Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 5Х2ГСМФ |
| Designation GOST Latin | 5X2GCMF |
| Transliteration | 5H2GSMF |
| The chemical elements | 5Cr2MnСMoV |
Description
5Х2ГСМФ steel is used: for the production of forgings of various parts of General machinery; heavy-duty one-piece hammer stamps weight not exceeding 5 t
Note
Steel medium-alloyed multicomponent. Along with increased heat resistance, hot strength and wear resistance, the steel has the worst technological properties requires a higher heat for hardening, reduced hardenability and machinability.
Standards
| Name | Code | Standards |
|---|---|---|
| Metal forming. Forgings | В03 | TU 108.11.917-87 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Ni | Fe | Cu | V | Mo |
|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 108.11.917-87 | 0.46-0.54 | ≤0.02 | ≤0.025 | 0.8-1 | 1.6-2.3 | 0.6-0.8 | ≤0.4 | The rest | ≤0.3 | 0.1-0.2 | 0.25-0.35 |
Fe is the basis.
According to TU 108.11.917-87, the total content of sulfur and phosphorus should be ≤ 0.040%. The use of ferrotitanium for deoxidizing and modifying steel with the addition of titanium by 0.0050% is permitted.
According to TU 108.11.917-87, the total content of sulfur and phosphorus should be ≤ 0.040%. The use of ferrotitanium for deoxidizing and modifying steel with the addition of titanium by 0.0050% is permitted.