Brass Lmcs (ЛМцС58-2-2)

Brass LSdh Brass ЛЦ40Сd (ЛС59-1ЛД) Brass LC40S (LS59-1L) Brass ЛЦ40Мц3Ж (ЛМцЖ55-3-1) Brass ЛЦ40Мц3А Brass ЛЦ40Мц1,5 (ЛМц58-2L) Brass LC40AJ Brass ЛЦ38Мц2С2 Brass ЛЦ37Мц2С2К Brass LC30A3 (LA67-2,5) Brass ЛЦ25С2 Brass LC23A6Zh3Mz2 Brass ЛЦ16К4 (ЛК80-3L) Brass ЛЦ14К3С3 Brass LC10 (L90L) Brass LSch LSd brass LS Brass Brass VOC Brass LMZSCA Brass LMZSC Brass LMZS (LMZS58-2-2) Brass LMZKA Brass LMZh LKS Brass Brass LK2 Brass LK1 Brass LC Brass LAMZ (LAMZ66-6-3-2) Brass LA

Designation

Name The value
Designation GOST Cyrillic ЛМцС
Designation GOST Latin LMtsC
Transliteration LMtsS
The chemical elements ЛMnPb
Name The value
Designation GOST Cyrillic ЛМцС58-2-2
Designation GOST Latin LMtsC58-2-2
Transliteration LMtsS58-2-2
The chemical elements ЛMnPb58-2-2

Description

Brass Lmcs is used: for the manufacture of structural parts, equipment and shipbuilding; anti-friction parts with a simple configuration; the reinforcement of railway bearings; casting parts, metallurgical machinery (bearings, bushings and other friction parts, including reinforcement of railway bearings).

Note

Brass stamps Lmcs is a charging material for the melting of brass stamps Lc38mc2s2. The coefficient of friction of brass without lubrication of 0.24, with a lubricant — 0,016. Maximum load: static 100 kg/cm2, the dynamic is 60 kgf/cm2 sec.

Standards

Name Code Standards
Secondary non-ferrous metals, alloys and wastes В57 GOST 1020-97
Castings from non-ferrous metals and alloys В84 OST 24.916.01-71

Chemical composition

Standard P Mn Si Ni Fe Cu As Al Zn Sn Sb Pb Bi
GOST 1020-97 ≤0.05 1.8-2.5 ≤0.4 ≤1 ≤0.8 56-60 ≤0.05 ≤0.8 The rest ≤0.5 ≤0.1 1.5-2.5 ≤0.01
OST 24.916.01-71 - 1.5-2.5 - ≤1 ≤0.8 57-60 - ≤1 The rest ≤0.5 ≤0.1 1.5-2.5 -
Zn is the basis.
According to GOST 1020-97, nickel can be included in the mass fraction of copper, in this case nickel in the sum of impurities is not taken into account. Total total content of impurities is ≤2,20%.
According to OST 24.916.01-71 the total content of impurities is ≤ 2.50%. The content of nickel is allowed due to the copper content.

Mechanical characteristics

σB, MPa d Brinell hardness number, MPa
Casting as supplied. Without heat treatment
≥343 ≥8 ≥90
≥245 ≥10 ≥70

Description mechanical marks

Name Description
σB Limit short-term strength
d Elongation after rupture

Physical characteristics

Temperature r, кг/м3
20 8500

A description of the physical symbols

Name Description
l Coefficient of thermal conductivity
С Specific heat

Our consultant will save your time

+49(1523) 72 15 100
E-mail:
Telegram:
WhatsApp:
Ask a question

Subscription

Special offers and discounts. :)
Nickel tape, Stainless steel wire, Nickel wire, BrB2 circle, HN60VT pipe