Alloy MA2-1pch
Designation
| Name |
The value |
| Designation GOST Cyrillic |
МА2-1пч |
| Designation GOST Latin |
MA2-1pch |
| Transliteration |
MA2-1pch |
| The chemical elements |
CuAl2-1пч |
Description
Alloy MA2−1pch used: for the manufacture of semi-finished products (sheets, plates, rods, sheets, tubes, wire, stampings and forgings) by hot deformation; extruded sections with cross sectional area up to 12 cm2 and a diameter of the circumscribed circle of up to 150 mm; ingots and slabs intended for the production of panels, stampings complex configuration for welding constructions with maximum operating temperatures up to +150 °C — long, up to +200 °C — short-term.
Standards
| Name |
Code |
Standards |
| Sectional and shaped rolling |
В52 |
GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 19657-84, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92 |
| Non-ferrous metals, including rare metals, and their alloys |
В51 |
GOST 14957-76, TU 1-4-015-80 |
| Bars |
В55 |
GOST 18351-73 |
| Pipes from non-ferrous metals and alloys |
В64 |
GOST 19441-74 |
| Sheets and stripes |
В53 |
GOST 21990-76 |
Chemical composition
| Standard |
Mn |
Si |
Ni |
Fe |
Cu |
Al |
Zn |
Mg |
Be |
| GOST 14957-76 |
0.2-0.6 |
≤0.01 |
≤0.001 |
≤0.005 |
≤0.01 |
3.8-5 |
0.8-1.5 |
The rest |
≤0.002 |
Mg is the basis.
According to GOST 14957-76 the mass fraction of other impurities is ≤ 0.10%. "Other impurities" include impurities whose permissible content limits are not indicated (≤), as well as impurities not included in the table, the content of which is not determined. Beryllium is not determined, but is introduced by calculation.
Mechanical characteristics
| Section, mm |
sT|s0,2, MPa |
σB, MPa |
d |
Brinell hardness number, MPa |
| Plate hot rolled according to GOST 21990-76 without heat treatment in the state of delivery (longitudinal samples) |
| 12-32 |
≥137 |
≥245 |
≥8 |
- |
| 32-40 |
- |
≥226 |
≥6 |
- |
| Extruded GOST 19657-84 without heat treatment in the state of delivery (in cross-section provided the cross-sectional area of the profile in cm2) |
| 5-12 |
≥145 |
≥255 |
≥8 |
≥42 |
| 5 |
≥155 |
≥265 |
≥9 |
≥45 |
| Bars and rods, hot-pressed in the delivery condition without heat treatment according to GOST 18351-73 (longitudinal samples) |
| 160-200 |
- |
≥245 |
≥5 |
- |
| 8-160 |
≥145 |
≥255 |
≥8 |
- |
| Tubes extruded in the state of delivery according to GOST 19441-74 (samples) |
| - |
- |
≥225 |
≥8 |
- |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| sT|s0,2 |
Yield strength or limit of proportionality with a tolerance for residual deformation of 0.2% |
| σB |
Limit short-term strength |
| d |
Elongation after rupture |
Physical characteristics
| Temperature |
Е, ГПа |
r, кг/м3 |
l, Вт/(м · °С) |
R, НОм · м |
| 20 |
42 |
1790 |
963 |
120 |
A description of the physical symbols
| Name |
Description |
| Е |
The normal elasticity modulus |
| r |
Density |
| l |
Coefficient of thermal conductivity |
| С |
Specific heat |