ferrous metals, including rare metals, and their alloys В51 GOST 17711-93, GOST Р 50425-92
Castings from non-ferrous metals and alloys В84 OST 5Р.9209-82

Chemical composition

Standard P Mn Si Ni Fe Cu Al Zn Sn Sb Pb
OST 5Р.9209-82 ≤0.05 3-4 ≤0.2 ≤0.5 0.5-1.5 53-58 ≤0.6 The rest ≤0.5 ≤0.1 ≤0.5
Zn is the basis.
According to GOST 17711-93 and OST 5P.9209-82, the total amount of impurities should be ≤ 1.70%. Impurities not specified are taken into account in the total amount of impurities. The mass fraction of nickel in brass is allowed at the expense of copper and is not included in the sum of impurities. In the brass used for casting propellers, the mass fraction of copper should be 55.0-58.0%, aluminum - no more than 0.80%, lead - no more than 0.30%.

Mechanical characteristics

sT|s0,2, MPa σB, MPa d5, % kJ/m2, кДж/м2 Brinell hardness number, MPa
Castings on OST 1 90077-72
≥196 ≥490 ≥10 - ≥100
≥186 ≥441 ≥18 ≥392 ≥90
- ≥392 ≥10 - ≥90

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture
kJ/m2 Toughness

Our consultant will save your time

+49(1516) 758 59 40
E-mail:
Telegram:
WhatsApp:
Ask a question

Subscription

Special offers and discounts. :)
Titanium tube, Titanium rod, Copel wire, Heat-resistant sheet, Chromel wire