Brass Lsdch

Brass LSdh Brass ЛЦ40Сd (ЛС59-1ЛД) Brass LC40S (LS59-1L) Brass ЛЦ40Мц3Ж (ЛМцЖ55-3-1) Brass ЛЦ40Мц3А Brass ЛЦ40Мц1,5 (ЛМц58-2L) Brass LC40AJ Brass ЛЦ38Мц2С2 Brass ЛЦ37Мц2С2К Brass LC30A3 (LA67-2,5) Brass ЛЦ25С2 Brass LC23A6Zh3Mz2 Brass ЛЦ16К4 (ЛК80-3L) Brass ЛЦ14К3С3 Brass LC10 (L90L) Brass LSch LSd brass LS Brass Brass VOC Brass LMZSCA Brass LMZSC Brass LMZS (LMZS58-2-2) Brass LMZKA Brass LMZh LKS Brass Brass LK2 Brass LK1 Brass LC Brass LAMZ (LAMZ66-6-3-2) Brass LA

Designation

Name The value
Designation GOST Cyrillic ЛСдч
Designation GOST Latin LCdch
Transliteration LSdch
The chemical elements ЛPbдч

Description

Brass Lsdch used: for the manufacture of injection molding and other types of casting; bushing and bearing cages.

Note

Brass stamps Lsdch is a charging material for the melting of brass stamps LC40S.

Standards

Name Code Standards
Secondary non-ferrous metals, alloys and wastes В57 GOST 1020-97

Chemical composition

Standard Mn Si Ni Fe Cu Al Sn Sb Pb Zr
GOST 1020-97 ≤0.5 ≤0.1 ≤0.5 ≤0.5 59-61 ≤0.1 ≤0.5 ≤0.05 0.8-1.5 The rest
Zr is the base.
In the mass fraction of copper, nickel can be included, in which case nickel is not taken into account in the sum of the impurities.
Total total content of impurities ≤1,40%.
The ratio (Fe + Mn) / Si should be for brass grades LSDh - from 4 to 6.

Mechanical characteristics

sT|s0,2, MPa σB, MPa d5, %
Chill casting
160-178 405-419 ≥30

Description mechanical marks

Name Description
sT|s0,2 Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2%
σB Limit short-term strength
d5 Elongation after rupture

Our consultant will save your time

+49 (170) 650 7006
E-mail:
Telegram:
WhatsApp:
Ask a question

Subscription

Special offers and discounts. :)
Circle 79nm, Pipe seamless 08X18H10T, India Institute 0, 29nk pipe, 309 sheet