Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | А8 |
| Designation GOST Latin | A8 |
| Transliteration | A8 |
| The chemical elements | - |
Description
Aluminium A8 is used: for the production of pigs, ingots, wire rod, flat ingots, cast by semi-continuous method or continuous casting, and is intended for rolling into sheets, strips and other semi-finished products; aluminum Kommandos powder brands APS-1A and APS-1B, APS-2, APS-3 is intended for the production teploperenosa deformable material type SAP.
Note
Aluminium technical purity.
Grade of aluminium A8 corresponds to the chemical composition of the marches of aluminium EN AW-1080А established in the European standard EN 1080 573−3-94 and brands and 1180А, registered by the American aluminum Association.
Standards
| Name | Code | Standards |
|---|---|---|
| Solid alloys, metal-ceramic products and powders, metal | В56 | GOST 10096-76 |
| Pipes from non-ferrous metals and alloys | В64 | GOST 18475-82, TU 1-4-074-88 |
| Non-ferrous metals, including rare metals, and their alloys | В51 | GOST 9498-79, GOST 11069-2001, GOST 11070-74, GOST 19437-81 |
Chemical composition
| Standard | Mn | Si | Fe | Cu | Al | Ti | Zn | Mg |
|---|---|---|---|---|---|---|---|---|
| GOST 11069-2001 | ≤0.02 | ≤0.1 | ≤0.12 | ≤0.01 | ≥99.8 | ≤0.01 | ≤0.04 | ≤0.02 |
Al is the base.
According to GOST 19437-81 and GOST 11069-2001, the Ga content is ≤ 0.030%. The content of other impurities (individually) is ≤ 0.020%. The total content of all impurities is ≤ 0.20%.
According to GOST 19437-81 and GOST 11069-2001, the Ga content is ≤ 0.030%. The content of other impurities (individually) is ≤ 0.020%. The total content of all impurities is ≤ 0.20%.
Mechanical characteristics
| Section, mm | σB, MPa | d10 |
|---|---|---|
| Cold-rolled tubes in the delivery condition according to GOST 18475-82, OST 4.021.119-92 samples (in cross-section shows the thickness of the wall) | ||
| ≥60 | ≥20 | |
| ≤2 | ≥80 | ≥4 |
| 2-5 | ≥80 | ≥5 |
Description mechanical marks
| Name | Description |
|---|---|
| Section | Section |
| σB | Limit short-term strength |
| d10 | Elongation after rupture |