Alloy 35KKH8F
Alloy 52K12F (52KFB)
Alloy UNDK24
Alloy EX9K15M2
Alloy EX5K5
Alloy EX3
Alloy EB6
Alloy 5X14V (5XV14)
Alloy 52KFTM
Alloy 52KF
Alloy 52K9F (52KF9)
Alloy 52K7F (52KF7)
Alloy 52K5F (52KF5)
Alloy 52K13F (52KFA)
Alloy 52K11F (52KFV)
Alloy 52K10F (52KF11)
Alloy 40KNB (EP966)
Alloy 35KH8F
Alloy 35KX6F
Alloy 35KX4F
Alloy 35KX15
Alloy 35KX12
Alloy 25X15KYUBF (EC33; 25X15K1)
Alloy 25NY
Alloy 22Kh15KTF (EK159; 22Kh15KA)
Alloy 20NCHG (EP298)
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | 35КХ8Ф |
| Designation GOST Latin | 35KX8F |
| Transliteration | 35KH8F |
| The chemical elements | 35CoCr8P |
Description
Alloy 35KKH8 °F used: for the manufacture of the active part of the hysteresis motors; parts color TV; small-sized permanent magnets.
Note
The alloy with the specified parameters private (in the maximum permeability) of the hysteresis loop. Acquires magnetic properties after cold deformation and tempering. The alloy anisotropic, but can be manufactured with reduced anisotropy. Alloy with coercive force of not less than 60 um and a residual induction of at least 11,000 Gauss.
Standards
| Name | Code | Standards |
|---|---|---|
| Classification, nomenclature and general norms | В30 | GOST 10994-74 |
| Sheets and stripes | В33 | TU 14-1-1252-75 |
| Tapes | В34 | TU 14-1-1870-75 |
| Sectional and shaped rolling | В32 | TU 14-11-245-88 |
Chemical composition
| Standard | C | S | P | Mn | Cr | Si | Fe | V | Co |
|---|---|---|---|---|---|---|---|---|---|
| GOST 10994-74 | ≤0.09 | ≤0.02 | ≤0.02 | ≤0.4 | 7.5-8.5 | ≤0.3 | The rest | 7.5-8.5 | 34.3-35.8 |
Fe is the basis.