Powder material the titanium Hydride
Powder material Titanium Hydride
Powder material DTKT
Designation
| Name | The value |
|---|---|
| Designation GOST Cyrillic | Гидрид титана |
| Designation GOST Latin | Gidpid titaha |
| Transliteration | Gidrid titana |
| The chemical elements | Gaдрид титана |
Description
Powder material the titanium Hydride is used: to produce a protective atmosphere during heat treatment of parts (except time spiral).
Note
The powder of the hydride of titanium from titanium sponge obtained by the method of hydrogenation and subjected to hydrometallurgical processing.
Standards
| Name | Code | Standards |
|---|---|---|
| Solid alloys, metal-ceramic products and powders, metal | В56 | TU 14-1-2159-77 |
Chemical composition
| Standard | C | Ni | Fe | N | Ti | Ca | Mg | Cl | H |
|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-2159-77 | ≤0.07 | ≤0.08 | ≤0.3 | ≤0.08 | The rest | ≤0.05 | ≤0.08 | ≤0.05 | ≥3.5 |
Ti is the basis.
According to TU 14-1-2159-77, the chemical composition is given for the titanium hydride powder material. The total chlorine content is indicated. The free chlorine content should not be more than 0.0050%.
According to TU 14-1-2159-77, the chemical composition is given for the titanium hydride powder material. The total chlorine content is indicated. The free chlorine content should not be more than 0.0050%.
Technological properties
| Name | The value |
|---|---|
| Features of production | Granulometric composition of powder titanium hydride on the other 14-1-2159-77 must meet the following requirements: when sifting the powder through a mesh 025-028 according to GOST 6613 the rest of it should not be more than 3%. The powder must not contain foreign inclusions and lumps. |