Steel ПК10Х13М2Д4-68 (Ж10Х13М2Д4-69)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
ПК10Х13М2Д4-68 |
| Designation GOST Latin |
PK10X13M2D4-68 |
| Transliteration |
PK10H13M2D4-68 |
| The chemical elements |
PCo10Cr13Mo2Cu4-68 |
| Name |
The value |
| Designation GOST Cyrillic |
Ж10Х13М2Д4-69 |
| Designation GOST Latin |
Zh10X13M2D4-69 |
| Transliteration |
G10H13M2D4-69 |
| The chemical elements |
Ж10Cr13Mo2Cu4-69 |
Description
Steel ПК10Х13М2Д4−68 is used: for the manufacture by the method of single pressing sredneshirotnykh structural components used in mechanical engineering and instrument making.
Note
Powder steel is corrosion resistant.
The material should be applied after the impregnation with compounds that protect against internal corrosion. Compositions for the impregnation in accordance with OST 4G 0.054.213.
Standards
| Name |
Code |
Standards |
| Solid alloys, metal-ceramic products and powders, metal |
В56 |
OST 107.460094.118-88, OST 107.460009.002-90 |
Chemical composition
| Standard |
C |
Cr |
Fe |
Cu |
N |
Mo |
| OST 107.460094.118-88 |
≤0.16 |
12-15 |
The rest |
3.5-4.5 |
0.2-0.4 |
1.5-2.5 |
Fe is the basis.
Mechanical characteristics
| Section, mm |
σB, MPa |
d |
kJ/m2, кДж/м2 |
Brinell hardness number, MPa |
| Properties of the material to heat treatment at OST 107.460094.118-88 |
|
≥539 |
≥0.6 |
≥58.8 |
280-340 |
| Material properties for OST 107.460094.118-88 after heat treatment: a Vacation in vacuum at 750-850 °C (extract 3 hours) |
|
≥352 |
≥0.6 |
≥58.8 |
207-321 |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| σB |
Limit short-term strength |
| d |
Elongation after rupture |
| kJ/m2 |
Toughness |
Physical characteristics
| Temperature |
r, кг/м3 |
| 20 |
6700 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
| l |
Coefficient of thermal conductivity |
| С |
Specific heat |
Technological properties
| Name |
The value |
| Microstructure |
Is not controlled to heat treatment. After heat treatment - martensite, ferrite alloy, copper is allowed in a free state. |