Steel ПК20Х13М2-74 (Ж20Х13М2-74)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
ПК20Х13М2-74 |
| Designation GOST Latin |
PK20X13M2-74 |
| Transliteration |
PK20H13M2-74 |
| The chemical elements |
PCo20Cr13Mo2-74 |
| Name |
The value |
| Designation GOST Cyrillic |
Ж20Х13М2-74 |
| Designation GOST Latin |
Zh20X13M2-74 |
| Transliteration |
G20H13M2-74 |
| The chemical elements |
Ж20Cr13Mo2-74 |
Description
Steel ПК20Х13М2−74 is used: for the manufacture by cold deformation sredneshirotnykh structural components used in mechanical engineering and instrument making; tool holders of the tool; after heat treatment for parts operating under alternating loads and subject to wear.
Note
Powder steel is corrosion resistant.
The material should be applied after the impregnation with compounds that protect against internal corrosion. Compositions for the impregnation in accordance with OST 4G 0.054.213.
Standards
| Name |
Code |
Standards |
| Solid alloys, metal-ceramic products and powders, metal |
В56 |
OST 107.460094.118-88, OST 107.460009.002-90 |
Chemical composition
| Standard |
C |
Cr |
Fe |
N |
Mo |
| OST 107.460094.118-88 |
≤0.16 |
12-15 |
The rest |
0.05-0.15 |
1.5-2.5 |
Fe is the basis.
Mechanical characteristics
| Section, mm |
σB, MPa |
kJ/m2, кДж/м2 |
Brinell hardness number, MPa |
| Properties of the material to heat treatment at OST 107.460094.118-88 |
|
≥500 |
≥88.2 |
130-170 |
| Material properties for OST 107.460094.118-88 after heat treatment: a Vacation in vacuum at 750-850 °C (extract 3 hours) |
|
≥900 |
≥98 |
240-360 |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| σB |
Limit short-term strength |
| kJ/m2 |
Toughness |
Physical characteristics
| Temperature |
r, кг/м3 |
| 20 |
7400 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
| l |
Coefficient of thermal conductivity |
Technological properties
| Name |
The value |
| Microstructure |
Is not controlled to heat treatment. After heat treatment - Martensite alloyed ferrite. |