Aluminium A995
Aluminum A0
Aluminum A35
Aluminum A5
Aluminum A5E
Aluminum A6
Aluminum A7
Aluminum A7E
Aluminum A8
Aluminum A85
Aluminum A95
Aluminum A97
Aluminum A98
Aluminum A99
Aluminum A995
Aluminum A7E
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | А995 |
| Designation GOST Latin | A995 |
| Transliteration | A995 |
| The chemical elements | - |
Description
Aluminium A995 used: for the production of billets cast by semi-continuous method or continuous casting, and is intended for rolling into sheets, strips and other semi-finished products; ingots, wire, ribbon; drawn wire for wire and cables and wire for welding and other purposes; aluminium powder Kommandos brands of APS-1, APS-1B, APS-2, APS-3 is intended for the production teploperenosa deformable material type SAP.
Note
High purity aluminium.
Standards
| Name | Code | Standards |
|---|---|---|
| Solid alloys, metal-ceramic products and powders, metal | В56 | GOST 10096-76 |
| Sectional and shaped rolling | В52 | GOST 13616-97, GOST 13617-97, GOST 13618-97, GOST 13619-97, GOST 13620-90, GOST 13621-90, GOST 13622-91, GOST 13623-90, GOST 13624-90, GOST 13737-90, GOST 13738-91, GOST 17575-90, GOST 17576-97, GOST 29296-92, GOST 29303-92, GOST Р 50066-92, GOST Р 50067-92, GOST Р 50077-92 |
| Non-ferrous metals, including rare metals, and their alloys | В51 | GOST 4004-64, GOST 9498-79, GOST 11069-2001, GOST 11070-74, GOST 19437-81 |
| Wire of non-ferrous metals and their alloys | В74 | OST 1 92005-2002 |
| Bars | В55 | TU 1-1-115-74 |
Chemical composition
| Standard | Mn | Si | Fe | Cu | Al | Ti | Zn | Mg |
|---|---|---|---|---|---|---|---|---|
| GOST 11069-2001 | ≤0.001 | ≤0.0015 | ≤0.0015 | ≤0.001 | ≥99.995 | ≤0.001 | ≤0.001 | ≤0.001 |
Al is the base.
According to GOST 19437-81 and GOST 11069-2001, the Ga content is 0.0030%. The content of other impurities (each individually) is ≤ 0.001%. The total content of all impurities is ≤ 0.0050%.
According to GOST 19437-81 and GOST 11069-2001, the Ga content is 0.0030%. The content of other impurities (each individually) is ≤ 0.001%. The total content of all impurities is ≤ 0.0050%.
Mechanical characteristics
| σB, MPa | d5, % | Brinell hardness number, MPa |
|---|---|---|
| Cast aluminum delivery condition | ||
| ≥50 | ≥45 | 13-15 |
Description mechanical marks
| Name | Description |
|---|---|
| σB | Limit short-term strength |
| d5 | Elongation after rupture |