Alloy Н60МФЛ
Designation
| Name |
The value |
| Designation GOST Cyrillic |
Н60МФЛ |
| Designation GOST Latin |
H60MFL |
| Transliteration |
N60MFL |
| The chemical elements |
Ni60CuP |
Description
Alloy Н60МФЛ used: for the manufacture of the 1st, 2nd and 3rd groups casting parts spool valves, resistant to hydrochloric acid and other aggressive environments, high temperatures of the working medium up to +300 °C and rated working pressure not exceeding 1.6 MPa (16 kgf/cm2).
Note
Corrosion resistant Nickel-based alloy.
Standards
| Name |
Code |
Standards |
| Castings, steel |
В82 |
OST 26-07-402-83, ST ЦКБА 014-2004 |
Chemical composition
| Standard |
C |
S |
P |
Mn |
Cr |
Si |
Ni |
Fe |
V |
Ti |
Mo |
| ST ЦКБА 014-2004 |
≤0.06 |
≤0.02 |
≤0.025 |
≤1 |
≤0.3 |
≤1 |
The rest |
≤6 |
≤1.7 |
≤0.3 |
33-36 |
Ni is the basis.
Mechanical characteristics
| σB, MPa |
d |
| Casting parts of pipe fittings. Heat oven to 1100-1175 °C (extract 3 to 4 minutes per 1 mm wall thickness castings), air cooling or water |
| ≥620 |
≥1.5 |
Description mechanical marks
| Name |
Description |
| σB |
Limit short-term strength |
| d |
Elongation after rupture |