Bronze Bro6c6s3 (БрОЦС6-6-3)
Bronze БрО3Ц8С4Н1 (БрОЦСН3-8-4-1)
Bronze БрО8Ц4 (БрОЦ8-4)
Bronze БрО8С21 (БрОС8-21)
Bronze БрО8С12 (БрОС8-12)
Bronze БрО8Н4Ц2 (БрОНЦ8,5-4-2)
Bronze БрО6Ц6С3 (БрОЦС6-6-3)
Bronze БрО6Ц6С2х (БрОЦС6-6-2х)
Bronze БрО6Ц4С2Н1 (БрОЦСН6-4-2-1)
Bronze БрО6С6Ц3
Bronze БрО6К2Ц1
Bronze БрО5Ц6С5 (БрОЦС5-6-5)
Bronze БрО5Ц5С5 (БрОЦС5-5-5)
Bronze БрО5С25 (БрОС5-25)
Bronze БрО4Ц8С5
Bronze БрО4Ц7С5 (БрОЦС3,5-7-5)
Bronze БрО4Ц4С17 (БрОЦС4-4-17)
Bronze БрО3Ц7С5Н1 (БрОЦСН3-7-5-1)
Bronze БрО3Ц6С5 (БрОЦС3-6-5)
Bronze БрО3Ц13С4 (БрОЦС3-13-4)
Bronze БрО3Ц12С5 (БрОЦС3-12-5)
Bronze БрО3,5Ц7С5
Bronze BrO19
Bronze БрО16С5 (БрОС16-5)
Bronze БрО10Ц2Н2 (БрОЦН10-2-2)
Bronze БрО10Ц2Н1,5 (БрОЦН10-2-1,5)
Bronze БрО10Ц2 (БрОЦ10-2)
Bronze БрО10Ф1 (БрОФ10-1)
Bronze БрО10Ф0,7Н0,5 (БрОФН10-0,7-0,5)
Bronze БрО10С2Н3 (БрОСН10-2-3)
Bronze БрО10С10 (БрОС10-10)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | БрО6Ц6С3 |
| Designation GOST Latin | BpO6Ts6C3 |
| Transliteration | BrO6Ts6S3 |
| The chemical elements | BaSn6Zn6Pb3 |
| Name | The value |
|---|---|
| Designation GOST Cyrillic | БрОЦС6-6-3 |
| Designation GOST Latin | BpOTsC6-6-3 |
| Transliteration | BrOTsS6-6-3 |
| The chemical elements | BaSnZnPb6-6-3 |
Description
Bronze Bro6c6s3 used: for the manufacture of valves for critical applications, anti-friction parts, bearings; shaped castings.
Note
Recommended as a substitute for brass Lmcs (ЛМцС58−2-2).
Standards
| Name | Code | Standards |
|---|---|---|
| Non-ferrous metals, including rare metals, and their alloys | В51 | GOST 613-79, OST 1 90054-72 |
| Castings from non-ferrous metals and alloys | В84 | OST 1 90046-72 |
Chemical composition
| Standard | S | P | Si | Ni | Fe | Cu | As | Al | Zn | Sn | Sb | Pb | Bi | Mg |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| GOST 613-79 | ≤0.05 | ≤0.05 | ≤0.02 | ≤2 | ≤0.4 | The rest | ≤0.15 | ≤0.05 | 5-7 | 5-7 | ≤0.5 | 2-4 | ≤0.02 | ≤0.02 |
| OST 1 90054-72 | - | ≤0.05 | ≤0.02 | - | ≤0.4 | The rest | - | ≤0.05 | 5-7 | 5-7 | ≤0.5 | 2-4 | ≤0.02 | - |
Cu is the basis.
The total percentage of impurities in the OST 1 90054-72 (elements with a content ≤) is 1.3%. Impurities that are not regulated by the table are included in the total amount of impurities.
According to GOST 613-79, the total content of impurities should be ≤ 1.30%. Impurities not regulated by the standard are included in the total amount of impurities. The mass fraction of nickel due to copper and the sum of impurities is not included.
The total percentage of impurities in the OST 1 90054-72 (elements with a content ≤) is 1.3%. Impurities that are not regulated by the table are included in the total amount of impurities.
According to GOST 613-79, the total content of impurities should be ≤ 1.30%. Impurities not regulated by the standard are included in the total amount of impurities. The mass fraction of nickel due to copper and the sum of impurities is not included.
Mechanical characteristics
| σB, MPa | d5, % | Brinell hardness number, MPa |
|---|---|---|
| Castings are supplied without heat treatment | ||
| ≥147 | ≥6 | ≥60 |
| ≥176.2 | ≥4 | ≥60 |
| Casting investment casting according to OST 1 90046-72 (samples separately cast or cut from castings) | ||
| ≥177 | ≥10 | ≥60 |
Description mechanical marks
| Name | Description |
|---|---|
| σB | Limit short-term strength |
| d5 | Elongation after rupture |