Cast Iron L-NiCuCr15-6-3
Designation
| Name |
The value |
| Designation GOST Cyrillic |
L-NiCuCr15-6-3 |
| Designation GOST Latin |
L-NiCuCr15-6-3 |
| Transliteration |
L-NiCuCr15-6-3 |
| The chemical elements |
L-NiCuCr15-6-3 |
Description
Cast iron L-NiCuCr15−6-3 is used: for the manufacture of parts of nasosov, valves, furnaces, bushings for the ring holders of the pistons.
Note
Nickel cast iron. Has good corrosion resistance, especially in alkaline media, in dilute solutions of acids, in sea water and in salt solutions. Has good heat resistance, good bearing properties, high thermal expansion, has no magnetic properties at low content of chromium. Cast iron L-NiCuCr15−6-3 has the best resistance to erosion and corrosion than cast iron brand L-NiCuCr15−6-2.
Standards
| Name |
Code |
Standards |
| Castings with special properties (cast iron and steel) |
В83 |
GOST 7769-82 |
Chemical composition
| Standard |
C |
Mn |
Cr |
Si |
Ni |
Fe |
Cu |
| GOST 7769-82 |
≤3 |
0.5-1.5 |
2.5-3.5 |
1-2.8 |
13.5-17.5 |
The rest |
5.5-7.5 |
Fe is the basis.
Mechanical characteristics
| σB, MPa |
d4 |
Brinell hardness number, MPa |
| Castings on OST 1 90077-72 |
| 190-240 |
1-2 |
150-250 |
Description mechanical marks
| Name |
Description |
| σB |
Limit short-term strength |
| d4 |
Elongation after rupture |
Physical characteristics
| Temperature |
Е, ГПа |
| 20 |
98-113 |
A description of the physical symbols
| Name |
Description |
| l |
Coefficient of thermal conductivity |
| a |
The coefficient of linear expansion |