Н65Д29ЮТ alloy (K-Monel)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
Н65Д29ЮТ |
| Designation GOST Latin |
H65D29JuT |
| Transliteration |
N65D29YuT |
| The chemical elements |
Ni65Д29AlTe |
| Name |
The value |
| Designation GOST Cyrillic |
К-Монель |
| Designation GOST Latin |
K-Mohel |
| Transliteration |
K-Monel |
| The chemical elements |
Co-Cuонель |
Description
Alloy Н65Д29ЮТ used: for manufacturing of details of pumps and increased corrosion resistance; the shafts of modules, sections and input units of submersible centrifugal pumps; shafts of submersible centrifugal pumps, ECNC for oil.
Standards
| Name |
Code |
Standards |
| Bulls. Blanks. Slabs |
В31 |
TU 14-1-3833-84 |
| Sectional and shaped rolling |
В32 |
TU 14-1-3917-85 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Si |
Ni |
Fe |
Cu |
Al |
Ti |
| TU 14-1-3917-85 |
0.1-0.2 |
≤0.005 |
≤0.008 |
0.5-1 |
0.1-0.5 |
The rest |
0.9-1.5 |
27.5-30 |
2-4 |
0.25-1 |
Ni is the basis.
According to TU 14-1-3917-85 and TU 14-1-3833-84, the chemical composition is presented for the alloy N65D29YUT-ISH (K-monel) of vacuum induction smelting with subsequent electroslag remelting.
Mechanical characteristics
| sT|s0,2, MPa |
σB, MPa |
d |
| The billet is hot rolled in the state of delivery on the other 14-1-3833-84. Quenching in water technology manufacturer |
| 245-588 |
587-833 |
≥30 |
| The grooved bars as supplied on the other 14-1-3917-85. Aging at 620±10 °C (delay of 6-10 h), air cooling |
| ≥880 |
≥980 |
≥11 |
Description mechanical marks
| Name |
Description |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB |
Limit short-term strength |
| d |
Elongation after rupture |
Technological properties
| Name |
The value |
| Features of storage |
Bars on the other 14-1-3917-85 are supplied without grease, wrapped in synthetic film and Packed in returnable metal containers, made by the user. The total mass of bars in a bundle not more than 1 ton is permitted by an agreement with the consumer metal packaging in returnable containers a few of the ligament weight not exceeding 5 tonnes (gross). Storage of packaged bars are made in closed rooms with natural ventilation at temperatures from -60 °C to +50 °C without direct exposure to moisture. Storage and intrashop transportation of bundles and uncompressed bars must be carried out without damage. |