Brass Lazhmc (ЛАЖМц66-6-3-2)

Brass LSdh Brass ЛЦ40Сd (ЛС59-1ЛД) Brass LC40S (LS59-1L) Brass ЛЦ40Мц3Ж (ЛМцЖ55-3-1) Brass ЛЦ40Мц3А Brass ЛЦ40Мц1,5 (ЛМц58-2L) Brass LC40AJ Brass ЛЦ38Мц2С2 Brass ЛЦ37Мц2С2К Brass LC30A3 (LA67-2,5) Brass ЛЦ25С2 Brass LC23A6Zh3Mz2 Brass ЛЦ16К4 (ЛК80-3L) Brass ЛЦ14К3С3 Brass LC10 (L90L) Brass LSch LSd brass LS Brass Brass VOC Brass LMZSCA Brass LMZSC Brass LMZS (LMZS58-2-2) Brass LMZKA Brass LMZh LKS Brass Brass LK2 Brass LK1 Brass LC Brass LAMZ (LAMZ66-6-3-2) Brass LA

Designation

Name The value
Designation GOST Cyrillic ЛАЖМц
Designation GOST Latin LAZhMts
Transliteration LAGMts
The chemical elements ЛAlFeMn
Name The value
Designation GOST Cyrillic ЛАЖМц66-6-3-2
Designation GOST Latin LAZhMts66-6-3-2
Transliteration LAGMts66-6-3-2
The chemical elements ЛAlFeMn66-6-3-2

Description

Brass lazhmc used: for the manufacture of structural components for critical applications operating at high specific and alternating loads; casting parts, metallurgical machinery (nuts of the adjusting screws; hollow shafts Stripping mechanisms of cranes; and massive crowns worm wheels, heavy duty).

Note

Corrosion resistant to action of air and water brass. Brass stamps Lazhmc is a charging material for the melting of brass stamps Lc23a6zh3mc2.
The maximum permissible speed of rotation 1.0 m/sec. Maximum load capacity: static — 50 kgf/cm2, dynamic — 50 kgf/cm2 sec.

Standards

Name Code Standards
Secondary non-ferrous metals, alloys and wastes В57 GOST 1020-97
Castings from non-ferrous metals and alloys В84 OST 24.916.01-71

Chemical composition

Standard Mn Si Ni Fe Cu Al Zn Sn Sb Pb
GOST 1020-97 1.5-3 ≤0.3 ≤1 2-4 63-70 4-7 The rest ≤0.7 ≤0.1 ≤0.7
OST 24.916.01-71 1.5-2.5 - ≤1 2-4 64-68 6-7 The rest ≤1 ≤0.1 ≤1
Zn is the basis.
According to GOST 1020-97, nickel can be included in the mass fraction of copper, in this case nickel in the sum of impurities is not taken into account. Total total content of impurities is ≤ 1.80%.
According to OST 24.916.01-71 the total content of impurities is ≤2.10%. The content of nickel is allowed due to the copper content.

Mechanical characteristics

σB, MPa d Brinell hardness number, MPa
Casting as supplied. Without heat treatment
≥638 ≥7 -
≥589 ≥7 ≥160
≥687 ≥7 -

Description mechanical marks

Name Description
σB Limit short-term strength
d Elongation after rupture

Physical characteristics

Temperature r, кг/м3
20 8500

A description of the physical symbols

Name Description
l Coefficient of thermal conductivity
С Specific heat

Our consultant will save your time

+49 (170) 650 7006
E-mail:
Telegram:
WhatsApp:
Ask a question

Subscription

Special offers and discounts. :)
Copper sheet, Titanium wire, brkmts3-1 wire, XH78T pipe, 03h17n14m3 pipe