Alloy Alloy 273
Alloy MNTS16-29-1.8
Alloy MNMts43-0.5 (Kopel)
Alloy MNMts5-3.7
Alloy MNMz60-20-20
Alloy MNMts68-4-2
Alloy MNMtsAZh3-12-0.25-0.2
Alloy MNMtsAZh3-12-0,3-0,3 (Manganin)
Alloy MNMtsAZhVTNb40-2-1,5-1,4 (MN40S)
Alloy MNMZh40-1,4-0,45
Alloy MNTs12-24
Alloy MNTs15-20 (Neusilber)
Alloy MNTs18-20
Alloy MNC18-27
Alloy MNMts4.5-1.5 (Alloy A)
Alloy Neusilber 30
Alloy NK
Alloy NK2.4 (Cilin)
Alloy HM25
Alloy NM40A
Alloy NM60A
Alloy NMZhMz28-2,5-1,5
Alloy NMMKZhMC30-4-2-1 (VKM)
Alloy NMMZTA26-1,5-1,1-0,5
Alloy NMCAT3-1,5-0,6
Alloy NMCATC1-1,5-2,5-0,15
Alloy NHC9-0.9 (Silch)
Alloy Alloy 273
Alloy MNA13-3 (Kunial A)
Castolin Alloy
Alloy MN0.6 (Alloy TP)
Alloy MN10
Alloy MN15
Alloy MH16 (Alloy TB)
Alloy MH17 (Alloy B)
Alloy MN19 (Melchior)
Alloy MN2.15
Alloy MN23
Alloy MN25
Alloy MN45 (Constantan)
Alloy MN6
Alloy MN95-5
Alloy MNMts40-1.5 (Constantan)
Alloy MNA6-1.5 (Kunial B)
Alloy MNAZHMZ6-0.8-0.8-0.6 (BS-3)
Alloy MNAKH11-2,5-1,0-0,8 (Alloy 131)
Alloy MNAHMC15-3,5-2-3 (Alloy 538)
Alloy MNAHMc20-4-3-4 (Alloy 546; Camelon)
Alloy MNAXMZ4,5-4,5-0,7-2,5 (Kamelin)
Alloy MNZh5-1
Alloy MNZh9.3-0.5 (Menigel)
Alloy MNZHKT5-1-0,2-0,2
Alloy MNZHMZ10-1-1
Alloy MNZHMZ30-1-1
Alloy MNMts3-12 (Manganin)
Designation
| Name |
The value |
| Designation GOST Cyrillic |
273 |
| Designation GOST Latin |
273 |
| Transliteration |
273 |
| The chemical elements |
273 |
Description
Alloy Alloy 273 is used: for the manufacture of bars drawn (7−35 mm), and extruded (36−245 mm); pipes; parts shipbuilding, working in aggressive environments.
Standards
| Name |
Code |
Standards |
| Non-ferrous metals, including rare metals, and their alloys |
В51 |
GOST 28873-90 |
| Bars |
В55 |
TU 48-21-583-77, TU 48-21-583-зкс-2008 |
| Pipes from non-ferrous metals and alloys |
В64 |
TU 48-21-591-77 |
Chemical composition
| Standard |
Si |
Ni |
Fe |
Cu |
Ti |
Zr |
| TU 48-21-583-77 |
≤0.05 |
17.2-19 |
≤0.05 |
The rest |
0.5-0.7 |
0.1-0.23 |
Cu is the basis.
According to TU 48-21-583-77 the chemical composition of alloy 273 is given. The content of undetectable impurities should not exceed 0.080% in total. The silicon content is guaranteed by the manufacturer.
Mechanical characteristics
| Section, mm |
σB, MPa |
d5, % |
| Bars in ruins, and delivery on the other 48-21-583-77 |
| 36-67 |
≥422 |
≥15 |
| 70-145 |
≥392 |
≥15 |
| 20-35 |
≥490 |
≥8 |
| 7-19 |
≥540 |
≥5 |
Description mechanical marks
| Name |
Description |
| Section |
Section |
| σB |
Limit short-term strength |
| d5 |
Elongation after rupture |
Technological properties
| Name |
The value |
| Macrostructure and contamination |
At the bend in the bars should not be of non-metallic inclusions, delaminations, voids and utain visible to the naked eye. |